Manufacturing method of reinforced floorboard with high surface brightness

A technology for laminate flooring and a manufacturing method, which is applied in chemical instruments and methods, devices for coating liquid on surfaces, floors, etc., can solve the problems of complex production process, high production cost of laminate flooring, and inattentiveness to surface brightness, etc. Improve impact resistance and load-bearing capacity, fast curing speed, and improve the effect of appearance quality

Inactive Publication Date: 2017-02-01
普洱绿洲木业有限公司
View PDF9 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, in the surface treatment of laminate flooring, people are accustomed to only emphasizing the surface wear resistance and color effect, and consumers often pay little attention to the brightness of the surface.
Manufacturers of laminate flooring are also unwilling to get involved because of the high production cost and complicated production process of laminate flooring with high surface brightness.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A method for making a laminated floor with a high surface brightness, comprising the following steps:

[0028] Steel plate treatment: mechanically polish the surface of the steel plate, and chemically polish the chrome-plated layer to obtain a chrome-plated steel plate; the chemical polishing is to plate the chrome layer in the electrolyte, wherein the voltage is 1000 volts, and the time is 4 hours.

[0029] Wear-resistant layer treatment: immerse the wear-resistant paper in the wear-resistant paper impregnating glue, wherein the weight ratio of the wear-resistant paper to the wear-resistant paper impregnating glue is 1:1, and the composition of the wear-resistant paper impregnating glue includes, by weight , 45 parts of polyvinyl chloride type III resin; 7 parts of dichlorobenzophenone, 8 parts of melamine, 20 parts of fatty acid alkyd resin, and 4 parts of butyl acetate. The impregnated wear-resistant paper is taken out and dried to 10% dry; the composite aluminum oxi...

Embodiment 2

[0032] A method for making a laminated floor with a high surface brightness, comprising the following steps:

[0033] Steel plate treatment: mechanically polish the surface of the steel plate, and chemically polish the chromium-plated layer to obtain a chrome-plated steel plate; the chemical polishing is to plate the chromium layer in an electrolyte, wherein the voltage is 1600 volts, and the time is 3 hours.

[0034] Wear-resistant layer treatment: immerse the wear-resistant paper in the wear-resistant paper impregnating glue, wherein the weight ratio of the wear-resistant paper to the wear-resistant paper impregnating glue is 1: 2, and the composition of the wear-resistant paper impregnating glue includes, by weight , 75 parts of polyvinyl chloride type III resin; 12 parts of dichlorobenzophenone, 25 parts of melamine, 30 parts of fatty acid alkyd resin, and 7 parts of butyl acetate. The impregnated wear-resistant paper is taken out and dried to 40% dry; the composite alumin...

Embodiment 3

[0037] A method for making a laminated floor with a high surface brightness, comprising the following steps:

[0038] Steel plate treatment: mechanically polish the surface of the steel plate, and chemically polish the chrome-plated layer to obtain a chrome-plated steel plate; the chemical polishing is to plate the chrome layer in the electrolyte, wherein the voltage is 1400 volts, and the time is 4 hours.

[0039]Wear-resistant layer treatment: immerse the wear-resistant paper in the wear-resistant paper impregnating glue, wherein the weight ratio of the wear-resistant paper to the wear-resistant paper impregnating glue is 1:3; the composition of the wear-resistant paper impregnating glue includes, by weight , 56 parts of polyvinyl chloride type III resin; 10 parts of dichlorobenzophenone, 17 parts of melamine, 24 parts of fatty acid alkyd resin, and 6 parts of butyl acetate. The impregnated wear-resistant paper is taken out and dried to 30% dry; the composite aluminum oxide ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Thicknessaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a manufacturing method of a reinforced floorboard with the high surface brightness. The manufacturing method comprises the following steps that a steel plate is treated, specifically, the surface of the steel plate is polished to obtain a chrome-plated steel plate; an abrasion-resisting layer is treated, specifically, abrasion-resisting paper is dipped into abrasion-resisting paper dipping glue, taken out and made 10-40% dried; composite aluminum oxide powder is uniformly poured and sprayed on the surface of the dipped abrasion-resisting paper, and an abrasion-resisting layer is obtained; patterned paper and balance paper are dipped with composite melamine resin; the dipped patterned paper and the abrasion-resisting layer are sequentially laid on a fiberboard; and the dipped balance paper is laid under the fiberboard, hot pressing is conducted through the chrome-plated steel plate, and the reinforced floorboard with the high surface brightness is obtained. The surface brightness of the floorboard manufactured through the manufacturing method can reach up to 100+ / -10 degree, and the floorboard is obviously superior to ordinary floorboards. The floorboard is firm, high in corrosion resistance and long in service life, and the brightness is not prone to weakening in the use process.

Description

technical field [0001] The patent of the present invention relates to a floor, in particular to a method for making a reinforced floor with a high surface brightness. Background technique [0002] Laminated flooring is also called impregnated paper laminated wood flooring / laminated wood flooring. It is made of one or more layers of special paper impregnated with thermosetting amino resin. Heat-pressed, formed floors. Laminate flooring has the advantages of wear resistance, impact resistance, deformation resistance, and pollution resistance, and has been widely used in people's daily lives. [0003] However, in the surface treatment of laminate flooring, people are accustomed to only emphasizing the surface wear resistance and color effect, and consumers often pay little attention to the brightness of the surface. Manufacturers of laminate flooring are also unwilling to get involved because of the high production cost and complicated production process of laminate flooring ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): E04F15/02B32B37/10B32B37/06B32B38/08B32B38/00B05D7/24
CPCB05D7/24B05D7/544B05D2203/22B05D2451/00B05D2506/25B05D2602/00B32B37/06B32B37/10B32B38/00B32B38/08E04F15/02B05D2401/10B05D2401/32B05D2420/01
Inventor 罗杨
Owner 普洱绿洲木业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com