Lead acid storage battery positive electrode lead paste

A technology of lead-acid battery and positive electrode paste, which is applied in the direction of battery electrodes, circuits, electrical components, etc., can solve problems such as limited effects, and achieve the goals of preventing early capacity decay, increasing early capacity, high formability and active material utilization. Effect

Inactive Publication Date: 2017-02-08
CHAOWEI POWER CO LTD
View PDF3 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Commonly used positive electrode additives such as carbon materials are difficult to...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A kind of lead-acid accumulator anode lead paste, is made from the raw material of following parts by weight: 70 parts of lead powder, 10 parts of sulfuric acid, 3 parts of water, 0.5 part of short fiber, 1 part of sodium perborate, 0.1 part of sodium pyroantimonate, red Dan 1 part, titanium oxide 0.1 part.

[0020] Wherein, the lead powder is Shimadzu lead powder or Barton lead powder, the mass percent concentration of sulfuric acid is 45%, the purity of sodium perborate is 95wt%, the purity of potassium pyroantimonate is 99wt%, and the particle size of red lead is 1.5 μm , the purity of titanium dioxide is 99wt%, the particle size is 100nm, and the short fiber is polythiophene fiber.

Embodiment 2

[0022] A kind of lead-acid accumulator anode lead paste, is made from the raw material of following parts by weight: 70 parts of lead powder, 10 parts of sulfuric acid, 3 parts of water, 0.5 part of short fiber, 1 part of sodium perborate, 0.1 part of sodium pyroantimonate, red Dan 1 part, titanium oxide 0.1 part.

[0023] Wherein, the lead powder is Shimadzu lead powder or Barton lead powder, the mass percent concentration of sulfuric acid is 45%, the purity of sodium perborate is 95wt%, the purity of potassium pyroantimonate is 99wt%, and the particle size of red lead is 1.5 μm , the purity of titanium dioxide is 99wt%, the particle size is 100nm, and the short fiber is polypyrrole fiber.

Embodiment 3

[0025] A kind of lead-acid storage battery cathode lead paste, is made from the raw material of following parts by weight: 70 parts of lead powder, 15 parts of sulfuric acid, 7 parts of water, 1 part of short fiber, 1 part of sodium perborate, 1.5 parts of sodium pyroantimonate, red Dan 3 parts, titanium oxide 1.5 parts.

[0026] Wherein, the lead powder is Shimadzu lead powder or Barton lead powder, the mass percent concentration of sulfuric acid is 45%, the purity of sodium perborate is 97wt%, the purity of potassium pyroantimonate is 99.5wt%, and the particle size of red lead is 1 μm , the purity of titanium dioxide is 99.5wt%, the particle size is 90nm, and the short fibers are polyvinyl chloride fibers.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses lead acid storage battery positive electrode lead paste, and belongs to the technical field of lead acid storage battery manufacturing. The lead acid storage battery positive electrode lead paste is prepared from lead powder, sulfuric acid, water, short fiber, sodium perborate, sodium pyroantimonate, red lead and titanium black. Besides the ingredients of the lead powder, the sulfuric acid, the water and the short fiber, the lead acid storage battery positive electrode lead paste also comprises the effective ingredients of the sodium perborate, the red lead, the titanium black conducting ceramic materials and the like. The hole shape and the porosity are maintained by a lead acid storage battery assembled in such a way in the charging and discharging process; the positive electrode active ingredients have high forming performance and active ingredient utilization rate; high capacity is realized during high-rate discharging; the network structure of the positive electrode active substances is stable; the early stage capacity of the battery can be increased; the early capacity attenuation of the battery can be prevented; meanwhile, the hydrogen separation potential of the battery is obviously reduced.

Description

technical field [0001] The invention relates to the technical field of lead-acid storage battery manufacturing, in particular to a lead-acid storage battery anode lead paste. Background technique [0002] Lead-acid battery has a history of more than 150 years since it was invented by Plant in 1859. The technology is very mature and it is the most widely used chemical power source in the world. Although new batteries such as nickel-cadmium batteries, nickel-metal hydride batteries, and lithium-ion batteries have been introduced and applied in recent years, lead-acid batteries still rely on high-current discharge performance, stable voltage characteristics, wide temperature range, and large single-cell capacity. It can charge and discharge hundreds of cycles, good storage performance (especially suitable for dry charge storage), high safety, rich and renewable raw materials, low price and other advantages, in most traditional fields and some emerging fields application field,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H01M4/57H01M4/62
CPCH01M4/57H01M4/62Y02E60/10
Inventor 王江林周丽朱军平代少振项晨吴鑫
Owner CHAOWEI POWER CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap