Preparation method of high-strength fireproof corrosion-resistant type bamboo boards

A high-strength, fire-resistant technology, applied in the pretreatment of molding materials, manufacturing tools, wood treatment, etc., can solve the problems of limited application and popularization, inability to encounter fire, and unsatisfactory insect and moisture resistance.

Inactive Publication Date: 2017-03-08
叙永县象实竹木业有限责任公司
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing bamboo board preparation process is mostly prepared by cutting, crushing, mixing, curing, pressing, and curing, and can obtain relatively high-quality environmentally friendly bamboo boards, but its strength is not ideal, and the insect-proof and moisture-proof performance is also in some special cases. The humid area is not ideal, and it is obvious that it cannot be exposed to fire, which greatly limits its application and popularization

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Choose 3-year-old, larger-diameter bamboo, pre-cut and deknot the selected bamboo, and cut each section to a length of 50cm; vertically cut each section of bamboo to form a thin strip of bamboo; cook at a high temperature of 100°C 1h; after taking it out, place it on a hollow shelf, place a heater under the shelf for drying, and control the temperature of the heater at 60°C for 3 hours; at the same time, there is a hair dryer on the side of the shelf for intermittent blowing, with a low wind speed of 3m / s. The blowing lasts for 5 minutes each time, and the interval is 10 minutes each time; at the same time, there is an ultraviolet germicidal lamp vertically irradiated above the shelf, the wave band is 200nm, the intensity is 20uw / cm2, and the irradiation is carried out for 2 hours; it is crushed into bamboo powder; for mixing, take 70 parts of bamboo powder, silicon powder 5 parts, 8 parts of mica powder, 6 parts of starch, 20 parts of water, 15 parts of PVC powder, stir...

Embodiment 2

[0024] Choose 3-year-old, larger-diameter bamboo, and first cut and remove knots from the selected bamboo. After cutting, each section has a length of 80cm; vertically cut each section of bamboo to form a thin and long strip of bamboo; cook at a high temperature of 120°C 1h; after taking it out, place it on a hollow shelf, place a heater under the shelf for drying, and control the temperature of the heater at 40°C for 4 hours; at the same time, there is a hair dryer on the side of the shelf for intermittent blowing, with a low wind speed of 5m / s, every The blowing lasts for 5 minutes, and the interval is 10 minutes each time; at the same time, there is an ultraviolet germicidal lamp irradiated vertically above the shelf, the wave band is 250nm, the intensity is 30uw / cm2, and the irradiation is carried out for 2 hours; it is crushed into bamboo powder; for mixing, take 90 parts of bamboo powder, silicon powder 10 parts, 3 parts of mica powder, 4 parts of starch, 30 parts of wate...

Embodiment 3

[0026] Choose 4-year-old bamboo with a larger diameter, and first cut and remove the knots from the selected bamboo. After cutting, each section has a length of 60cm; each section of bamboo is vertically cut to form a thin and long strip of bamboo; high temperature 110°C cooking 0.5h; after taking it out, place it on a hollow shelf, place a heater under the shelf for drying, and control the temperature of the heater at 50°C for 5 hours; at the same time, there is a hair dryer on the side of the shelf for intermittent blowing, with a low wind speed of 4m / s. Each blow lasts for 5 minutes, and each interval is 10 minutes; at the same time, there is an ultraviolet germicidal lamp irradiated vertically above the shelf, the wave band is 220nm, the intensity is 25uw / cm2, and the irradiation is carried out for 3 hours; it is crushed into bamboo powder; for mixing, take 80 parts of bamboo powder, silicon 80 parts of mica powder, 5 parts of mica powder, 5 parts of starch, 20 parts of wat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A preparation method of high-strength fireproof corrosion-resistant type bamboo boards comprises the following steps that selected bamboo wood is cut primarily, and bamboo joints are removed; perpendicular sectioning is conducted, so that thin type long-strip-shaped bamboo wood is formed; the thin type long-strip-shaped bamboo wood is steamed for 0.5-1 h at the high temperature of 100-120 DEG C; the thin type long-strip-shaped bamboo wood is placed on a hollowed-out rack to be dried, blown and irradiated with ultraviolet rays; the thin type long-strip-shaped bamboo wood is smashed into bamboo powder; materials are mixed, wherein 70-90 parts of the bamboo powder, 5-10 parts of silica powder, 3-8 parts of mica powder, 4-6 parts of starch, 20-30 parts of water and 15-25 parts of PVC powder are fetched and stirred to be evenly mixed; then, 15-30 parts of bonding adhesive is added and stirred to be evenly mixed with the mixture; aging is conducted; pressing and solidifying are conducted; and the surfaces of obtained products are coated with a nanometer-scale fireproof coating material. The bamboo wood is pretreated through preceding processes, so that the moisture and sugar in the bamboo wood are greatly reduced; besides, ultraviolet irradiation is also conducted, and formula auxiliary materials are added during material mixing; and in this way, the strength, the fire resistance, the inspect preventing performance and the corrosion resistance of the final bamboo boards are improved, and the application range of the bamboo boards is widened.

Description

technical field [0001] The invention relates to a bamboo board technology, in particular to a method for preparing a high-strength fire-resistant and anti-corrosion bamboo board. Background technique [0002] In the building materials industry, particle board is widely used as a kind of particle board, occupying a place in the market with its low cost and mature technology, and becoming the choice of most furniture design and decoration design. However, the environmental protection performance and durability of this kind of board are all unsatisfactory. Bamboo board has excellent physical properties, and has the advantages of small coefficient of water absorption, no cracking, no deformation, etc., and it is currently emerging rapidly. The existing bamboo board preparation process is mostly prepared by cutting, crushing, mixing, curing, pressing, and curing, and can obtain relatively high-quality environmentally friendly bamboo boards, but its strength is not ideal, and the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B27N3/04B27N7/00B27N1/00B27K5/00B27K5/04B27K9/00C08L97/02C08L3/02C08L27/06C08K3/36C08K3/34
CPCB27N3/04B27K5/00B27K5/0085B27K5/04B27K9/002B27K2240/20B27N1/00B27N7/005C08L97/02C08L2205/035
Inventor 王定超
Owner 叙永县象实竹木业有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products