Polycarbonate composition with antibacterial function

A polycarbonate and composition technology, which is applied in building structures, building components, building insulation materials, etc., to achieve the effects of low cost of raw materials, protection of human health, and good sterilization and antibacterial functions

Inactive Publication Date: 2017-03-15
佛山市高明区生产力促进中心
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there is no relatively efficient polycarbonate composition with antibacterial function

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0014] The preparation method of the polycarbonate composition with antibacterial function comprises the following steps:

[0015] (1) After weighing each constituent raw material according to the formula ratio, place it separately;

[0016] (2) Preheat the polycarbonate to 90°C and set aside;

[0017] (3) Cedar wood oil, nano-silver oxide, Cathone, triethanolamine, isothiazolinone, 2-hydroxyethylamine, pentachlorophenol, omethoate, imidacloprid, cypermethrin, 8-hydroxyquinoline copper, asphalt horseshoe Grease, 4-dipalmitoylproline, cyanoacrylate, crotonaldehyde, copper sulfate pentahydrate, Thiobacterium copper, oxazolidinones, bis-imidazolidinyl urea were put into the mixer, at a temperature of 102 ℃ After stirring at a speed of 90r / min for 50min, then put the plasticizer and antistatic agent into the mixer, and at a temperature of 105°C, stir at a speed of 85r / min for 60min and set aside;

[0018] (4) Put the materials of steps (2) and (3) together into a twin-screw extr...

Embodiment 1

[0020] A polycarbonate composition with antibacterial function, the composition raw materials include: 106 parts of polycarbonate, 28 parts of cedar wood oil, 13 parts of nano-silver oxide, 18 parts of Cathone, 18 parts of triethanolamine, 12 parts of isothiazolinone, 14 parts of 2-hydroxyethylamine, 5 parts of pentachlorophenol, 5 parts of omethoate, 3 parts of imidacloprid, 16 parts of cypermethrin, 15 parts of 8-hydroxyquinoline copper, 8 parts of asphalt mastic, 4-dipalmitoyl Amino acid 11 parts, cyanoacrylate 16 parts, crotonaldehyde 22 parts, copper sulfate pentahydrate 19 parts, Thiobacterium copper 12 parts, oxazolidinones 22 parts, diazolidinyl urea 15 parts, plasticizer 25 parts 28 parts, antistatic agent.

Embodiment 2

[0022] A polycarbonate composition with antibacterial function, the composition raw materials include: 95 parts of polycarbonate, 25 parts of cedar oil, 10 parts of nano-silver oxide, 15 parts of Cathone, 14 parts of triethanolamine, 8 parts of isothiazolinone, 9 parts of 2-hydroxyethylamine, 3 parts of pentachlorophenol, 2 parts of omethoate, 1 part of imidacloprid, 14 parts of cypermethrin, 11 parts of 8-hydroxyquinoline copper, 5 parts of asphalt mastic, 4-dipalmitoylpreserve Amino acid 8 parts, cyanoacrylate 14 parts, crotonaldehyde 20 parts, copper sulfate pentahydrate 15 parts, Thiobacterium copper 9 parts, oxazolidinones 17 parts, diazolidinyl urea 13 parts, plasticizer 21 parts 25 parts, antistatic agent.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a polycarbonate composition with an antibacterial function and relates to the technical field of high polymer materials. The polycarbonate composition is prepared from the following raw materials: 95 to 110 parts of polycarbonate, 25 to 30 parts of cedarwood oil, 10 to 15 parts of nano silver oxide, 15 to 20 parts of 5-chloro-2-methyl-4-isothiazolin-3-one, 14 to 22 parts of triethanolamine, 8 to 15 parts of isothiazolinone, 9 to 17 parts of 2-hydroxyethylamine, 3 to 7 parts of pentachlorophenol, 2 to 8 parts of omethoate, 1 to 4 parts of imidacloprid, 14 to 19 parts of cypermethrin, 11 to 20 parts of copper 8-hydroxyquinoline, 5 to 12 parts of asphalt mastic, 8 to 14 parts of 4-dipalmitoyl hydroxyproline, 14 to 19 parts of cyanoacrylate, 20 to 25 parts of crotonaldehyde and 15 to 23 parts of copper sulfate pentahydrate. The polycarbonate composition provided by the invention has the beneficial effects that the raw materials are low in price, and a preparation process is simple; the prepared polycarbonate composition has the functions of inhibiting and killing bacteria.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to a polycarbonate composition with antibacterial function. Background technique [0002] Polycarbonate (referred to as PC) is a high molecular polymer containing carbonate groups in the molecular chain. According to the structure of the ester group, it can be divided into aliphatic, aromatic, aliphatic-aromatic and other types. Polycarbonate resin is known for its excellent impact resistance, dielectric properties, high heat resistance, high dimensional stability, high transparency, high flame retardancy, UV radiation resistance, coloring properties, FDA compliance, easy reinforcement and The physical modification potential of chemical modification has rapidly formed a global commodity, and its production scale is also increasing. It has become the second largest engineering plastic after polyamide (PA), and is widely used in electronics, electrical appliances, and automo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L69/00C08L91/00C08L95/00C08K13/02C08K3/22C08K5/17C08K5/47C08K5/5398
Inventor 贺海兰
Owner 佛山市高明区生产力促进中心
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap