Ecological antibacterial high-sensitivity polyester fiber and method for producing same

A polyester fiber and production method technology, applied in the field of ecological antibacterial high-sensitivity polyester fiber and its production, can solve the problems of low comfort and wearability, antibacterial effect, poor dimensional stability of breathable and moisture permeability, etc. Ease of operation and the effect of increasing productivity

Active Publication Date: 2017-03-15
ZHEJIANG JINXIA NEW MATERIAL TECH CO LTD +1
View PDF4 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This technology solves the problems of warp knitted fabrics in the prior art, such as poor antibacterial effect, poor air permeability and moisture permeability, and dimensional stability, and low comfort and wearability of the product

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ecological antibacterial high-sensitivity polyester fiber and method for producing same
  • Ecological antibacterial high-sensitivity polyester fiber and method for producing same
  • Ecological antibacterial high-sensitivity polyester fiber and method for producing same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0057] An ecological antibacterial high-sensitivity polyester fiber, its breaking strength is 2.0-3.5cN / dtex, and its fracture growth rate is 10-25%. More than 90%, the antibacterial rate of Escherichia coli is greater than 92%; the far-infrared emission rate of ecological antibacterial high-sensitivity polyester fiber is greater than 85%.

[0058] Please see attached figure 1 , a kind of production method of ecological antibacterial high-sensitivity polyester fiber, its specific steps are:

[0059] (1) Preparation of ecological antibacterial high-sensitivity masterbatch, with high-efficiency antibacterial agent, modified bamboo charcoal powder, polyethylene glycol as raw materials, through the method of twin-screw melt blending extrusion, to prepare ecological antibacterial high-sensitivity masterbatch;

[0060] The high-efficiency antibacterial agent is a novel antibacterial agent containing amino antibacterial groups, specifically bisdimethylaminoethanol pentaerythritol di...

Embodiment 2

[0078] An ecological antibacterial high-sensitivity polyester fiber, its breaking strength is 2.0-3.5cN / dtex, and its fracture growth rate is 10-25%. More than 90%, the antibacterial rate of Escherichia coli is greater than 92%; the far-infrared emission rate of ecological antibacterial high-sensitivity polyester fiber is greater than 85%.

[0079] A kind of production method of ecological antibacterial high-sensitivity polyester fiber, its specific steps are:

[0080] (1) Preparation of ecological antibacterial high-sensitivity masterbatch, with high-efficiency antibacterial agent, modified bamboo charcoal powder, polyethylene glycol as raw materials, through the method of twin-screw melt blending extrusion, to prepare ecological antibacterial high-sensitivity masterbatch;

[0081] The high-efficiency antibacterial agent is a novel antibacterial agent containing amino antibacterial groups, specifically bisdimethylaminoethanol pentaerythritol diphosphate.

[0082] The prepara...

Embodiment 3

[0096] An ecological antibacterial high-sensitivity polyester fiber, its breaking strength is 2.0-3.5cN / dtex, and its fracture growth rate is 10-25%. More than 90%, the antibacterial rate of Escherichia coli is greater than 92%; the far-infrared emission rate of ecological antibacterial high-sensitivity polyester fiber is greater than 85%.

[0097] A kind of production method of ecological antibacterial high-sensitivity polyester fiber, its specific steps are:

[0098] (1) Preparation of ecological antibacterial high-sensitivity masterbatch, with high-efficiency antibacterial agent, modified bamboo charcoal powder, polyethylene glycol as raw materials, through the method of twin-screw melt blending extrusion, to prepare ecological antibacterial high-sensitivity masterbatch;

[0099] The high-efficiency antibacterial agent is a novel antibacterial agent containing amino antibacterial groups.

[0100] The preparation method of bis-dimethylaminoethanol pentaerythritol diphosphat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Breaking strengthaaaaaaaaaa
Intrinsic viscosityaaaaaaaaaa
Login to View More

Abstract

The invention relates to an ecological antibacterial high-sensitivity polyester fiber and a method for producing the same. The method includes particular steps of (1), preparing ecological antibacterial high-sensitivity master batch from efficient antibacterial agents, modified bamboo charcoal powder and polyethylene glycol by the aid of double-screw melt blending extrusion processes; (2), preparing ecological antibacterial high-sensitivity polyester fibers, to be more specific, spinning and extruding conventional polyester chips by the ecological antibacterial high-sensitivity master batch prepared at the step (1) by the aid of melt blending spinning processes via spinning assemblies, cooling virgin fibers by means of circular air blowing, applying oil to clusters and carrying out drawing, heat-setting and winding to obtain the ecological antibacterial high-sensitivity polyester fiber. The ecological antibacterial high-sensitivity master batch is used as a modification auxiliary at the step (2). The ecological antibacterial high-sensitivity polyester fiber and the method have the advantages that the antibacterial performance of the ecological antibacterial high-sensitivity polyester fiber include that the antibacterial rate of the ecological antibacterial high-sensitivity polyester fiber for staphylococcus aureus is higher than 90%, and the antibacterial rate of the ecological antibacterial high-sensitivity polyester fiber for Escherichia coli is higher than 92%; the far infrared emittance of the ecological antibacterial high-sensitivity polyester fiber is higher than 85%.

Description

[0001] 【Technical field】 [0002] The invention relates to the technical field of functional polyester fibers, in particular to an ecological antibacterial high-sensitivity polyester fiber and a production method thereof. [0003] 【Background technique】 [0004] In the field of home textiles and decorative textiles, antibacterial properties are the most important indicators. However, the currently used synthetic fibers do not have antibacterial properties, so external antibacterial agents are often used for antibacterial modification of fibers; the current preparation methods It is mainly post-processing, and the antibacterial properties of fibers or fabrics are modified by coating and finishing fibers or fabrics with antibacterial agents on the surface and finishing them with antibacterial oils. The substrate with polar functional groups has a very good effect, and the ionic bonding between polar functional groups is used to improve the adhesion of the finishing agent. However...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D01F6/92D01F1/10C08K5/521C08K3/04C08L71/02C07F9/6574A01N57/36A01P3/00A01P7/02
CPCA01N57/36C07F9/65746C08K3/04C08K5/521D01F1/103D01F6/92C08L71/02Y02P20/54
Inventor 张志明
Owner ZHEJIANG JINXIA NEW MATERIAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com