a foam cement

A foamed cement and cement technology, applied in the field of foamed cement, can solve the problems of long time required for setting and curing, and achieve significant economic and social benefits, good thermal insulation effect, and good waterproof performance.

Active Publication Date: 2019-04-26
北京宝辰联合科技股份有限公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In this process, after the cement slurry is foamed, it needs to be cured for 4 hours before it can be removed from the mold, and it can be cut after 7 days of continuous curing. It takes a long time to set and solidify

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • a foam cement
  • a foam cement
  • a foam cement

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A foamed cement, comprising the following components in mass percentage: 30% cement, 5% ceramic tile polishing powder, 1% foaming component, 0.1% foam stabilizing component, 0.5% waterproofing component, and 0.5% reinforcing component , The balance is water.

[0024] Among them, the cement is composed of Portland cement and aluminate cement in a mass ratio of 5:1; the alumina content in aluminate cement is 40%; the specific surface area of ​​ceramic tile polishing powder is greater than 600m 2 / kg; the foaming component is composed of hydrogen peroxide, fatty alcohol polyoxyethylene ether sodium sulfate and lauryl dimethyl betaine in a mass ratio of 5:2:1; the foam stabilizing component is composed of hydroxypropyl starch ether and lauryl Acyl diethanolamine is composed of 0.5:1 by mass ratio; the waterproof component is composed of water glass, sodium fluorosiliconate and triethanolamine phosphate by mass ratio of 1:2:1; the reinforcing component is composed of diethan...

Embodiment 2

[0026] A foamed cement, comprising the following components in mass percentage: 45% cement, 10% ceramic tile polishing powder, 4% foaming component, 1% foam stabilizing component, 2% waterproofing component, and 2% reinforcing component , The balance is water.

[0027] The cement is composed of Portland cement and aluminate cement in a mass ratio of 10:1; the alumina content in aluminate cement is 45%; the specific surface area of ​​ceramic tile polishing powder is greater than 600m 2 / kg; the foaming component is composed of hydrogen peroxide, fatty alcohol polyoxyethylene ether sodium sulfate and lauryl dimethyl betaine in a mass ratio of 10:0.5:1; the foam stabilizing component is composed of hydroxypropyl starch ether and lauryl Acyl diethanolamine is composed of 2:1 by mass ratio; the waterproof component is composed of water glass, sodium fluorosilicone and triethanolamine phosphate by mass ratio of 2:0.5:1; the reinforcing component is composed of diethanol monoisopropa...

Embodiment 3

[0029] A foamed cement, comprising the following components in mass percentage: 40% cement, 8% ceramic tile polishing powder, 3% foaming component, 0.5% foam stabilizing component, 1% waterproofing component, and 1 reinforcing component %, the balance is water.

[0030] The cement is composed of Portland cement and aluminate cement in a mass ratio of 8:1; the alumina content in aluminate cement is 50%; the specific surface area of ​​ceramic tile polishing powder is greater than 600m 2 / kg; the foaming component is composed of hydrogen peroxide, fatty alcohol polyoxyethylene ether sodium sulfate and lauryl dimethyl betaine in a mass ratio of 5:1:1; the foam stabilizing component is composed of hydroxypropyl starch ether and lauryl Acyl diethanolamine is composed of 1:1 mass ratio; the waterproof component is composed of water glass, sodium fluorosilicone and triethanolamine phosphate in a mass ratio of 1:1:1; the reinforcing component is composed of diethanol monoisopropanolami...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention discloses foaming cement which comprises the following components in percentage by mass: 30-45% of cement, 5-10% of ceramic brick polishing powder, 1-4% of a foaming component, 0.1-1% of a foam stabilizing component, 0.5-2% of a waterproof component, 0.5-2% of a reinforcing component and the balance water, wherein cement is composed of silicate cement and aluminate cement in a mass ratio of (5-10) to 1. The foaming cement disclosed by the invention has the characteristics of high strength, good waterproof performance, good thermal insulation effect, good durability and the like; and a great deal of ceramic brick polishing powder further can be comprehensively utilized, so that social resources are saved, using efficiency is improved, and economic benefits and social benefits are remarkable.

Description

technical field [0001] The invention belongs to the technical field of building energy conservation, and in particular relates to foamed cement. Background technique [0002] According to statistics, the heating energy consumption of buildings in my country is three times that of developed countries with similar climatic conditions. In order to improve the thermal insulation function of buildings, adding insulation layers to buildings is an important measure for building energy conservation. It is made of polystyrene board, extruded board, polyurethane and other organic materials, but organic insulation materials have disadvantages such as flammability and aging. Foamed cement is an inorganic thermal insulation material, which has the advantages of light weight, non-combustibility, thermal insulation, and the same lifespan as the building, and has a good application prospect. [0003] Foamed cement is mainly formed by introducing air bubbles through chemical or physical foam...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/06C04B38/10C04B38/02
CPCC04B28/06C04B38/02C04B38/10C04B2111/27C04B7/02C04B18/165C04B22/068C04B24/166C04B24/12C04B24/38C04B24/122C04B14/045C04B24/005C04B22/148C04B22/002
Inventor 王义
Owner 北京宝辰联合科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com