Pretreatment slurry for cashmere fabric digital printing and printing technology of cashmere fabric digital printing

A digital printing and fabric technology, applied in textiles and papermaking, dyeing, dry-cleaning fiber products, etc., can solve the problems of cashmere fiber damage, poor adsorption and permeability, poor fabric dyeing, etc., to reduce damage, reduce hindrance, color fastness high degree of effect

Inactive Publication Date: 2017-03-29
TIANJIN POLYTECHNIC UNIV
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Specifically, the hydrophobic lipid layer on the surface of the cashmere fiber and the highly cross-linked and dense outer cuticle prevent the diffusion and transfer of the dye molecules to the inside of the fiber through the scale l...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Pretreatment slurry for cashmere fabric digital printing and printing technology of cashmere fabric digital printing
  • Pretreatment slurry for cashmere fabric digital printing and printing technology of cashmere fabric digital printing
  • Pretreatment slurry for cashmere fabric digital printing and printing technology of cashmere fabric digital printing

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] A kind of cashmere fabric pre-treatment pulp, prepared according to the following formula:

[0037]

[0038] Cashmere fabric digital printing process: sizing→drying (temperature 40°C, time 10min)→steaming (temperature 100°C, time 60min)→cold water washing (room temperature, 10min)→soaping (soaping agent A2g / L, alginic acid cracking Enzyme 1mg / L, Na 2 CO 3 0.5g / L, temperature 60°C, time 5min) → hot water wash (temperature 60°C, time 5min) → warm and cold water wash (room temperature, 5min)

[0039] According to the above-mentioned pretreatment and printing process, the k / s value of the printed fabric is 27, compared with the ratio of TCEP and sodium dodecylsulfonate not added in the pretreatment pulp, the increased value is 17, and the dry rubbing fastness is 4-5 grades, Wet rubbing fastness is grade 4, soaping and fading fastness is grade 4, cotton staining grade 4-5, wool staining grade 4-5.

Embodiment 2

[0041] A kind of cashmere fabric pre-treatment pulp, prepared according to the following formula:

[0042]

[0043] Cashmere fabric digital printing process: sizing→drying (temperature 40°C, time 10min)→steaming (temperature 100°C, time 60min)→cold water washing (room temperature, 10min)→soaping (soaping agent A 2g / L, alginic acid Lyase 1mg / L, Na 2 CO 3 0.5g / L, temperature 60°C, time 5min) → hot water wash (temperature 60°C, time 5min) → warm and cold water wash (room temperature, 5min)

[0044] The k / s value of the printed fabric according to the above-mentioned pretreatment and printing process is 18, compared with the ratio of TCEP and lauryl betaine not added in the pretreatment pulp, the increase value is 12, and the dry rubbing fastness is 4-5 grades, wet Rubbing fastness is grade 4, soaping and fading fastness is grade 3-4, cotton staining grade 4-5, wool staining grade 4-5.

Embodiment 3

[0046] A kind of cashmere fabric pre-treatment pulp, prepared according to the following formula:

[0047]

[0048] Cashmere fabric digital printing process: sizing→drying (temperature 40°C, time 10min)→steaming (temperature 100°C, time 60min)→cold water washing (room temperature, 10min)→soaping (soaping agent A 2g / L, alginic acid Lyase 1mg / L, Na2CO3 0.5g / L, temperature 60°C, time 5min) → hot water wash (temperature 60°C, time 5min) → warm and cold water wash (room temperature, 5min)

[0049] The k / s value of the printed fabric according to the above-mentioned pretreatment and printing process is 12, compared with the ratio of TCEP and sodium dodecylsulfonate not added in the pretreatment slurry, the increased value is 5, the dry rubbing fastness is 4 grades, and the wet rubbing fastness is 4 grades. The fastness is 3-4 grades, the color fastness to soaping and fading is 3-4 grades, the cotton staining is 4-5 grades, and the wool staining is 4-5 grades.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a pretreatment slurry for cashmere fabric digital printing and a printing technology of cashmere fabric digital printing. The pretreatment slurry is composed of sodium alginate paste, plant seed gelatine KCA-90 paste, TCEP, penetrant, urea, ammonium sulfate and water; the printing technology of cashmere fabric digital printing comprises the steps of sizing; conducting drying at the temperature of 40 DEG C for 10 min; conducting steaming at the temperature of 85 DEG C for 4-5 min; conducting cold washing at the room temperature for 10 min; conducting soaping at the temperature of 60 DEG C for 5 min with soaping agent A being 2g/L, and alginate lyase being 1 mg/L, and Na2CO3 being 0.5g/L; conducting hot washing at the temperature of 60 DEG C for 5 min; conducting cold washing at the room temperature for 5 min. By combining the pretreatment processing and the digital printing technology, the obtained printing cashmere fabric is high in tinctorial yield, uniform in color, free of phenomenon of grinning of white ground, clear in floral pattern margin, and good in color fastness.

Description

technical field [0001] The invention relates to the field of digital printing, in particular, the invention relates to a cashmere fabric digital printing pretreatment slurry and a digital printing process. Background technique [0002] Cashmere is a natural fiber with many excellent properties that other fibers cannot match. It is called "diamond fiber" and is favored by consumers. From the perspective of international clothing consumption and textile technology development trends, the demand for high-end cashmere printed products is increasingly strong in the international market, but my country's current deep-processing technology and models of cashmere products can no longer meet the increasingly diverse development needs of the market. Due to the limitations of cashmere fiber characteristics and traditional weaving techniques, most of the patterns and patterns of cashmere products in my country are realized by weaving methods such as jacquard and intarsia, which makes it...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06P3/14D06P1/48D06P1/62D06P1/649D06P1/66D06P1/667D06P1/673D06P5/30D06L1/16
CPCD06P3/14D06L1/16D06P1/48D06P1/623D06P1/6497D06P1/66D06P1/667D06P1/67333D06P5/30
Inventor 田俊莹何天虹秦跃赵伟林张芳芳
Owner TIANJIN POLYTECHNIC UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap