A kind of long-acting antibacterial thermal underwear and preparation method thereof

A thermal underwear and long-lasting technology, applied in the field of clothing, can solve the problems of artificial synthetic fibers not being skin-friendly enough, thermal insulation effect needs to be improved, silver particles are not stable enough, etc., and achieve the effect of good thermal insulation effect, stable structure and convenient finishing

Inactive Publication Date: 2018-05-04
柯华
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Adding nano-silver to thermal underwear to make antibacterial underwear has a long history, but they generally add nano-silver particles in the process of making synthetic fibers, or soak the cloth in a silver-containing solution, and then let the silver absorb Deposited on the surface of the cloth; the defect of the former is that the artificial synthetic fibers are not skin-friendly enough, and the warmth retention effect needs to be improved, while the defect of the latter is that the silver particles deposited on the surface of the cloth are not stable enough, and it is easy to fail after repeated washing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] In step (1), the mass fraction of the acetone solution is 10%, the soaking time is 1h, and the liquid squeeze rate is 80%; the pH value of the strong alkali solution is 14, and it is reacted at 80°C for 2h; wherein, the The strong alkali solution mainly includes one of sodium hydroxide and potassium hydroxide, and the acid is one of dilute hydrochloric acid, dilute nitric acid and dilute sulfuric acid;

[0034] In step (2), at first preparation graphene oxide concentration is the graphene oxide aqueous solution of 20g / L and Ag + Concentration is the silver-ammonia solution of 2g / L, then according to the ratio that volume ratio is 1:1, described graphene oxide aqueous solution and described silver-ammonia solution are evenly mixed together;

[0035] In step (4), the extruded water is 80% of the total water absorption of cotton fibers;

[0036] In step (5), the ascorbic acid solution concentration is 20g / L, and the volume ratio of the cotton fiber and ascorbic acid solut...

Embodiment 2

[0042] In the step (1), the mass fraction of the acetone solution is 15%, the soaking time is 50min, and the squeeze rate is 78%; the pH value of the strong alkali solution is 13.5, and the reaction is carried out at 82°C for 1h45min; wherein, the The strong alkali solution mainly includes one of sodium hydroxide and potassium hydroxide, and the acid is one of dilute hydrochloric acid, dilute nitric acid and dilute sulfuric acid;

[0043] In step (2), at first preparation graphene oxide concentration is the graphene oxide aqueous solution of 40g / L and Ag + Concentration is the silver-ammonia solution of 4g / L, then according to the ratio that volume ratio is 1:1, described graphene oxide aqueous solution and described silver-ammonia solution are evenly mixed together;

[0044]In step (4), the extruded water is 75% of the total water absorption of cotton fibers;

[0045] In step (5), the ascorbic acid solution concentration is 40g / L, and the volume ratio of the cotton fiber and...

Embodiment 3

[0051] In step (1), the mass fraction of the acetone solution is 20%, the soaking time is 40min, and the liquid squeeze rate is 75%; the pH value of the strong alkali solution is 13, and it is reacted at 85°C for 1h30min; wherein, the The strong alkali solution mainly includes one of sodium hydroxide and potassium hydroxide, and the acid is one of dilute hydrochloric acid, dilute nitric acid and dilute sulfuric acid;

[0052] In step (2), at first preparation graphene oxide concentration is the graphene oxide aqueous solution of 60g / L and Ag + Concentration is the silver-ammonia solution of 6g / L, then according to the ratio that volume ratio is 1:1, described graphene oxide aqueous solution and described silver-ammonia solution are evenly mixed together;

[0053] In step (4), the extruded water is 70% of the total water absorption of cotton fibers;

[0054] In step (5), the ascorbic acid solution concentration is 60g / L, and the volume ratio of the cotton fiber and ascorbic ac...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
concentrationaaaaaaaaaa
quality scoreaaaaaaaaaa
Login to view more

Abstract

The invention discloses long-acting antibacterial warm-keeping underwear and a preparation method thereof. The underwear is mainly prepared by blending foamed silver / graphene / cotton fiber compound and untreated cotton fibers, wherein the foamed silver / graphene / cotton fiber compound is prepared by the following steps: pretreating cotton fibers; then, soaking into a mixed solution of silver ammonia and graphene oxide; putting cotton fibers containing Ag<+> and graphene oxide into an ascorbic acid solution; and performing hydrothermal reduction, quickly freezing for molding, and lyophilizing in vacuum. The long-acting antibacterial warm-keeping underwear prepared by the method has the advantages of long antibacterial effect, good insulating effect, strong air permeability and good perspiration absorbability, can be easily washed, is able to bear rubbing, and is extremely convenient to arrange.

Description

technical field [0001] The invention belongs to the field of clothing, in particular to a long-acting antibacterial thermal underwear and a preparation method thereof. Background technique [0002] The material of thermal underwear is required to be light, soft, skin-friendly and breathable. Existing thermal underwear often adopts cotton fiber and artificial synthetic fiber to make, and the warming effect of cotton fiber is not ideal enough, and artificial synthetic fiber easily causes skin allergy, dry, rough, thickening, even chapped, dermatitis etc. occur. In addition, people wear more clothes in winter, and it is not easy to get rid of them in time after sweating, which causes bacteria to easily breed in the thermal underwear in the inner layer. [0003] The latest research has found that silver has an adsorption effect on microorganisms in the liquid. After the microorganisms are adsorbed by silver, the enzymes that play a role in respiration will lose their effectiven...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): A41B17/00D06M11/83C08J9/28D06M101/06
CPCA41B17/00A41B2400/34C08J9/28C08J2201/0484C08J2205/026C08J2301/02D06M11/83D06M16/00D06M2101/06
Inventor 刘丽蓉王勇丁超
Owner 柯华
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap