A nanoparticle and tin dioxide technology, applied in the direction of tin oxide, etc., can solve the problems of non-spherical tin dioxide preparation, difficult growth and design materials, lengthy preparation process, etc., and achieve low cost, low price and high chemical activity. Effect

Inactive Publication Date: 2017-05-10
JILIN UNIV
View PDF5 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention is that, compared with spherical structures, due to the lack of non-spherical templates, the lengthy preparation process and the accompanying high cost, and the difficulty in growing design materials on the high-curvature edges of the templates, non-spherical two The preparation of tin oxide is still difficult

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method for hierarchical hollow cubic stannic oxide nanometer particle
  • Preparation method for hierarchical hollow cubic stannic oxide nanometer particle
  • Preparation method for hierarchical hollow cubic stannic oxide nanometer particle

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Weigh 17mg of ZnO, 240mg of NaOH, 292mg of CTAB and 210mg of SnCl 4 , then dissolve ZnO, NaOH, and CTAB with 25mL deionized water and stir for 5min, then dissolve SnCl with 5ml deionized water 4 , and then add the SnCl4 solution dropwise to the aqueous solution containing ZnO, NaOH, and CTAB, fully stir for 10 minutes and then let it stand for 24 hours, then stir the solution for 5 minutes and then transfer it to a hydrothermal reaction kettle, and conduct a hydrothermal reaction at 180°C for 12 hours. After the reaction, wash with deionized water and absolute ethanol for three times each, and then dry the precipitate at 60°C in an air atmosphere to collect hierarchical hollow cube-shaped tin dioxide nanoparticles composed of ultrafine nanorods. The scanned picture See attached figure 1 , the transmission scan picture is attached figure 2 .

[0031] The X-ray diffraction pattern of the hierarchical hollow cube-shaped tin dioxide nanoparticles composed of one-dimensi...

Embodiment 2

[0033] Weigh 17mg of ZnO, 240mg of NaOH, 292mg of CTAB and 210mg of SnCl 4 , then dissolve ZnO, NaOH, and CTAB with 25mL deionized water and stir for 5min, then dissolve SnCl with 5ml deionized water 4 , and then add the SnCl4 solution dropwise to the aqueous solution containing ZnO, NaOH, and CTAB, fully stir for 10 minutes and then let it stand for 24 hours, then stir the solution for 5 minutes and then transfer it to a hydrothermal reaction kettle, and conduct a hydrothermal reaction at 200 ° C for 12 hours. After the reaction was completed, each was washed with deionized water and absolute ethanol for three times, and then the precipitate was dried at 60°C in an air atmosphere to collect hierarchical hollow cube-shaped tin dioxide nanoparticles composed of a mixture of nanosheets and nanorods. The scanned picture is attached Figure 5 , the transmission scan picture is attached Image 6 .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to a preparation method for a hierarchical hollow cubic stannic oxide nanometer particle composed of ultrafine nano-rods and belongs to the technical field of nanometer material preparation. The method comprises the following steps: taking solid cubic zinc hydroxystannate as a precursor, covering a layer of stannic oxide nano-rods on the surface of the zinc hydroxystannate after the hydrothermal reaction for a period of time, and meanwhile, decomposing the inner zinc hydroxystannate, thereby acquiring the hierarchical hollow cubic stannic oxide nanometer particle composed of the ultrafine nano-rods in the shape similar to the shape of zinc hydroxystannate. Compared with the traditional template method, the preparation method has the advantages of low cost, few steps and simple operation; the prepared hollow stannic oxide nanometer particle has an obvious hierarchical structure and a mesoporous structure, is difficult to agglomerate, is excellent in crystallinity and is high in specific surface area; the hierarchical hollow cubic stannic oxide nanometer particle is composed of a large quantity of orderly arrayed nano-rods and the size of the nano-rods is close to the debye length; the air-sensitive characteristic is excellent; and the hierarchical hollow cubic stannic oxide nanometer particle has a potential application value in the field of air-sensitive sensors.

Description

technical field [0001] The invention belongs to the technical field of nanomaterial preparation, and in particular relates to a method for preparing hierarchical hollow cubic tin oxide nanoparticles composed of ultrafine nanorods. This type of hierarchical hollow structure exhibits excellent performance in the field of gas sensors. gas-sensing performance. Background technique [0002] In recent years, hierarchical hollow structure nanomaterials with various morphologies have received more and more attention in the fields of fundamental research and practical applications. Its applications include drug delivery, catalysis, gas sensing, clean energy conversion, energy storage, etc. Today, the best way to prepare a well-formed hollow structure consists of coating the desired material on a removable template, or transforming it with preformed particles according to different principles (chemical displacement method, Kirkendall effect, acid-base etching, etc.) generate. Altho...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C01G19/02
CPCC01G19/02C01P2002/72C01P2004/03C01P2004/04C01P2004/38C01P2004/62
Inventor 曾毅王艳哲郑伟涛
Owner JILIN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap