Anti-scale inhibitor for treating industrial circulating water

A scale and corrosion inhibitor, industrial circulating water technology, applied in water/sludge/sewage treatment, special treatment targets, complexes/solubilizer treatment, etc., can solve the problem of secondary pollution of phosphorus environment and achieve good compatibility Non-toxic, stable in nature and good in biodegradability

Inactive Publication Date: 2017-05-10
安徽省蓝天能源环保科技有限公司
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It has good performance and high stability, but phosphorus scale inhibitors are easy to be controlled

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0016] Example 1:

[0017] (1) A scale and corrosion inhibitor used in the treatment of industrial circulating water. The ingredients are weighed according to mass percentage: acrylic acid-hydroxypropyl acrylate copolymer 1.0%; ethylene-ethyl acrylate copolymer 0.5%; DETPMP 0.1%; 1-Boc-3-methylaminopyrrolidine 50%; PBTCA 0.1%; ATMP 0.1%; HEDP 0.03%; sodium nitrite 0.3%; acetaldehyde 0.5%; cyclohexylamine 14%; deionized water 25%.

[0018] (2) Install the dropping funnel, reflux condenser and thermometer in the four-neck flask, and the electric stirrer controls the stirring speed. First add deionized water and PBTCA to the four-necked flask, heat to about 70℃, stir to dissolve fully, and at a speed of 160 r / min, add ethylene-ethyl acrylate copolymer and the ring to the reaction device dropwise. Hexylamine, continue to heat up to 90°C and react for 2 hours;

[0019] (3) Add acetaldehyde, acrylic acid-hydroxypropyl acrylate copolymer and DETPMP, continue to heat up to about 100°C, and...

Example Embodiment

[0021] Example 2:

[0022] (1) A scale and corrosion inhibitor for industrial circulating water treatment, weighing ingredients according to mass percentage: acrylic acid-hydroxypropyl acrylate copolymer 1.5%; ethylene-ethyl acrylate copolymer 1.0%; DETPMP 0.3%; 1-Boc-3-methylaminopyrrolidine 55%; PBTCA 0.3%; ATMP 0.3%; HEDP 0.2%; sodium nitrite 0.5%; acetaldehyde 1.0%; cyclohexylamine 15%; deionized water 25%.

[0023] (2) Install the dropping funnel, reflux condenser and thermometer in the four-neck flask, and the electric stirrer controls the stirring speed. First add deionized water and PBTCA to the four-necked flask, heat to about 80℃, stir to dissolve fully, and at a speed of 160 r / min, add dropwise ethylene-ethyl acrylate copolymer and the ring to the reaction device. Hexylamine, continue to heat up to 100°C and react for 3 hours;

[0024] (3) Add acetaldehyde, acrylic acid-hydroxypropyl acrylate copolymer and DETPMP, continue to raise the temperature to about 100°C, and rea...

Example Embodiment

[0026] Example 3:

[0027] (1) A scale and corrosion inhibitor for industrial circulating water treatment. The ingredients are weighed according to mass percentage: acrylic acid-hydroxypropyl acrylate copolymer 2.0%; ethylene-ethyl acrylate copolymer 1.5%; DETPMP 0.5%; 1-Boc-3-methylaminopyrrolidine 60%; PBTCA 0.5%; ATMP 0.5%; HEDP 0.4%; sodium nitrite 1.0%; acetaldehyde 2.0%; cyclohexylamine 16%; deionized water 25%.

[0028] (2) Install the dropping funnel, reflux condenser and thermometer in the four-neck flask, and the electric stirrer controls the stirring speed. First add deionized water and PBTCA to the four-necked flask, heat to about 90℃, stir to dissolve fully, and at a speed of 160 r / min, add dropwise the ethylene-ethyl acrylate copolymer and the ring to the reaction device. Hexylamine, continue to heat up to 110°C and react for 4 hours;

[0029] (3) Add acetaldehyde, acrylic acid-hydroxypropyl acrylate copolymer and DETPMP, continue to heat up to about 115°C, and react ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an anti-scale inhibitor for treating industrial circulating water and relates to the technical field of industrial circulating water treatment. The anti-scale inhibitor comprises the following components by weight percent: 1.0-2.0% of crylic acid-crylic acid hydroxypropyl acrylate, 0.5-1.5% of ethylene-ethyl acrylate copolymer, 0.1-0.5% of DETPMP, 50-60% of 1-Boc-3-methylamino pyrrolidine, 0.1-0.5% of PBTCA, 0.1-0.5% of ATMP, 0.03-0.4% of HEDP, 0.3-1.0% of sodium nitrite, 0.5-2.0% of acetaldehyde, 14-16% of cyclohexane and 25% of deionized water. The dosing is reasonable; the preparation process is simple; the product is easy to dissolve oxygen; the oxygenation in water can be prevented; the anti-scale inhibitor is low in phosphorus content and excellent in biodegradability and can be compounded with various salt inhibiters.

Description

technical field [0001] The invention belongs to the field of chemical reagents, in particular to a scale and corrosion inhibitor used for industrial circulating water treatment. Background technique [0002] Industrial circulating water treatment is the process of removing some substances harmful to production and life in water through physical and chemical methods. Conditioning process. Industrial circulating water treatment methods are mainly divided into physical treatment and chemical treatment. Physical treatment technologies mainly include: magnetic treatment, electrostatic treatment, photochemical treatment, ultrasonic treatment, etc. Physical treatment technology has the advantages of simple operation, low operating cost, non-toxic and non-polluting. This method is suitable for water with low hardness, but the water treatment effect of complex water with high hardness in my country is not satisfactory. [0003] Chemical treatment technology usually adds a certain ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C02F5/14C02F5/10C02F5/08C02F5/12
CPCC02F5/105C02F5/125C02F5/145C02F2303/08
Inventor 王慈慈赵长艳伍金猴
Owner 安徽省蓝天能源环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap