Plasticizer

A plasticizer and adhesive technology, applied in the field of plasticizers, can solve the problems of poor environmental protection, human discomfort, unpleasant gas, etc., and achieve good high temperature resistance and low temperature resistance, high tensile strength, adhesion good performance

Inactive Publication Date: 2017-05-31
佛山市高明区生产力促进中心
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, most of the plasticizers currently used have poor environmental protection, poor plasticizing effect, and unsatisfactory stability. endanger human health

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A kind of plasticizer, composition comprises 33 parts of di-sec-octyl phthalate, 15 parts of polyvinyl chloride, 8 parts of chlorinated rubber, 3 parts of gel, 2 parts of binder, 13 parts of sodium carboxymethyl cellulose 1 part, 1 part of naphthalene, 2 parts of flying graphite;

[0017] The composition of the gel includes 18 parts of glycerin, 7 parts of latex, 2 parts of propylene oxide, 4 parts of ethylene oxide, 1 part of vaseline, and 3 parts of rhenium;

[0018] The composition of the adhesive includes 15 parts of fumed white carbon black, 3 parts of sodium bentonite, 2 parts of eucalyptol, 5 parts of menthol, 1 part of geraniol, 7 parts of jasmonate and 8 parts of epoxy resin.

[0019] Further, the preparation method of the gel is: (1) weigh glycerin, latex, propylene oxide, ethylene oxide, vaseline and rhenium according to the composition formula, stir evenly, and mix; (2) add water, water and material The mass ratio is 3:1, add water and then stir for 8 minut...

Embodiment 2

[0021] A plasticizer comprising 45 parts of di-sec-octyl phthalate, 26 parts of polyvinyl chloride, 19 parts of chlorinated rubber, 9 parts of gel, 7 parts of adhesive, 22 parts of sodium carboxymethyl cellulose 6 parts, 6 parts of naphthalene, 7 parts of flying graphite;

[0022] The composition of the gel includes 26 parts of glycerin, 15 parts of latex, 8 parts of propylene oxide, 12 parts of ethylene oxide, 6 parts of vaseline, and 11 parts of rhenium;

[0023] The composition of the adhesive includes 26 parts of fumed white carbon black, 8 parts of sodium bentonite, 6 parts of eucalyptol, 12 parts of menthol, 5 parts of geraniol, 16 parts of jasmonate and 20 parts of epoxy resin.

[0024] Further, the preparation method of the gel is: (1) weigh glycerin, latex, propylene oxide, ethylene oxide, vaseline and rhenium according to the composition formula, stir evenly, and mix; (2) add water, water and material The mass ratio is 3:1, add water and then stir for 16 minutes; (3...

Embodiment 3

[0026] A plasticizer, the composition includes 39 parts of dioctyl phthalate, 20 parts of polyvinyl chloride, 16 parts of chlorinated rubber, 6 parts of gel, 6 parts of adhesive, 18 parts of sodium carboxymethyl cellulose 4 parts, 4 parts of naphthalene, 4 parts of flying graphite;

[0027] The composition of the gel includes 21 parts of glycerin, 11 parts of latex, 5 parts of propylene oxide, 8 parts of ethylene oxide, 4 parts of vaseline, and 7 parts of rhenium;

[0028] The composition of the adhesive includes 19 parts of fumed white carbon black, 6 parts of sodium bentonite, 4 parts of eucalyptol, 8 parts of menthol, 3 parts of geraniol, 11 parts of jasmine, and 14 parts of epoxy resin.

[0029] Further, the preparation method of the gel is: (1) weigh glycerin, latex, propylene oxide, ethylene oxide, vaseline and rhenium according to the composition formula, stir evenly, and mix; (2) add water, water and material The mass ratio is 3:1, add water and then stir for 12 minut...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a plasticizer, and relates to the technical field of additives. The plasticizer comprises the following components: 33-45 parts of dicapryl phthalate, 15-26 parts of polyvinyl chloride, 8-19 parts of chlorinated rubber, 3-9 parts of gel, 2-7 parts of adhesive, 13-22 parts of sodium carboxymethylcellulose, 1-6 parts of naphthalene, and 2-7 parts of aerographite, wherein the gel comprises the following components: 18-26 parts of glycerinum, 7-15 parts of latex, 2-8 parts of epoxypropane, 4-12 parts of ethylene oxide, 1-6 parts of vaseline, and 3-11 parts of rhenium. The plasticizer has the beneficial effects that the cost is low; the formula is reasonable; the adhering performance is high; the tensile strength is high; in addition, the flavor of mint can be generated; the plasticizer is capable of sterilizing.

Description

technical field [0001] The invention relates to the technical field of additives, in particular to a plasticizer. Background technique [0002] Plasticizer (plasticizer) is a kind of polymer material additive, and it is also a phthalate (PAEsphthalates) in environmental estrogen. There are many kinds, the most common variety is DEHP (commercial name DOP), DEHP chemical name Bis(2-ethylhexyl)phthalate is a colorless, odorless liquid widely used in industry. Plasticizers, also known as plasticizers in general, are polymer material additives widely used in industry. Adding this kind of substance in plastic processing can make it more flexible, easy to process, and can be used legally Industrial applications. Plasticizers are bulk industrial products and are widely used in various fields of the national economy, including thousands of products such as plastics, rubber, adhesives, cellulose, resins, medical devices, and cables. However, most of the plasticizers currently used ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L15/02C08L1/28C08L91/06C08L63/00C08K13/02C08K5/12C08K3/04C08K3/36C08K3/34C08K5/00
CPCC08L27/06C08L2201/08C08L2205/035C08L15/02C08L1/286C08L91/06C08L63/00C08K13/02C08K5/12C08K3/04C08K3/36C08K3/346C08K5/0058
Inventor 贺海兰
Owner 佛山市高明区生产力促进中心
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com