High-wear-resistance modified-nano-molybdenum-disulfide-containing semisynthetic cutting fluid and preparation method thereof

A nano-molybdenum disulfide, high wear-resistant technology, used in lubricating compositions, petroleum industry and other directions, can solve the problems of anti-wear and stability to be improved, achieve good emulsification effect, improve stability, and good biodegradability Effect

Inactive Publication Date: 2017-05-31
ANHUI CHENGYOU AUTO PARTS MFG
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Shi Renzong prepared a water-based semi-synthetic cutting fluid using mineral oil and extreme pressure slip agent in "Research on the Preparation of Semi-Synthetic Cutting Fluid", but its anti-wear and stability still need to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0018] A highly wear-resistant semi-synthetic cutting fluid containing modified nano molybdenum disulfide is characterized in that it is made of the following raw materials in parts by weight:

[0019] Sulfur powder 8, organic alcohol amine 25, boric acid 10, oleic acid 7, sodium alginate 3, nanomolybdenum disulfide 4, sodium dodecylsulfonate 12, tungsten powder 3, palm oil 40, lauric acid 9, Span 80 3, Tween 80 3, paraffin base oil 10, dimethicone 2, distilled water 100.

[0020] The preparation method of a highly wear-resistant semi-synthetic cutting fluid containing modified nano-molybdenum disulfide is characterized in that it is made by the following steps:

[0021] a. Stir and heat 5-10 parts of organic alkanolamine in a water bath to 60-80°C, add boric acid, continue heating and stirring for 50-100 minutes, then add oleic acid, continue to react for 30-60 minutes, and obtain organic borate antirust after cooling extreme pressure additives;

[0022] b. Add sodium algin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
friction coefficientaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-wear-resistance modified-nano-molybdenum-disulfide-containing semisynthetic cutting fluid and a preparation method thereof. The invention is characterized in that the cutting fluid is prepared from the following raw materials in parts by weight: 3-8 parts of sulfur powder, 15-25 parts of organic hydramine, 5-10 parts of boric acid, 4-7 parts of oleic acid, 2-3 parts of sodium alginate, 2-4 parts of nano molybdenum disulfide, 5-12 parts of sodium dodecylsulfate, 2-3 parts of tungsten powder, 30-40 parts of palm oil, 5-9 parts of lauric acid, 2-3 parts of Span 80, 2-3 parts of Tween 80, 5-10 parts of paraffin base oil, 1-2 parts of polydimethylsiloxane and 50-100 parts of distilled water. The sodium alginate is utilized to disperse the nano molybdenum disulfide, so that the surface contains abundant functional groups; and the nano molybdenum disulfide has favorable compatibility after being added into the additives, thereby enhancing the wear resistance, extreme pressure performance and stability of the cutting fluid. The synthetic tungsten disulfide enables the lubricating oil to have higher wear resistance.

Description

technical field [0001] The invention relates to a semi-synthetic cutting fluid, in particular to a highly wear-resistant semi-synthetic cutting fluid containing modified nano molybdenum disulfide and a preparation method thereof. Background technique [0002] Semi-synthetic metal cutting fluid, also known as micro-emulsion metal cutting fluid, is diluted with water in a certain proportion, and the diameter of the emulsified particles is less than 1 μm. It is used in metal cutting and other processing industries. At the same time, it has good lubricity of emulsion and good synthetic fluid. It has excellent cleaning characteristics and suitable extreme pressure performance. It is a kind of cutting fluid with great development prospects; the main components of semi-synthetic metal cutting fluid are lubricating base oil (mineral oil), water, emulsifier, rust inhibitor, Extreme pressure anti-wear agent, defoamer, anti-mold and fungicide, etc. The content of emulsifier, mineral o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C10M173/00C10N40/22C10N30/06C10N30/12C10N30/16
CPCC10M173/00C10M2201/043C10M2201/05C10M2201/066C10M2201/087C10M2205/16C10M2207/126C10M2207/289C10M2207/40C10M2209/102C10M2209/12C10M2215/042C10M2219/044C10M2229/041C10N2030/06C10N2030/12C10N2030/16C10N2040/22C10N2010/02
Inventor 倪明光
Owner ANHUI CHENGYOU AUTO PARTS MFG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com