A kind of fan blade and preparation method thereof

A technology for fan blades and blade bodies, applied in the field of fan blades and their preparation, can solve the problems of high heating temperature, anti-erosion, poor corrosion effect, blade deformation, etc., so as to reduce erosion wear and avoid coating bonding strength. The effect of falling and small deformation

Active Publication Date: 2019-07-05
WUXI TURBINE BLADE
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to address the above problems, to provide a fan blade and its preparation method, to solve the problem of poor anti-erosion and corrosion effects of the existing fan blades, and to prepare the coated fan blades by manual flame spraying and melting. layer, the heating temperature is high, the surface oxidation is serious, and it is easy to cause serious deformation of the blade

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of fan blade and preparation method thereof
  • A kind of fan blade and preparation method thereof
  • A kind of fan blade and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0023] The technical solutions of the present invention will be further described below in conjunction with the accompanying drawings and through specific implementation methods. It should be understood that the embodiments described here are only used to explain the present invention, but not to limit the present invention.

[0024] Please refer to figure 1 and figure 2 As shown, in this embodiment, a fan blade includes a blade body, and a composite coating 1 is provided on the pressure surface and the suction surface of the air inlet side of the blade body, and the composite coating 1 located on the pressure surface of the blade body The length of the coating 1 is the same as the length of the pressure surface of the blade body, the width of the composite coating 1 located on the pressure surface of the blade body is 1 / 4 of the width of the pressure surface of the blade body, and the rest of the pressure surface of the blade body is provided with 0.15~ The WC-10Co-4Cr coa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a fan blade. The fan blade comprises a blade body. Composite coatings are arranged on a pressure surface and a force suction surface which are located on one side of the air inlet edge of the blade body. The width of the composite coating located on the pressure surface of the blade body is 1 / 5-1 / 3 of the width of pressure surface of the blade body, and the rest parts of pressure surface of the blade body are provided with a WC-10Co-4Cr coating. The width of the composite coating located on the force suction surface of the blade body is 1 / 5-1 / 3 of the width of force suction surface of the blade body, and the rest parts of force suction surface of the blade body are provided with a WC-10Co-4Cr coating. Each composite coating comprises a NiCrMoW coating and a WC-17Ni coating which are arranged from interior to exterior in sequence. The invention further discloses a preparation method of the fan blade. The preparation method comprises the following steps of a, fusion covering, b, sand blasting, c, spraying, and d, coating sealing. According to the blade prepared through the preparation method, the overall deformation of the blade is smaller than 0.5 mm and has good corrosion resistance and erosion-abrasion resistance, so that the service life is greatly prolonged.

Description

technical field [0001] The invention relates to the field of blades, in particular to a fan blade and a preparation method thereof. Background technique [0002] The fan is the main auxiliary machine of the boiler unit. The medium conveyed by the fan is flue gas, and the working temperature is usually in the range of 130-200°C. The harmful gas components in the flue gas mainly include sulfur dioxide, carbon monoxide, hydrocarbons, and nitrogen dioxide; among them, the corrosive medium includes SO2 and trace amounts of SO3 and NOx, and contains high-hardness dust particles such as SiO2, Al2O3, and Fe2O3; traditional The blades are only sprayed with a layer of nickel-based alloy powder near the air intake edge and then sprayed with WC-Ni wear-resistant coating. The coating has poor anti-erosion and corrosion effects. The above-mentioned corrosive medium and high-hardness dust particles will corrode the fan blades. And strong erosion and wear. After the blades are worn, the ef...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23C24/10C23C4/06C23C4/129C23C4/134C23C28/02
CPCC23C4/06C23C24/106C23C28/021C23C28/027
Inventor 张铁磊崔慧然崔启政
Owner WUXI TURBINE BLADE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com