A kind of titanium plating treatment method on the surface of aluminum alloy

A technology of aluminum alloy surface and treatment method, which is applied in the field of aluminum surface treatment, can solve the problems of high melting point, difficulty in forming high-quality titanium film, high temperature, etc., and achieve the effects of enhanced performance, good electroplating effect, and guaranteed activity

Active Publication Date: 2018-06-26
QIYANG HONGTAI ALUMINUM IND
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the methods of titanium plating mainly include vacuum titanium plating film and chemical titanium plating film. Vacuum titanium plating film requires higher temperature and is suitable for materials with higher melting point; titanium film

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of titanium plating treatment method on the surface of aluminum alloy
  • A kind of titanium plating treatment method on the surface of aluminum alloy

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0051] Below in conjunction with embodiment, the present invention will be further described. The following description is by way of example, but the protection scope of the present invention should not be limited thereto.

[0052] The titanium plating treatment method on the aluminum alloy surface of the present embodiment, its treatment process is as follows:

[0053] (1) Preparation of each liquid:

[0054] (1) Preparation of alkaline mixed aqueous solution:

[0055] Potassium hydroxide, sodium silicate, dodecylphenol vinyl ether and sodium pyrophosphate were respectively taken, according to potassium hydroxide 45g / L, sodium silicate 7g / L, dodecylphenol vinyl ether 12g / L, pyrophosphoric acid The concentration ratio of sodium is 7g / L, and it is evenly mixed with clean water to form an alkaline mixed aqueous solution.

[0056] (2) Preparation of acidic mixed aqueous solution:

[0057] Take hydrochloric acid, oxalic acid, and myristyl phenol vinyl ether respectively, and m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses an aluminum alloy surface titanium plating treatment method, and relates to the technical field of aluminum alloy material surface treatment. The treatment process comprises: (a) deoiling; (b) dewaxing; (c) anodic oxidation; (d) acid etching; and (e) titanium plating; and titanium plating treatment liquid is prepared by the following raw materials in parts by weight: 20-35 of potassium chloride, 10-20 of titanium potassium oxalate, 2.5-5.5 of dimethyl carbonate, 5-10 of titanium sulfate, 1-3 of potassium carbonate, 3-7 of methyl butynol, 1-3 of nickel sulfate, 2-5 of butynediol, 1-2.5 of adenine corrosion inhibitor, 0.25-1 of neodymium chloride, and 2-8 of hydroxyethyl acrylate. The method capable of forming a layer of titanium film with high hardness and corrosion resistance on the surface of an aluminum alloy has such characteristics as high efficiency, simple operation and capability of improving the quality of aluminum alloy products, can be used for treating aluminum alloy profiles, also can be used for treating aluminum alloy parts, and in particular, is suitable for treating aluminum alloy shell parts and aluminum alloy panels.

Description

technical field [0001] The invention relates to the technical field of aluminum surface treatment, in particular to a method for treating the surface of an aluminum alloy with titanium plating. Background technique [0002] Because aluminum alloy is light in weight, low in cost, easy to process and shape, and easy to color and dye, it has been widely used. However, restricted by the physical and chemical properties of metal aluminum itself, its surface hardness is low, and it is prone to scratches or scratches. Although in recent years, some imitation titanium aluminum alloy profiles have appeared on the market, the surface is golden yellow, and the hardness is slightly higher than that of conventional aluminum alloy profiles, but compared with stainless steel or titanium materials, its hardness and corrosion resistance Sex etc. are still far apart. For this reason, some titanium-plated materials have appeared on the market, that is, a layer of titanium film with high hard...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C25D5/44C25D3/54C23G1/22C23G1/12C25D11/08C23F1/20
CPCC23F1/20C23G1/125C23G1/22C25D3/54C25D5/44C25D11/08
Inventor 刘健曾飞蒋国富蒋有名黄建国谭永宏欧光川
Owner QIYANG HONGTAI ALUMINUM IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com