Sewage treatment composite gel material for microbe embedding, and preparation method thereof

A composite gel and sewage treatment technology, applied in biological water/sewage treatment, adsorption water/sewage treatment, water/sludge/sewage treatment, etc., can solve the problem that magnetic multi-walled carbon nanotubes are not cost-effective and cannot be effectively adsorbed Remove heavy metal ions, can not effectively degrade organic matter and other problems, to achieve the effect of improving mechanical strength, improving water-soluble swelling, and low cost

Active Publication Date: 2016-04-27
河南格恩阳光环境科技有限公司
View PDF6 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The invention uses microorganisms to treat sewage, and in addition, microorganisms are easily inactivated and lost without external protection, and the effect on sewage treatment is not good, and organic matter cannot be effectively degraded
Patent Publication No. 102060371A discloses a composite material for sewage treatment, which consists of 28-48% magnetic multi-walled carbon nanotubes, 12-26% bromelain and 28-50% The additives are prepared, and the magnetic multi-walled carbon nanotubes used in this invention are not cost-effective, high in cost, and cannot effectively absorb and remove heavy metal ions

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] (1) Add 46 parts by weight of carrageenan and 84 parts by weight of water into the reactor, control the temperature at 86°C, stir continuously until dissolved, cool to 44°C, add 17 parts by weight of polyacrylamide to stir and dissolve, ultrasonically disperse, and finally get mixture;

[0033] (2) 7 parts by weight of activated sludge, 12 parts by weight of porous starch, 0.14 parts by weight of KH 2 PO 4 , 7 parts by weight of water are added in the mixer, under the stirring condition of 130r / min, react for 7 minutes to obtain the porous starch mixture;

[0034] (3) Mix the mixed solution obtained in step (1) with the porous starch mixed solution obtained in step (2) and 3 parts by weight of sepiolite, 2 parts by weight of N,N,-methylene acrylamide, 0.7 parts by weight Potassium carbonate and 0.24 parts by weight of calcium chloride were added to the reactor, stirred and reacted for 2.2 hours, the temperature was controlled at 44° C., and the pH value was controlled...

Embodiment 2

[0036] (1) Add 44 parts by weight of carrageenan and 82 parts by weight of water into the reactor, control the temperature at 84°C, stir continuously until dissolved, cool to 42°C, add 16 parts by weight of polyacrylamide to stir and dissolve, ultrasonically disperse, and finally get mixture;

[0037](2) 6 parts by weight of yeast, 11 parts by weight of porous starch, 0.12 parts by weight of K 2 HPO 4 , 6 parts by weight of water are added in the mixer, under the stirring condition of 110r / min, react for 6 minutes to obtain the porous starch mixture;

[0038] (3) Mix the mixed solution obtained in step (1) with the porous starch mixed solution obtained in step (2) and 2 parts by weight of bentonite, 1.2 parts by weight of N,N,-methylenebisacrylamide, 0.6 parts by weight of potassium sulfate , 0.22 parts by weight of calcium chloride was added to the reactor and stirred for 2.1 hours. The temperature was controlled at 42° C., and the pH value was controlled at 6.9. Finally, i...

Embodiment 3

[0040] (1) Add 40 parts by weight of carrageenan and 80 parts by weight of water into the reactor, control the temperature at 80°C, stir continuously until dissolved, cool to 40°C, add 15 parts by weight of polyacrylamide to stir and dissolve, ultrasonically disperse, and finally get mixture;

[0041] (2) 4 parts by weight of Pseudomonas, 10 parts by weight of porous starch, 0.1 part by weight of NH 4 NO 3 , 5 parts by weight of water are added in the mixer, under 100r / min stirring condition, react 5 minutes, obtain porous starch mixed solution; (3) the mixed solution that step (1) obtains and step (2) obtain The porous starch mixture, 1 weight part of heavy calcium carbonate, 1 weight part of epichlorohydrin, 0.5 weight part of potassium chloride, and 0.2 weight part of calcium chloride were added to the reactor and stirred for 2 hours. The temperature was controlled at 40°C, and the pH The value is controlled at 6.8, and finally washed with physiological saline to obtain a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to a sewage treatment composite gel material for microbe embedding, and a preparation method thereof. The sewage treatment composite gel material for microbe embedding comprises, by weight, 60-80 parts of carrageenan, 5-15 parts of polyacrylamide, 5-8 parts of porous starch, 4-8 parts of microbes, 0.1-0.3 parts of a growth factor, 1-4 parts of inorganic powder, 1-3 parts of a cross-linking agent and 0.5-0.8 parts of a potassium salt. The composite gel material is prepared by adopting carrageenan and the polyacrylamide composite gel as an embedding agent, the porous starch as an adsorbent and a carrier and the inorganic powder as an additive, is used for embedding microbes, is applied to sewage treatment, can effectively adsorb and remove heavy metal ions and degrade organic matters, and has the advantages of simple preparation process, low cost and market application prospect.

Description

technical field [0001] The invention belongs to the field of sewage treatment, and in particular relates to a sewage treatment composite gel material embedding microorganisms and a preparation method thereof. Background technique [0002] Water accounts for 70% of the earth's area, of which seawater accounts for 97.3%, and available fresh water accounts for only 2.7%. 77.2% of fresh water exists in snow-capped mountains and glaciers, 22.4% exists in soil and groundwater (precipitation and surface water infiltration), only 0.4% Surface water is rivers, lakes, glaciers and other water bodies. Overview of my country's water resources: The total length of rivers and rivers in my country is 420,000 kilometers, and the lakes are 75,600 square kilometers, accounting for 0.8% of the total land area. The total water resources are 2.8 trillion m 3 , 2,300 cubic meters per capita, accounting for only 1 / 4 of the world's per capita possession, ranking 121, and one of the 13 water-poor c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C02F3/34C02F101/20
CPCC02F1/28C02F3/34C02F2101/20
Inventor 陈庆廖大应
Owner 河南格恩阳光环境科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap