High-temperature-resistant nylon wire and preparation method thereof

A high temperature resistant, nylon thread technology, applied in the field of nylon thread, can solve the problem of not being able to achieve high temperature resistance, and achieve the effects of improving construction performance, reducing film forming temperature, and simple steps

Inactive Publication Date: 2017-05-31
SUZHOU CHENHENG WEAVING
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Nylon thread is an extremely important part in the weaving industry. With the continuous development of the economy, people have higher and higher requirements for nylon thread. The nylon thread in the prior art still has many shortcomings, and it cannot achieve high temperature resistance and corrosion resistance. Function, in order to improve work efficiency and reduce scrap rate, the present invention proposes a high temperature resistant nylon thread and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] This embodiment provides a high temperature resistant nylon thread, the surface of the nylon thread is coated with a layer of high temperature resistant coating, and the high temperature resistant coating is composed of two components A: B = 2:1. The count contains the following components:

[0024] Component A includes the following components in parts by mass: refractory material: 12 parts, carrier: 9 parts, alkali-free glass fiber: 8 parts, nylon: 17 parts, color masterbatch: 9 parts, 3-butanediol : 3 parts, diethylene glycol: 2 parts, flame retardant: 11 parts, film-forming aid: 11 parts, defoamer: 4 parts;

[0025] Component B includes the following components in parts by mass: binder: 11 parts, suspending agent: 9 parts, heat stabilizer: 14 parts, glass fiber treatment agent: 8 parts, activated carbon: 8 parts, polyphenylene ether Resin powder: 18 parts, styrene-butadiene rubber: 11 parts, toluene: 5 parts, plasticizer: 4 parts, coupling agent: 5 parts, flame ret...

Embodiment 2

[0033] This embodiment provides a high temperature resistant nylon thread, the surface of the nylon thread is coated with a layer of high temperature resistant coating, and the high temperature resistant coating is composed of two components A: B = 2:1. The count contains the following components:

[0034] Component A includes the following components in parts by mass: refractory material: 18 parts, carrier: 12 parts, alkali-free glass fiber: 11 parts, nylon: 21 parts, color masterbatch: 11 parts, 3-butanediol : 7 parts, diethylene glycol: 6 parts, flame retardant: 14 parts, film-forming aid: 15 parts, defoamer: 9 parts;

[0035] Component B includes the following components in parts by mass: binder: 16 parts, suspending agent: 12 parts, heat stabilizer: 18 parts, glass fiber treatment agent: 13 parts, activated carbon: 12 parts, polyphenylene ether Resin powder: 20 parts, styrene-butadiene rubber: 16 parts, toluene: 8 parts, plasticizer: 7 parts, coupling agent: 8 parts, fla...

Embodiment 3

[0043] This embodiment provides a high temperature resistant nylon thread, the surface of the nylon thread is coated with a layer of high temperature resistant coating, and the high temperature resistant coating is composed of two components A: B = 2:1. The count contains the following components:

[0044] Component A includes the following components in parts by mass: refractory material: 15 parts, carrier: 10 parts, alkali-free glass fiber: 9 parts, nylon: 19 parts, color masterbatch: 10 parts, 3-butanediol : 5 parts, diethylene glycol: 4 parts, flame retardant: 12 parts, film-forming aid: 13 parts, defoamer: 5 parts;

[0045] Component B includes the following components in parts by mass: binder: 15 parts, suspending agent: 10 parts, heat stabilizer: 15 parts, glass fiber treatment agent: 10 parts, activated carbon: 10 parts, polyphenylene ether Resin powder: 19 parts, styrene-butadiene rubber: 14 parts, toluene: 6 parts, plasticizer: 5 parts, coupling agent: 7 parts, flam...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-temperature-resistant nylon wire. The component A comprises the following ingredients in parts by mass: 12-18 parts of refractory material, 9-12 parts of carrier, 8-11 parts of alkali-free glass fiber, 17-21 parts of nylon, 9-11 parts of color master batch, 3-7 parts of 3-butanediol, 2-6 parts of diethylene glycol, 11-14 parts of flame retardant, 11-15 parts of film forming aid and 4-9 parts of defoaming agent. The component B comprises the following ingredients in parts by mass: 11-16 parts of adhesive, 9-12 parts of suspending agent, 14-18 parts of heat stabilizer, 8-13 parts of glass fiber treating agent, 8-12 parts of activated carbon, 18-20 parts of polyphenylene oxide resin powder, 11-16 parts of styrene-butadiene rubber, 5-8 parts of methylbenzene, 4-7 parts of plasticizer, 5-8 parts of coupling agent and 4-6 parts of flame retardant. The method enhances the work efficiency, lowers the production cost and simplifies the production steps.

Description

technical field [0001] The invention relates to the technical field of nylon threads, in particular to a high-temperature-resistant nylon thread and a preparation method thereof. Background technique [0002] Nylon thread is an extremely important part in the weaving industry. With the continuous development of the economy, people have higher and higher requirements for nylon thread. The nylon thread in the prior art still has many shortcomings, and it cannot achieve high temperature resistance and corrosion resistance. Function, in order to improve work efficiency and reduce scrap rate, the invention proposes a high temperature resistant nylon thread and its preparation method. Contents of the invention [0003] The technical problem to be solved by the present invention is to propose a high-temperature-resistant nylon thread in view of the above shortcomings of the prior art. =2:1 ratio is compounded, and A and B comprise the following components in parts by mass: [0...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/59D06M15/53D06M15/693D06M11/79D06M11/46D06M13/148D06M13/165D06M13/292D06M13/50D06M13/402D06M13/224D06M101/34
CPCD06M15/59D06M11/46D06M11/79D06M13/148D06M13/165D06M13/224D06M13/292D06M13/402D06M13/50D06M15/53D06M15/693D06M2101/34
Inventor 叶冬明
Owner SUZHOU CHENHENG WEAVING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com