ABS material with high heat resistance and flame retardance

An ABS material and high heat-resistant technology, applied in the field of ABS materials, can solve the problems of heat distortion temperature and impact strength reduction, and achieve the effects of inhibiting decomposition, reducing costs, and reducing pollution

Inactive Publication Date: 2017-06-13
NINGBO KADEER ELECTRICAL APPLIANCES
View PDF0 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the heat distortion temperature and impact strength of general ABS materials will be significantly reduced due to the addition of flame retardants.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0020] The invention provides a high heat-resistant and flame-retardant ABS material, which is composed of the following components in mass percentage: 60%-80% of ABS resin; 10%-20% of brominated flame retardant; 3%-10% of antimony flame retardant; Composite smoke suppressant 1-2%; inorganic flame retardant synergist 1%-5%; anti-dripping agent 0.1-1.0%; other processing aids 1%-5%; The melt index is 10g / 10min-30g / 10min.

[0021] Brominated flame retardants are any one or a combination of two or more of decabromodiphenylethane, brominated epoxy, brominated triazine, tetrabromobisphenol A, and brominated polystyrene; The agent is any one of antimony trioxide, antimony pentoxide, antimony trisulfide, or a combination of two or more; the composite smoke suppressant is a compound of molybdenum compound and nano-metal oxide, and the nano-metal oxide The compound is any one of magnesium oxide, copper oxide, zinc oxide, and ferric oxide; the inorganic flame retardant synergist is any...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
Login to view more

Abstract

The invention provides a high heat-resistant and flame-retardant ABS material, which consists of 60%-80% by mass percentage of ABS resin, 8%-20% of brominated flame retardant, and 3%-10% of antimony Flame retardant, 1%-2% compound smoke suppressant, 1%-5% inorganic flame retardant synergist, 0.1-1.0% anti-dripping agent and 1%-5% other processing aids; The invention also provides a method for preparing the above-mentioned high heat-resistant and flame-retardant ABS material; the invention uses ABS resin as a matrix, and combines flame retardants, smoke suppressants and special processing aids to prepare a material with high heat resistance. Burning ABS material; it can be used to make heater plastic shells and other electrical industries, and can also be widely used in communication industry, automobile industry, building materials, decorative materials, cables.

Description

technical field [0001] The invention relates to an ABS material, in particular to a high heat-resistant and flame-retardant ABS material. Background technique [0002] In recent years, the state has put forward strict fire and flame retardant requirements for plastic materials used in household appliances, office supplies, auto parts, etc., and formulated corresponding technical standards and specifications. Therefore, the flame retardant problem of ABS has been paid more and more attention by countries all over the world. [0003] ABS material is a thermoplastic polymer material structure with high strength, good toughness and easy processing. In ABS resin, the synergistic properties between the three components can be exhibited: the properties of acrylonitrile component in ABS are heat resistance, chemical resistance, rigidity, and tensile strength; the properties of butadiene are impact resistance Strength; the characteristics of styrene are processing fluidity and glos...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L55/02C08L25/06C08L25/12C08L27/18C08K13/02C08K5/03C08K5/3492C08K5/136C08K3/22C08K3/30C08K3/34C08K3/38
Inventor 张善琴
Owner NINGBO KADEER ELECTRICAL APPLIANCES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products