Multilobal hollow polyester fiber FDY (fully drawn yarn) and preparation method thereof

A polyester fiber, hollow shape technology, applied in the field of polyester spinning, can solve the problems of weakening extrusion swelling effect, reducing surface tension, poor shape retention effect of special-shaped fibers, etc.

Active Publication Date: 2017-06-13
JIANGSU HENGKE ADVANCED MATERIALS CO LTD
View PDF3 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The purpose of the present invention is to overcome the poor shape retention effect of the prior art for preparing special-shaped fibers, to provide a multi-lobed hollow polyester fiber FDY filament and its preparation method. The present invention introduces a small amount of rigid structure into the polyester molecule The chain segment increases the rigidity of the polyester molecular chain. On the one hand, due to the small content of the rigid structural segment, it can maintain the excellent characteristics of the polyester body; Small surface tension, and then prepare shaped fibers with better shape retention

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Multilobal hollow polyester fiber FDY (fully drawn yarn) and preparation method thereof
  • Multilobal hollow polyester fiber FDY (fully drawn yarn) and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] A kind of preparation method of trilobal hollow polyester fiber FDY silk, at first prepare spinning melt, the steps are as follows:

[0052] (1) esterification makes dibasic acid glycol ester;

[0053] Prepare terephthalic acid, ethylene glycol and 2,6-naphthalene dicarboxylic acid into a slurry, the molar ratio of terephthalic acid, ethylene glycol and 2,6-naphthalene dicarboxylic acid is 1:1.2:0.02, add di After antimony, triphenyl phosphate and aluminum stearate are mixed evenly, carry out esterification reaction, the addition amount of antimony trioxide is 0.01% of the weight of terephthalic acid, and the addition amount of triphenyl phosphate is 0.01% of the weight of terephthalic acid. %, the esterification reaction is a pressurized reaction in a nitrogen atmosphere, the pressurized pressure is 0.1MPa, the temperature of the esterification reaction is 250 ° C, when the amount of water distilled in the esterification reaction reaches 90% of the theoretical value, i...

Embodiment 2

[0069]A kind of preparation method of trilobal hollow polyester fiber FDY silk, at first prepare spinning melt, the steps are as follows:

[0070] (1) esterification makes dibasic acid glycol ester;

[0071] Make a slurry of terephthalic acid, ethylene glycol and 4,4-biphenyl dicarboxylic acid, the molar ratio of terephthalic acid, ethylene glycol and 4,4-biphenyl dicarboxylic acid is 1:1.8:0.046, add acetic acid After antimony, trimethyl phosphite and zinc stearate are mixed evenly, carry out esterification reaction, the addition of antimony acetate is 0.045% of the weight of terephthalic acid, the addition of trimethyl phosphite is 0.045% of the weight of terephthalic acid %, the esterification reaction is a pressurized reaction in a nitrogen atmosphere, the pressurized pressure is 0.24MPa, the temperature of the esterification reaction is 258 ° C, when the amount of water distilled in the esterification reaction reaches 93% of the theoretical value, it is an esterification ...

Embodiment 3

[0091] A kind of preparation method of trilobal hollow polyester fiber FDY silk, at first prepare spinning melt, the steps are as follows:

[0092] (1) esterification makes dibasic acid glycol ester;

[0093] The diterephthalate of terephthalic acid, ethylene glycol and bisphenol A is made into slurry, and the mol ratio of the diterephthalate of terephthalic acid, ethylene glycol and bisphenol A is 1: 1.3:0.025, add antimony trioxide, triphenyl phosphate and aluminum stearate and mix evenly, then carry out esterification reaction, the amount of antimony trioxide added is 0.015% of the weight of terephthalic acid, the amount of triphenyl phosphate added It is 0.015% of the weight of terephthalic acid. The esterification reaction is pressurized in a nitrogen atmosphere. The pressurized pressure is 0.12 MPa, and the temperature of the esterification reaction is 251 ° C. When the amount of water distilled in the esterification reaction reaches the theoretical value 90% of the tim...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Melting pointaaaaaaaaaa
Dynamic viscosityaaaaaaaaaa
Monofilament denieraaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of polyester spinning, and relates to a multilobal hollow polyester fiber FDY (fully drawn yarn) and a preparation method thereof. A spinning melt comprises a saturated fatty acid metal salt and modified polyester according to a mass ratio of (0.0005 to 0.002) to 1; the saturated fatty acid metal salt is a fatty acid metal salt with carbon atom number of 12 to 22, melting point of 100 to 180 DEG C, and dynamic viscosity less than or equal to 1Pa.s; a molecular chain of the modified polyester comprises a terephthalic acid chain segment, an ethylene glycol chain segment and a rigid structure chain segment, the molar ratio of the rigid structure chain segment to the terephthalic acid chain segment is (0.02 to 0.05) to 1, the extrusion swelling ratio of the spinning melt is 1.20 to 1.31, and the post-filtering pressure is 80 to 120kg / cm<2> during spinning. The prepared multilobal hollow polyester fiber FDY has higher hollow degree and a better shape preserving effect.

Description

technical field [0001] The invention belongs to the field of polyester spinning, and relates to a multi-leaf hollow polyester fiber FDY filament and a preparation method thereof. Background technique [0002] Since its inception, polyethylene terephthalate (PET fiber or polyester fiber) fiber has high breaking strength and elastic modulus, moderate resilience, excellent heat setting, good heat resistance and light resistance, acid resistance, alkali resistance and corrosion resistance. It has a series of excellent performances, such as anti-wrinkle and non-ironing, and good crispness. It is widely used in clothing, home textiles and other fields. [0003] Home textiles are one of the three final product areas of the textile industry. With the improvement of people's quality of life, comfort, functionality, and environmental protection have increasingly become consumers' new requirements for home textiles. The polyester filament products used in home textile production in th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D01F6/92D01F1/10D01D5/24
Inventor 柳敦雷林枢珑于涛王峰
Owner JIANGSU HENGKE ADVANCED MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com