Preparation and use method of waterproof coating agent of outdoor exercise rope

A waterproof coating and rope technology, which is applied in the field of rope nets, can solve the problems of nylon fibers such as easy moisture absorption, reduced strength, and reduced wear resistance, and achieves simple production processes and usage methods, good water repellency, and low surface area. The effect of the tension value

Inactive Publication Date: 2017-07-18
SHANDONG ROPE TECH CO LTD
View PDF8 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Nylon fiber is easy to absorb moisture. After absorbing moisture, the weight of the rope will increase, and the strength will decrease accordingly, and the wear resistance will decrease. After the rope absorbs moisture and freezes, it loses its original softness and is difficult to operate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0025] A preparation method of an outdoor sports rope waterproof coating agent is realized through the following steps:

[0026] 1) Weigh the reactants in the components according to the volume content, add 1 / 2 emulsifier and 1 / 2 initiator into 1 / 2 ion water, and form emulsified aqueous solution system A in the colloid mill;

[0027] 2) Mix acrylate and acrylic acid monomers according to the volume ratio, slowly add to the above emulsifier system A in the colloid mill, and emulsify for 40 minutes to form prepolymer emulsion B;

[0028] 3) Put the remaining emulsifier, initiator, ionized water and 1 / 4 of the prepolymer emulsion B into a three-necked flask with a stirrer and a condenser, and heat it to 80-85°C in a water bath;

[0029] 4) Drop the remaining prepolymer emulsion B into the flask within 2-3 hours, continue to react for 2-3 hours after the dropwise addition, cool down and discharge to obtain a homogeneous emulsified dispersion, which is the waterproof coating agent....

Embodiment 1

[0034] To prepare a waterproof outdoor rescue rope with a diameter of 9.5 mm, the water absorption rate after finishing is required to be within 5%.

[0035] step 1:

[0036] 1) Weigh 10 parts of acrylate by volume as a mixture of ethyl methacrylate and butyl acrylate, 10 parts of fluorine-containing acrylic acid monomer as dodecafluoroheptyl acrylate, 0.3 parts of ammonium persulfate as the initiator, and 0.3 parts of ammonium persulfate as the emulsifier Add 8 parts of O-15 and ethylene glycol butyl ether mixture, and 57 parts of deionized water;

[0037] 2) Add 1 / 2 emulsifier and 1 / 2 initiator to 1 / 2 ionized water to form emulsified aqueous solution system A in the colloid mill;

[0038] 3) Mix ethyl methacrylate, butyl acrylate mixture and dodecafluoroheptyl acrylate in proportion, slowly add to the above emulsifier system A in the colloid mill, and emulsify for 40 minutes to form prepolymer emulsion B;

[0039] 4) Put the remaining emulsifier, initiator, deionized water...

Embodiment 2

[0044] To prepare a mountaineering rope with a diameter of 10.5mm, the water absorption performance after finishing is required to be within 3%.

[0045] step 1:

[0046] 1) Weigh 20 parts of acrylate by volume as lauryl acrylate, 30 parts of fluorine-containing acrylic acid monomer as perfluoroalkylsulfonamidoethyl acrylate, 0.1 part of sodium persulfate as initiator, and perfluoroalkyl as emulsifier 10 parts of ethoxy ether alcohol, 30 parts of deionized water;

[0047] 2) Add 1 / 2 emulsifier and 1 / 2 initiator to 1 / 2 ionized water to form emulsified aqueous solution system A in the colloid mill;

[0048] 3) Mix lauryl acrylate and perfluoroalkylsulfonamidoethyl acrylate in proportion, slowly add to the above emulsifier system A in the colloid mill, and emulsify for 40 minutes to form prepolymer emulsion B;

[0049] 4) Put the remaining emulsifier, initiator, deionized water and 1 / 4 of the prepolymer emulsion B into a three-necked flask with a stirrer and a condenser, and he...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation and use method of a waterproof coating agent of an outdoor exercise rope and relates to the field of a rope net. The waterproof coating agent is formed by pre-polymerizing and polymerizing acrylate and fluorine-containing acrylic monomer in an initiator and emulsifier aqueous solution system. The preparation technology and the use method are relatively simple; the cost of the raw materials is low; the raw materials are simple and are easily acquired; the water absorption not more than 5% is required on the basis of the requirement for waterproof property according to a performance index of the outdoor exercise rope; after the invention is applied, the test is performed according to a waterproof test method for Power Rope on the basis of international mountain climbing union standard UIAA101; the water absorption of the rope after being settled is 0-4%, meets the standard requirement and meets the requirement for the waterproof property of the rope in outdoor exercise.

Description

technical field [0001] The invention relates to the field of rope nets, in particular to a method for preparing and using a waterproof coating agent for outdoor sports ropes. Background technique [0002] The safety ropes used in outdoor sports such as high-altitude hiking, iceberg travel, and steep wall trekking are mostly made of nylon fibers. Nylon fiber is easy to absorb moisture. After absorbing moisture, the weight of the rope will increase, and the strength will decrease accordingly, and the wear resistance will decrease. Therefore, it is necessary to carry out waterproof finishing to this type of outdoor sports rope, so as to improve the safety and protection performance of the rope to outdoor sports personnel. Contents of the invention [0003] In order to solve the above-mentioned technical problems, the present invention provides a method for preparing and using a waterproof coating agent for outdoor sports ropes. The waterproof performance of the outdoor rope...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08F220/22C08F220/18C08F220/38C08F220/36C08F2/30C08F2/26D06M15/277D07B7/14
CPCD06M15/277D07B7/14C08F2/26C08F2/30C08F220/18C08F220/22C08F220/36C08F220/38D07B2501/2069C08F220/387C08F220/1818C08F220/1804C08F220/1802
Inventor 沈明陈岩刘瑞强尹延征刘俊谦刘鹏
Owner SHANDONG ROPE TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com