Water-based velvet effect auxiliary agent applicable to synthetic leather

A synthetic leather and water-based technology, applied in the direction of textiles and papermaking, can solve the problems of affecting the processing environment, increasing the cost of wastewater treatment, and the difficulty of wastewater treatment, etc., and achieves a long-lasting velvet feel, strong environmental protection in processing, and soft hand feeling. Effect

Inactive Publication Date: 2017-07-25
江西展邦科技有限公司
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, a large amount of organic solvents are used in the raw materials, including dimethylformamide, ethyl ester, and toluene. The extensive use of organic solvents seriously affects the processing environment, and the wastewater treatment is difficult, which increases the cost of wastewater treatment.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-based velvet effect auxiliary agent applicable to synthetic leather
  • Water-based velvet effect auxiliary agent applicable to synthetic leather
  • Water-based velvet effect auxiliary agent applicable to synthetic leather

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] (1) Add 15g of down fiber / polyvinylpyrrolidone and 0.5g of polyethylene oxide to 100g of water, and heat up to reflux state and mix for 15 minutes, then add 2g of polyvinyl alcohol modified activated clay and 0.15g of nano-titanium dioxide, and continue to reflux for heat preservation Mixed for 15min, then naturally cooled to room temperature to obtain material I;

[0029] (2) Add 5g soybean protein fiber / poloxamer and 0.5g polyethylene glycol 4000 to 50g water, and heat up to reflux state and mix for 15min, then add 0.3g polyaluminum sulfate ferric chloride and 0.05g pyrophosphorous acid tin, continue to reflux insulation and mix for 5min, then naturally cool to room temperature to obtain material II;

[0030] (3) Add material II, 3g of microcrystalline cellulose / chitosan, 2g of cationic polyacrylamide and 1g of sodium carboxymethylcellulose to material I, mix well and send it into a ball mill, pass through a 300-mesh sieve after ball milling for 8 hours , the resulti...

Embodiment 2

[0035] (1) Add 20g of down fiber / polyvinylpyrrolidone and 0.5g of polyethylene oxide to 100g of water, and heat up to reflux state and mix for 15 minutes, then add 3g of polyvinyl alcohol modified activated clay and 0.3g of nano-titanium dioxide, and continue to reflux for heat preservation Mixed for 15min, then naturally cooled to room temperature to obtain material I;

[0036] (2) Add 10 g of soybean protein fiber / poloxamer and 0.5 g of polyethylene glycol 4000 to 50 g of water, heat up to reflux and mix for 15 minutes, then add 0.5 g of polyaluminum sulfate ferric chloride and 0.05 g of pyrophosphorous acid tin, continue to reflux insulation and mix for 5min, then naturally cool to room temperature to obtain material II;

[0037](3) Add material II, 5g microcrystalline cellulose / chitosan, 2g cationic polyacrylamide and 2g sodium carboxymethyl cellulose to material I, mix well and send it into a ball mill, pass through a 300-mesh sieve after ball milling for 8 hours , the r...

Embodiment 3

[0057] Add the cashmere feeling auxiliary agent of equivalent embodiment 1, embodiment 2, comparative example 1, comparative example 2 and comparative example 3 respectively in the water-based polyurethane slurry (concrete raw material ratio is as shown in table 1, wherein cashmere feeling auxiliary agent Adding agent is 1.5wt%, in terms of solid content), and through the same processing technology, synthetic leather is made, and the cashmere-related properties of the synthetic leather are tested, and the test results are shown in Table 2.

[0058] Table 1 Synthetic leather preparation slurry ratio table

[0059]

[0060]

[0061] The synthetic leather performance test result of table 2

[0062]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a water-based velvet effect auxiliary agent applicable to synthetic leather, and relates to the technical field of synthetic leather functional auxiliary agents. The water-based velvet effect auxiliary agent applicable to the synthetic leather is prepared from the following raw materials in parts by weight: 15 to 20 parts of down fiber / polyvinylpyrrolidone, 5 to 10 parts of soybean protein fiber / poloxamer, 3 to 5 parts of microcrystalline cellulose / chitosan, 2 to 3 parts of cationic polyacrylamide, 2 to 3 parts of polyvinyl alcohol modified active argil, 1 to 2 parts of sodium carboxymethylcellulose, 0.5 to 1 part of polyethylene glycol 4000, 0.5 to 1 part of polyoxyethylene, 0.3 to 0.5 part of polyaluminium ferric sulfate chloride, 0.1 to 0.3 part of nanometer titanium dioxide powder, 0.05 to 0.1 part of stannous pyrophosphate and 100 to 150 part of water. The prepared water-based velvet effect auxiliary agent is added into waterborne polyurethane slurry and can be well blended and compatible with film forming raw materials, so that the processed and made synthetic leather has the characteristics of soft hand feeling, smooth velvet surface and uniform velvet hair; the hand feeling is similar to that of real leather; the use quality of a manufactured synthetic leather product is improved.

Description

[0001] Technical field: [0002] The invention relates to the technical field of functional auxiliary agents for synthetic leather, in particular to a water-based suede auxiliary agent suitable for synthetic leather. [0003] Background technique: [0004] Synthetic leather is made of impregnated non-woven fabric as a mesh layer and a microporous polyurethane layer as a grain layer. Its front and back are very similar to leather, and has a certain degree of air permeability, which is closer to natural leather than ordinary artificial leather. It is widely used in making shoes, boots, bags and ball games. [0005] During the processing of synthetic leather, functional additives need to be added to enhance the feel, appearance quality and use quality of synthetic leather products. The cashmere additive is a special functional additive for synthetic leather, and its purpose is to give the synthetic leather a delicate cashmere feel and make it have a touch close to genuine leather...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L89/00C08L39/06C08L71/02C08L1/04C08L5/08C08L33/26C08L1/28C08K13/06C08K9/04C08K3/30C08K3/22C08L75/04D06N3/00D06N3/14
CPCC08L89/00C08K2201/011C08L75/04C08L2205/02C08L2205/025C08L2205/035C08L2205/16D06N3/0061D06N3/0063D06N3/142D06N2211/28C08L39/06C08L71/02C08L1/04C08L5/08C08L33/26C08L1/286C08K13/06C08K9/08C08K9/04C08K2003/3045C08K2003/2241
Inventor 曾丽建郑建荣张维贤李海
Owner 江西展邦科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com