Polyester composition and preparation method thereof

A composition and polyester technology, applied in the field of materials, can solve the problems of unsatisfactory crystalline properties, influence on tensile strength, rigid thermal deformation temperature, impact resistance and creep resistance, crystallization rate influence, etc., and achieve short molding time. , The effect of improving the crystallization rate and excellent mechanical properties

Active Publication Date: 2017-07-28
SINOPLAST NEW MATERIAL
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the crystallization performance of poly-1,4-cyclohexanedimethyl terephthalate (PCT) is still unsatisfactory, and its crystallization rate not only affects its molding processing cycle, but also directly affects its tensile strength, rigidity, thermal deformation Temperature, impact resistance, creep resistance and other physical and mechanical properties

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyester composition and preparation method thereof
  • Polyester composition and preparation method thereof
  • Polyester composition and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0053] A polyester composition of the present embodiment is prepared from the following raw materials:

[0054]

[0055] The preparation method of above-mentioned polycarbonate composition, comprises the following steps:

[0056] (1) Place the PCT resin at 110° C., dry it for 6 hours, and cool it. Add the cooled PCT resin and the toughening agent into a high-speed mixer for pre-mixing;

[0057] (2) Add the white pigment, nucleating agent A, nucleating agent B, hindered phenolic antioxidant, phosphite antioxidant, lubricant and optical brightener to another high-speed mixer Mix, then join the obtained mixture in the high-speed mixer described in step (1) and mix;

[0058] (3) The mixture mixed in step (2) is placed in a parallel twin-screw extruder, and the glass fiber is added from the side feed of the parallel twin-screw extruder to melt and extrude, and granulate , the process parameters are as follows: the temperature of the first zone is 300°C, the temperature of the ...

Embodiment 2

[0061] A polyester composition of the present embodiment is prepared from the following raw materials:

[0062]

[0063] The preparation method of above-mentioned polycarbonate composition, comprises the following steps:

[0064] (1) Place the PCT resin at 110° C., dry it for 6 hours, and cool it. Add the cooled PCT resin and the toughening agent into a high-speed mixer for pre-mixing;

[0065] (2) Add white pigment, nucleating agent A, nucleating agent B, hindered phenolic antioxidant, phosphite antioxidant, lubricant and optical brightener to another high-speed mixer and mix, Then the mixture obtained is added to the high-speed mixer described in step (1) and mixed;

[0066] (3) The mixture mixed in step (2) is placed in a parallel twin-screw extruder, and the glass fiber is added from the side feed of the parallel twin-screw extruder to melt and extrude, and granulate , the process parameters are as follows: the temperature of the first zone is 295°C, the temperature o...

Embodiment 3

[0069] A polyester composition of the present embodiment is prepared from the following raw materials:

[0070]

[0071] The preparation method of above-mentioned polycarbonate composition, comprises the following steps:

[0072] (1) Place the PCT resin at 110°C, dry it for 6 hours, cool it, and add the cooled PCT resin and toughening agent into a high-speed mixer for pre-mixing;

[0073] (2) Add the white pigment, nucleating agent A, nucleating agent B, hindered phenolic antioxidant, phosphite antioxidant, lubricant and optical brightener to another high-speed mixer Mix, then join the obtained mixture in the high-speed mixer described in step (1) and mix;

[0074] (3) The mixture mixed in step (2) is placed in a parallel twin-screw extruder, and the glass fiber is added from the side feed of the parallel twin-screw extruder to melt and extrude, and granulate , the process parameters are as follows: the temperature of the first zone is 300°C, the temperature of the second...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a polyester composition and a preparation method thereof; the polyester composition is prepared from poly-1,4-cyclohexane dimethylene terephthalate (PCT) resin, glass fiber, nucleating agent A, nucleating agent B, a flexibilizer, an antioxidant, a lubricant and an additive. The poly-1,4-cyclohexane dimethylene terephthalate (PCT) resin has number-average molecular weight of 25000 to 30000; the nucleating agent A is sodium carboxylate organic small-molecular nucleating agent, having molecular weight of 100-200 g / mol; the nucleating agent B is an ionic polymer salt nucleating agent. The polyester composition has higher crystallizing rate so that a material takes short time to form, time cost of product processing is saved, crystallizing rate is largely increased, and the comprehensive properties of the material, such as impact property, bending performance, and thermal deformation temperature tolerance, can be better improved.

Description

technical field [0001] The invention relates to the field of materials, in particular to a polyester composition and a preparation method thereof. Background technique [0002] Polyester is a general term for polymers obtained by polycondensation of polyols and polyacids, mainly referring to polyethylene terephthalate (PET), poly 1,4-butylene terephthalate (PBT), polyethylene terephthalate 1,4-cyclohexanedimethanol formate (PCT), polyethylene naphthalate (PCN), polyethylene naphthalate (PEN) and their copolyesters. These polyesters are relatively inexpensive and, due to their high aromatic content, have a high glass transition temperature (T g ), which imparts good heat resistance, stiffness and toughness to shaped articles made from it. However, due to the slow crystallization rate, the use and promotion of polyester, especially poly-1,4-cyclohexanedimethylene terephthalate (PCT), is limited. [0003] Polyethylene terephthalate 1,4-cyclohexanedimethanol (PCT) is a new ty...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L67/02C08L53/02C08K13/04C08K7/14C08K5/098C08K5/103C08K5/353B29C47/92B29C48/92
CPCB29C48/92B29C2948/9258B29C2948/92704C08L67/02C08L2201/08C08L2203/20C08L2205/03C08L2205/24C08L53/02C08K13/04C08K7/14C08K5/098C08K5/103C08K5/353
Inventor 朱怀才刘小强朱正红许环杰徐文明
Owner SINOPLAST NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com