Cool quick-drying hydrophilic polyester fiber and preparation method thereof

A polyester fiber and hydrophilic technology, applied in fiber treatment, single-component polyester rayon, conductive/antistatic filament manufacturing, etc., can solve the problems of poor hygroscopicity and heat absorption, and save dyeing costs , The effect of broadening the scope of application

Inactive Publication Date: 2017-08-04
绍兴喜能纺织科技有限公司
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In order to solve the current problem of poor hygroscopicity and heat absorption of polyester fiber with cool properties, the present invention provides a kind of ice-cooling quick-drying hydrophilic polyester fiber and its processing method. The polyester fiber has good hygroscopicity, excellent moisture , water vapor transport, can quickly conduct heat absorption, anti-ultraviolet, rich in trace elements and amino acids

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Use commercially available hydrophilic polyester with a melting point of 240°C, an intrinsic viscosity (η) of 0.66dl / g, and a conventional moisture regain of 1.5%.

[0026] (1) Prepare hydrophilic polyester, jade powder, pearl powder, and higher fatty acid magnesium salt according to the mass ratio of 78:10:10:2 to prepare cold masterbatch;

[0027] (2) Blend and spin the cold masterbatch and hydrophilic polyester according to the mass ratio of 5:95, the spinning temperature is 280°C, and the filter precision is 25u;

[0028] (3) The spinneret with cross-shaped spinneret holes, the spinning speed is 4300m / min, the draft ratio is 2.6, and the setting temperature is 120°C, and the ice-cooled quick-drying hydrophilic polyester fiber 1 is prepared.

[0029] Ice-cooling and quick-drying hydrophilic polyester fiber 1 cross-section is cross-shaped, breaking strength 3.4cN / dtex, breaking elongation 22%, has good hygroscopicity, excellent moisture and water vapor transportabilit...

Embodiment 2

[0031] Commercially available hydrophilic polyester with a melting point of 235°C, an intrinsic viscosity (η) of 0.63dl / g, and a public moisture regain of 1.8%.

[0032] (1) Prepare hydrophilic polyester, jade powder, pearl powder, and higher fatty acid magnesium salt according to the mass ratio of 70:13:14:3 to prepare cold masterbatch;

[0033] (2) Blend and spin the cold masterbatch and hydrophilic polyester according to the mass ratio of 4:96, the spinning temperature is 276°C, and the filter precision is 15u;

[0034] (3) The spinneret with cross-shaped spinneret holes, the spinning speed is 4000m / min, the draft ratio is 2.8, and the setting temperature is 117°C, and the ice-cooled quick-drying hydrophilic polyester fiber 2 is prepared.

[0035] Ice-cooling and quick-drying hydrophilic polyester fiber 2 cross-section is cross-shaped, breaking strength 3.0cN / dtex, breaking elongation 28%, has good hygroscopicity, excellent moisture and water vapor transportability, can con...

Embodiment 3

[0037] Commercially available hydrophilic polyester with a melting point of 245°C, an intrinsic viscosity (η) of 0.68dl / g, and a public moisture regain of 1.2%.

[0038] (1) Prepare hydrophilic polyester, jade powder, pearl powder, and higher fatty acid calcium salts according to the mass ratio of 75:11:12:2 to prepare cold masterbatches;

[0039] (2) Blend and spin the cold masterbatch and hydrophilic polyester according to the mass ratio of 6:94, the spinning temperature is 283°C, and the filter precision is 40u;

[0040] (3) The spinneret with cross-shaped spinneret holes, the spinning speed is 4600m / min, the draft ratio is 2.4, and the setting temperature is 122°C, and the cold and quick-drying hydrophilic polyester fiber 3 is prepared.

[0041] The cross-section of ice-cooling and quick-drying hydrophilic polyester fiber is cross-shaped, the breaking strength is 3.8cN / dtex, and the breaking elongation is 25%. Contains trace elements and amino acids.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Breaking strengthaaaaaaaaaa
Melting pointaaaaaaaaaa
Intrinsic viscosityaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of differential chemical fiber, and provides a cool quick-drying hydrophilic polyester fiber and a processing method thereof, which aims at solving the problem of poor moisture absorbing property and poor heat absorbing property in the existing polyester fiber with cool characteristic. The cool quick-drying hydrophilic polyester fiber has the advantages that the cross section is in a cross shape; the break strength is 2.8 to 4.0cN / dtex, and the elongation at break is 18 to 30%; jade powder and perlite powder are contained; the moisture absorbing property is good, the water and steam conveying property is excellent, the heat can be quickly conducted and absorbed, the anti-ultraviolet property is realized, and the trace element and amino acid are contained.

Description

technical field [0001] The invention relates to the technical field of differential chemical fibers, in particular to an ice-cooling quick-drying hydrophilic polyester fiber and a processing method thereof. Background technique [0002] Cool textile fibers have always been a research direction for chemical fiber workers. At first, the breathability and quick-drying of the fibers were achieved by changing the cross-section of the fibers. Later, in order to improve the hydrophilicity of polyester, many researchers added a third , The fourth monomer to develop hydrophilic modified polyester. In recent years, the thermal conductivity of polyester has been enhanced by adding mica and jade powder to polyester to improve the cooling properties of polyester fiber. With the change of consumption concept, people's requirements for summer clothing are not only stylish, but also pay more attention to the inner coolness and comfort of clothing. Conventional polyester (PET) fiber is the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D01F6/92D01F1/10D01F1/09D01D5/253D01D13/00
CPCD01F6/92D01D5/253D01D13/00D01F1/09D01F1/10D01F1/106
Inventor 缪国华张娜
Owner 绍兴喜能纺织科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com