Multistage Heat Treatment Process for Composition Homogenization of aq80m Magnesium Alloy Billet

A technology of composition homogenization and magnesium alloy, applied in the field of magnesium alloy heat treatment

Active Publication Date: 2021-05-04
CENT SOUTH UNIV
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there are few reports on the homogenization heat treatment process of AQ80M magnesium alloy components, especially for large-size AQ80M magnesium alloy ingots.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Multistage Heat Treatment Process for Composition Homogenization of aq80m Magnesium Alloy Billet
  • Multistage Heat Treatment Process for Composition Homogenization of aq80m Magnesium Alloy Billet

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Put high-purity magnesium-aluminum-zinc ingots and MnCl in the smelting furnace in sequence 2 Granules, Mg-RE, Mg-Ca intermediate alloys and high-purity silver, the melting temperature is controlled at 660-790 °C; after the materials are melted, the slag is removed, and the bottom of the melt is filled with argon gas to stir and refine for 10 minutes; after refining, let it stand and cool down to 690 ℃, keep warm for 1h; press the melt into the electromagnetic mold, wait for the melt above the ingot to solidify and crystallize and the liquid level is 65mm from the vertical height of the upper surface of the mold, start the electromagnetic coil in the mold and start the casting machine at the same time to vertically For ingot pulling, the furnace temperature is 680-685°C during stable casting, the melt temperature in the splitter plate is 646-650°C, the ingot pulling speed is 36mm / min, and the cooling water flow rate is 26m 3 / h, the electromagnetic frequency applied by ...

Embodiment 2

[0021] Put high-purity magnesium-aluminum-zinc ingots and MnCl in the smelting furnace in sequence 2 Granules, Mg-RE, Mg-Ca intermediate alloys and high-purity silver, the melting temperature is controlled at 665-800 °C; after the materials are melted, the slag is removed, and the bottom of the melt is filled with argon gas for stirring and refining for 12 minutes; after refining, let stand and cool down to 688 ℃, keep warm for 1.5h; press the melt into the electromagnetic crystallizer, when the melt above the ingot head solidifies and crystallizes and the liquid level is 50mm vertically from the upper surface of the mold, start the electromagnetic coil in the mold and start the casting machine at the same time Vertical ingot pulling, the temperature in the furnace is 682-688°C during stable casting, the melt temperature in the splitter plate is 648-653°C, the ingot pulling speed is 36mm / min, and the cooling water flow rate is 34m 3 / h, the electromagnetic frequency applied by...

Embodiment 3

[0023] Put high-purity magnesium-aluminum-zinc ingots and MnCl in the smelting furnace in sequence 2 Granules, Mg-RE, Mg-Ca intermediate alloy and high-purity silver, the melting temperature is controlled at 670-780 °C; after the material is melted, the slag is removed, and the bottom of the melt is filled with argon gas for stirring and refining for 12 minutes; after refining, let it stand and cool down to 690 ℃, keep warm for 1h; press the melt into the electromagnetic crystallizer, when the melt above the ingot head is solidified and crystallized and the vertical height of the liquid level from the upper surface of the mold is 40mm, start the electromagnetic coil in the mold and start the casting machine at the same time to vertically For ingot pulling, the temperature in the furnace is 685-688°C during stable casting, the melt temperature in the splitter plate is 656-660°C, the ingot pulling speed is 21mm / min, and the cooling water flow rate is 40m 3 / h, the electromagneti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
lengthaaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a multi-stage heat treatment process for homogenizing the components of an AQ80M magnesium alloy billet. Mn0.05‑0.30%, RE0.01‑0.10%, Ca0.001‑0.020%. In the present invention, the large-size ingot is first placed in the annealing furnace, then the temperature is raised to 240-260°C and kept for 4-10 hours; then the temperature of the annealing furnace is raised to 410-420°C and kept for 32-48 hours; The furnace door is raised, and the billet is cooled to 250~300°C with the furnace, and then pushed out of the furnace to cool to room temperature in air. The invention adopts a multi-stage homogenization process, avoids the problems of excessive thermal stress and thermal cracking during the solid solution of large-sized ingots, promotes the full dissolution of the coarse second phase in the matrix, and promotes the uniform distribution of alloy elements.

Description

technical field [0001] The invention belongs to the technical field of magnesium alloy heat treatment, and relates to a multi-stage heat treatment process for homogenizing components of an AQ80M magnesium alloy billet. Background technique [0002] Magnesium alloys are known as "green engineering materials in the 21st century" because of their advantages such as low density, high specific strength, good damping performance, recyclability and pollution-free, and have become the structural materials with the most development potential in the fields of aerospace, national defense and military industry. one. AQ80M (Mg-Al-Zn-Ag series) magnesium alloy, as a medium-strength heat-resistant magnesium alloy, has good hot workability, room temperature mechanical properties and low cost, and it can be improved by adding a small amount of Ag element. High-temperature mechanical properties at a service temperature of 100-150°C; at present, this alloy has been successfully applied to the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22C1/03C22C23/02C22F1/06
CPCC22C1/03C22C23/02C22F1/06
Inventor 蒋树农曾钢刘楚明高永浩许诗源魏建胜
Owner CENT SOUTH UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap