Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Environment-friendly decorative plate

A decorative board and decorative board technology, applied in the field of environmental protection decorative board, can solve the problems of poor environmental protection performance of decorative board, low formaldehyde adsorption and degradation rate, wear resistance, poor pressure resistance and the like, and achieve low production cost, simple preparation process, The effect of prolonging the service life

Inactive Publication Date: 2017-08-29
MAANSHAN RUNQI NEW MATERIAL SCI & TECH
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing decorative boards have poor environmental protection performance, high formaldehyde emission, low formaldehyde adsorption and degradation rate, poor wear resistance and compression resistance, and short service life.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] The proportion of ingredients used is: 20 parts of nano carbon powder; 3 parts of PVC resin; 10 parts of reinforcing fiber; 1 part of flame retardant; 1 part of dispersant; 8 parts of polyethylene wax; 3 parts of water-based polyurethane, 5 parts of foam regulator 3 parts, stearic acid 3 parts, sodium fluorosilicate 3 parts, titanium dioxide 5 parts, stabilizer 3 parts, heavy calcium carbonate 25 parts, calcium sulfate whiskers 15 parts, silica fume 10 parts, diatomaceous earth 10 parts.

[0017] The manufacturing method of this embodiment includes the following steps:

[0018] A. Nano carbon powder; PVC resin; reinforcing fiber; flame retardant; dispersant; polyethylene wax; water-based polyurethane, foam regulator, stearic acid, sodium fluorosilicate, titanium dioxide, stabilizer, heavy calcium carbonate , calcium sulfate whiskers, silica fume, and diatomaceous earth are mixed and added to the mixer for high and low speed stirring. First, low speed stirring is perform...

Embodiment 2

[0024] The proportion of ingredients used is: 40 parts of nano carbon powder; 10 parts of PVC resin; 25 parts of reinforcing fiber; 5 parts of flame retardant; 5 parts of dispersant; 12 parts of polyethylene wax; 8 parts, 8 parts of stearic acid, 9 parts of sodium fluorosilicate, 12 parts of titanium dioxide, 10 parts of stabilizer, 40 parts of heavy calcium carbonate, 30 parts of calcium sulfate whiskers, 25 parts of silica fume, and 25 parts of diatomaceous earth.

[0025] The manufacturing method of this embodiment includes the following steps:

[0026] A. Nano carbon powder; PVC resin; reinforcing fiber; flame retardant; dispersant; polyethylene wax; water-based polyurethane, foam regulator, stearic acid, sodium fluorosilicate, titanium dioxide, stabilizer, heavy calcium carbonate , calcium sulfate whiskers, silica fume, and diatomaceous earth are mixed and added to the mixer for high and low speed stirring. First, low speed stirring is performed at a stirring rate of 500 ...

Embodiment 3

[0032] The proportion of ingredients used is: 25 parts of nano carbon powder; 4 parts of PVC resin; 12 parts of reinforcing fiber; 2 parts of flame retardant; 2 parts of dispersant; 9 parts of polyethylene wax; 4 parts of water-based polyurethane, 6 parts of foam regulator 4 parts, stearic acid 4 parts, sodium fluorosilicate 4 parts, titanium dioxide 6 parts, stabilizer 4 parts, heavy calcium carbonate 28 parts, calcium sulfate whiskers 17 parts, silica fume 13 parts, diatomaceous earth 12 parts.

[0033] The manufacturing method of this embodiment includes the following steps:

[0034] A. Nano carbon powder; PVC resin; reinforcing fiber; flame retardant; dispersant; polyethylene wax; water-based polyurethane, foam regulator, stearic acid, sodium fluorosilicate, titanium dioxide, stabilizer, heavy calcium carbonate , calcium sulfate whiskers, silica fume, and diatomaceous earth are mixed and added to the mixer for high and low speed stirring. First, low speed stirring is perfo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an environment-friendly decorative plate. The decorative plate comprises the following components in parts by weight: 20-40 parts of nano carbon powder, 3-10 parts of PVC resin, 10-25 parts of reinforced fibers, 1-5 parts of a flame retardant, 1-5 parts of a dispersing agent, 8-12 parts of polyethylene wax, 3-8 parts of waterborne polyurethane, 5-15 parts of a foaming regulator, 3-8 parts of stearic acid, 3-9 parts of sodium fluosilicate, 5-12 parts of titanium dioxide, 3-10 parts of a stabilizer, 25-40 parts of ground calcium carbonate, 15-30 parts of calcium sulfate whiskers, 10-25 parts of silica fume and 10-25 parts of diatomite. The environment-friendly decorative plate disclosed by the invention has the advantages that the preparation technology is simple, the production process is environment-friendly and pollution-free, the obtained decorative plate can adsorb and degrade harmful substances such as sulfide, nitride, formaldehyde, benzene and phenol, the production cost is low, the economic benefit is good, and the decorative plate also has wear-resistant and pressure-proof effects and long service life.

Description

technical field [0001] The invention relates to the technical field of decorative board preparation, in particular to an environmentally friendly decorative board. Background technique [0002] Decorative board is a kind of man-made board. It is a thermosetting laminated plastic made of high-temperature and high-pressure adhesives after chemical treatment with a variety of special papers. The board surface has various wood grains or patterns, bright and smooth, bright and beautiful, and has high wear resistance Good physical properties such as heat resistance, cold resistance and fire resistance. The walls and roofs of many high-end houses, well-made cabinets, cabinets, tables, beds, workbenches for precision instruments, laboratory test benches, TV sets, radios and other shells of broadcasting and telecommunications equipment, mostly use this new type of material. Decorative plates. The existing decorative boards have poor environmental protection performance, high forma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/16
CPCC04B26/16C04B2111/00017C04B2201/50C04B14/022C04B20/0048C04B24/2682C04B2103/63C04B2103/408C04B24/2611C04B24/085C04B22/126C04B14/305C04B14/28C04B14/383C04B18/146C04B14/08C04B2103/0068
Inventor 张伟施享
Owner MAANSHAN RUNQI NEW MATERIAL SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com