A heat treatment method and surface hardness technology, which is applied in the field of wear-resistant steel, can solve the problems of poor unevenness, low cooling speed, and small contact water of thin-gauge products, so as to solve the problem of uneven hardness, improve the qualified rate of plate shape, and reduce the roll The effect of track speed
Inactive Publication Date: 2017-09-15
SHANDONG IRON & STEEL CO LTD
View PDF5 Cites 1 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
But on the whole, there are two problems in the wear-resistant steel in domestic steel mills: (1) Most of the domestic quenching machines use roll-gap pressure quenching machines. Since the roller table equipment is a spiral water-separating roller, this will cause the surface of the steel plate to contact The amount of water is uneven, resulting in quenching watermarks on the surface, and poor hardness uniformity; (2) The unevenness of thin-gauge products is poor, resulting in almost all high-grade and thin-gauge wear-resistant plates imported in my country
[0005] Publication number CN102191363A, titled as a Chinese patent application for a production method of a wear-resistant steel plate with a thickness of 2 to 15mm, which adopts a roll-gap press
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0024] The present invention will be described in detail through specific embodiments below.
[0025] In order to realize the invention, the wear-resistant steel whose surface is 16-50 mm without quenching watermark and whose hardness fluctuation of the whole steel plate is within HBW3 has a high degree of uniformity, the hardness is between HBW350-HBW530, and the unevenness of the steel plate reaches 0-3mm / m, A wear-resistant steel plate with tempered martensite structure was obtained. The present invention performs quenching and tempering treatment on the rolled steel plate according to the heat treatment process parameters in Table 1. The main process parameters such as quenching heating temperature and tempering temperature of the steel plate are shown in Table 1. Corresponding properties of steel plates such as testing and grinding thickness, Brinell hardness and its fluctuation value, unevenness of steel plates are also listed in Table 2.
[0026] Table 1 Main producti...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention relates to the technical field of wear-resistant steel, in particular to a heat treatment method for improving the uniformity of surface hardness of wear-resistant steel. The heat treatment method for improving the uniformity of surface hardness of wear-resistant steel of the present invention comprises the following steps: 1) carrying out shot blasting treatment on the wear-resistant steel plate in a hot-rolled state; 2) entering the steel plate after shot blasting treatment into a roller hearth type continuous heat treatment furnace Heating; 3) using high-pressure water in the spiral roller gap type pressure quenching machine to perform quenching treatment; wherein, the water volume of the high-pressure section of the quenching machine is 2800~3000m3/h, and the water volume of the low-pressure section of the quenching machine is 2300~2500m3/h; 4 ) Tempering the quenched steel plate. The wear-resistant steel plate produced by the production method of the invention has good hardness uniformity, excellent plate shape and good surface quality, the unevenness of the steel plate reaches 0-3 mm/m, and a tempered martensite structure is obtained. The preparation method is simple and practical.
Description
technical field [0001] The invention relates to the technical field of wear-resistant steel, in particular to a heat treatment method for improving the uniformity of surface hardness of wear-resistant steel. Background technique [0002] As we all know, one-third to one-half of the world's materials are consumed every year due to wear and tear. Among the current wear-resistant materials, wear-resistant steel is the most widely used. It is often made into mechanical parts such as construction machinery, mining machinery, coal mining machinery, and crushers. It is widely used in metallurgy, mining, building materials, electric power, railways, and military affairs. In various departments, such as bulldozers, loaders, excavators, dump trucks and various mining machinery, grabs, stackers and reclaimers, feeding bending structures, crusher jaws, crushing walls, rolling mortar walls, tractor track shoes, Fans grind impact plates and railway switches, etc. Many key components wil...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.