Outdoor decoration Zisha coating material for building, and preparation method thereof

A construction, purple sand technology, applied in fire-retardant coatings, anti-fouling/underwater coatings, radiation-absorbing coatings, etc., can solve the problems of lack of wall strength, unable to achieve pure green environmental protection outdoor decoration effect, etc., to achieve the removal of formaldehyde , Eliminate odor and improve sleep quality

Inactive Publication Date: 2017-09-22
徐振海
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Existing outdoor coatings are deficient in heat preservation, UV protection, color life, wall strength, etc., and cannot meet the audience's pure green and environmentally friendly outdoor decoration effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] This embodiment is suitable for relatively fine and smooth wall coating materials.

[0023] First of all, choose materials, according to the weight percentage of purple sand soil, its composition should meet the following indicators: silicon dioxide 42-65%, aluminum oxide (Al2O3) 18-31%, ferric oxide (Fe2O3) 8- 12%, Calcium Oxide (CaO) 0.75-2.38%, Magnesium Oxide (MgO) 0.3-1.85; At the same time, select mineral materials with purple, yellow, gray and other colors and classify them.

[0024] The purple sand soil ores of various colors are mined to the material yard for classification and storage. The large and small purple sand ores are crushed by a crusher into 80-120 mesh, 40-80 mesh, 20-40 mesh, and then enter the pusher kiln. Carry out firing for 7-9 hours first, the firing temperature is 800-1200 degrees Celsius, then crush and sieve the fired cooked purple sand soil material, and divide it into 80 mesh, 100 mesh, 150 mesh, 200 mesh, 325 mesh5 kind of scraps. Then...

Embodiment 2

[0029] This embodiment is suitable for wall coating materials with relatively rough texture and uneven texture.

[0030] First of all, choose materials, according to the weight percentage of purple sand soil, its composition should meet the following indicators: silicon dioxide 42-65%, aluminum oxide (Al2O3) 18-31%, ferric oxide (Fe2O3) 8- 12%, Calcium Oxide (CaO) 0.75-2.38%, Magnesium Oxide (MgO) 0.3-1.85; At the same time, select mineral materials with purple, yellow, gray and other colors and classify them.

[0031] The purple sand soil ores of various colors are mined to the material yard for classification and storage. The large and small purple sand ores are crushed by a crusher into 80-120 mesh, 40-80 mesh, 20-40 mesh, and then enter the pusher kiln. Carry out firing for 7-9 hours first, the firing temperature is 800-1200 degrees Celsius, then crush and sieve the fired cooked purple sand soil material, and divide it into 80 mesh, 100 mesh, 150 mesh, 200 mesh, 325 mesh5 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to an outdoor decoration Zisha coating material for building, and a preparation method thereof, particularly to a building coating material and a preparation method thereof, wherein the building coating material comprises, by weight, 7.0% of a dispersion water, 0.2% of a thickener EBS-481F, 0.1% of a PH value regulator RF-86, 1.0% of a cosolvent ethylene glycol, 0.8% of a film forming aid TEXANOL, 0.5% of a dispersant RT-8027, 0.1% of a fungicide 623, 13.7% of a lacquer emulsion PX-7015, the material obtained by diluting 0.1% of a thickener 730 with 0.5% of water, 20-40% of Zisha clay with a particle size of 80-120 mesh, 10-30% of Zisha clay with a particle size of 40-80 mesh, 5.0-7.5% of Zisha clay with a particle size of 20-40 mesh, and 1.0% of a waterproof agent R-75. The preparation method comprises: breaking Zisha ore, firing, crushing, screening to achieve a particle size of 80-325 mesh, and mixing to obtain the product. According to the present invention, the prepared Zisha coating material has significant comprehensive effects, particularly such as air purification, formaldehyde removing, external body thermal insulation enhancing, ultraviolet radiation preventing, natural color achieving, wall crack preventing.

Description

technical field [0001] The invention relates to a building coating and a preparation method thereof, in particular to a purple sand coating for building exterior decoration and a preparation method thereof. Background technique [0002] Existing outdoor coatings are deficient in heat preservation, UV protection, color life, wall strength, etc., and cannot reach the pure green and environmental protection outdoor decoration effect of the audience. Contents of the invention [0003] The purpose of the present invention is to provide an outdoor purple sand paint for construction and its preparation method. The purple sand paint prepared by the present invention uses purple sand as the main ingredient and other auxiliary materials. The comprehensive effect is obvious, especially it can purify air, remove formaldehyde, and strengthen the external Insulation, protection from UV rays, natural color and protection from cracks in the walls all have obvious effects. [0004] The pu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/04C09D5/14C09D5/18C09D5/32C09D7/12C09D1/00
CPCC09D133/04C08K3/36C08K5/053C08K13/02C08K2003/2206C08K2003/222C08K2003/2227C08K2003/2272C08K2201/003C09D1/00C09D5/14C09D5/18C09D5/32
Inventor 徐振海
Owner 徐振海
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap