Waterproof sun-proof outer wall coating and preparing method thereof

A technology of exterior wall coating and light resistance, applied in the direction of coating, etc., can solve the problems of affecting the appearance, service life and product value of buildings, poor waterproof performance and light resistance of coatings, and peeling of coatings, etc., to achieve excellent waterproof and Light fastness, suitable for popularization and application, covering the effect of strong adhesion

Inactive Publication Date: 2017-09-22
HEFEI GUANGMIN BUILDING MATERIAL CO LTD
View PDF5 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, when coatings are applied to the exterior walls of buildings, there are some problems. For example, the waterproof performance and light resistance of coatings are not good. The coating on the outer layer will fall off and crack, which will seriously affect the appearance, service life and product value of the building.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A waterproof and sun-resistant exterior wall coating, the following raw materials are weighed for use: 40kg of polyethersulfone resin, 30kg of polyphenylene ether resin, 25kg of pure acrylic emulsion, 15kg of modified starch, 10kg of aerated aluminum powder, 5kg of Shuangfei powder, and 5kg of zeolite powder , tetrachloroisophthalonitrile emulsion 10kg, sodium bentonite 10kg, lauryl oleate 4kg, N-methylol acrylamide 3kg, anti-radiation agent 1kg, wetting and dispersing agent 1kg, film-forming aid 1kg, Oxidant 1kg and leveling agent 1kg;

[0024] The modified starch is prepared from the following ingredients: potato starch 20kg, methacrylic acid 5kg, styrene 3kg, hydrogen peroxide 3kg and sodium stearate 2kg; Sodium fatty acid was emulsified for 30 minutes under ultrasonic conditions to obtain an emulsion; then under ultrasonic conditions, potato starch was protected by nitrogen at room temperature, preheated at 60°C for 40 minutes, maintained at 60°C and added The hydr...

Embodiment 2

[0030] A waterproof and sun-resistant exterior wall coating, the following raw materials are weighed for use: 50kg of polyethersulfone resin, 35kg of polyphenylene ether resin, 30kg of pure acrylic emulsion, 20kg of modified starch, 15kg of aerated aluminum powder, 10kg of Shuangfei powder, and 10kg of zeolite powder , tetrachloroisophthalonitrile emulsion 15kg, sodium bentonite 15kg, lauryl oleate 6kg, N-methylol acrylamide 5kg, anti-radiation agent 3kg, wetting and dispersing agent 3kg, film-forming aid 3kg, anti-radiation agent Oxidant 2kg and leveling agent 2kg;

[0031] The modified starch is prepared from the following ingredients: potato starch 20kg, methacrylic acid 5kg, styrene 3kg, hydrogen peroxide 3kg and sodium stearate 2kg; Sodium fatty acid was emulsified under ultrasonic conditions for 45 minutes to obtain an emulsion; then under ultrasonic conditions, potato starch was protected by nitrogen at room temperature, preheated at 65°C for 45 minutes, maintained at 6...

Embodiment 3

[0037] A waterproof and sun-resistant exterior wall coating, the following raw materials are weighed for use: 60kg polyethersulfone resin, 40kg polyphenylene ether resin, 35kg pure acrylic emulsion, 25kg modified starch, 20kg aerated aluminum powder, 15kg Shuangfei powder, 15kg zeolite powder , tetrachloroisophthalonitrile emulsion 20kg, sodium bentonite 20kg, lauryl oleate 8kg, N-methylol acrylamide 7kg, anti-radiation agent 5kg, wetting and dispersing agent 5kg, film-forming aid 5kg, Oxidant 3kg and leveling agent 3kg;

[0038] The modified starch is prepared from the following ingredients: potato starch 20kg, methacrylic acid 5kg, styrene 3kg, hydrogen peroxide 3kg and sodium stearate 2kg; Sodium fatty acid was emulsified for 60 minutes under ultrasonic conditions to obtain an emulsion; then under ultrasonic conditions, potato starch was protected by nitrogen at room temperature, preheated at 70°C for 50 minutes, maintained at 70°C and added The hydrogen peroxide was react...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a waterproof sun-proof outer wall coating and a preparing method thereof, and relates to the field of novel building coatings. The coating is prepared from polyethersulfone resin, polyphenylene oxide resin, pure acrylic emulsion, modified starch, aerated aluminum powder, calcium-magnesium powder, zeolite powder, tetrachloroisophthalonitrile emulsion, sodium bentonite, dodecyl oleate, N-hydroxy methyl acrylamide, an anti-irradiation agent, a wetting dispersant reagent, a film forming auxiliary, an antioxidant and a flatting agent. The preparing method of the waterproof sun-proof outer wall coating includes the steps that the raw materials are mixed and milled; water are added into the milled materials and mixed to be even, and the waterproof sun-proof outer wall coating can be obtained. The waterproof sun-proof outer wall coating is easy and convenient to prepare and low in raw-material cost, has the excellent waterproof and sun-proof performance, and is long in service life and suitable for application and popularization.

Description

technical field [0001] The invention relates to the field of novel architectural coatings, in particular to a waterproof and light-resistant exterior wall coating and a preparation method thereof. Background technique [0002] Coatings are widely used, and are used on exterior walls, interior walls and floors of buildings. At present, when coatings are applied to the exterior walls of buildings, there are some problems. For example, the waterproof performance and light resistance of coatings are not good. The coating on the outer layer will fall off and crack, which will seriously affect the appearance, service life and product value of the building. Therefore, there is a need for improvement. Contents of the invention [0003] Aiming at the problems existing in the prior art, the present invention provides a waterproof and light-resistant exterior wall coating and a preparation method thereof. The exterior wall coating is simple and convenient to prepare, has low raw ma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D181/06C09D171/12C09D133/00C09D151/02C08F251/00C08F220/14C08F220/18
CPCC09D181/06C08F251/00C08K2201/003C08L2201/08C08L2205/035C08L71/12C08L33/00C08L51/02C08K13/04C08K7/26C08K5/20C08K5/101C08K3/346C08F220/14C08F212/08
Inventor 黄洋
Owner HEFEI GUANGMIN BUILDING MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com