Fireproof cable material and preparation method thereof

A technology for fireproof cables and raw materials, applied in the production of rubber insulators, organic insulators, and bulk chemicals, etc., can solve problems such as increasing installation difficulty, affecting electricity safety, and moisture absorption by fireproof layers, achieving good aging effect and prolonging service life. , the effect of high heat resistance

Inactive Publication Date: 2017-09-29
方碧水
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The continuous development and application of electric energy is a double-edged sword. The convenience brings irreplaceable advantages to people. The other convenience is that people must always be alert to the occurrence of house fires. Electricity has become a common topic of the times, and fireproof cables have emerged as the times require. Although the technology is increasing day by day, fireproof cables still have certain limitations in terms of time, temperature and effect. At the same time, there are also problems such as moisture absorption and poor flexibility of the fireproof layer. Not only Affects the safety of electricity use and increases the difficulty of installation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A fireproof cable material and a preparation method thereof. The raw materials are composed of the following proportions in parts by weight: 12 parts of active high-purity magnesium oxide, 7 parts of magnesium chloride, 16 parts of plant fiber, 8 parts of lithopone, 5 parts of glass fiber, 10 parts of 4,4'-bis(α,α-dimethylbenzyl)diphenylamine, 8 parts of ceramic fiber, 9 parts of polyolefin, 8 parts of synthetic resin, 9 parts of silicon carbide, 7 parts of synthetic mica, HY-109 18 parts of rubber adhesive, 5 parts of PVC, 55 parts of ethanol, 32 parts of helium.

[0016] Its preparation method is as follows:

[0017] A, under normal pressure, active high-purity magnesium oxide, magnesium chloride, polyolefin and silicon carbide are mixed and stirred at room temperature, and the stirring rate is 750r / min to obtain mixture A;

[0018] B. Mix and stir glass fiber and PVC, carry out polymerization reaction with ethanol as a catalyst under high temperature and high pressu...

Embodiment 2

[0022] A fireproof cable material and a preparation method thereof. The raw materials are composed of the following proportions in parts by weight: 10 parts of active high-purity magnesium oxide, 8 parts of magnesium chloride, 17 parts of plant fiber, 6 parts of lithopone, 4 parts of glass fiber, 8 parts of 4,4'-bis(α,α-dimethylbenzyl) diphenylamine, 10 parts of ceramic fiber, 10 parts of polyolefin, 12 parts of synthetic resin, 10 parts of silicon carbide, 9 parts of synthetic mica, HY-109 20 parts of rubber adhesive, 12 parts of PVC, 60 parts of ethanol, 40 parts of helium.

[0023] Its preparation method is as follows:

[0024] A, under normal pressure, active high-purity magnesium oxide, magnesium chloride, polyolefin and silicon carbide are mixed and stirred at room temperature, and the stirring rate is 600-750r / min to obtain mixture A;

[0025] B. Mix and stir the glass fiber and PVC, carry out polymerization reaction with ethanol as a catalyst under high temperature an...

Embodiment 3

[0029] A fireproof cable material and a preparation method thereof. The raw materials are composed of the following proportions in parts by weight: 15 parts of active high-purity magnesium oxide, 5 parts of magnesium chloride, 14 parts of plant fiber, 6 parts of lithopone, 4 parts of glass fiber, 8 parts of 4,4'-bis(α,α-dimethylbenzyl)diphenylamine, 5 parts of ceramic fiber, 8 parts of polyolefin, 5 parts of synthetic resin, 6 parts of silicon carbide, 6 parts of synthetic mica, HY-109 15 parts of rubber adhesive, 8 parts of PVC, 56 parts of ethanol, 32 parts of helium.

[0030] Its preparation method is as follows:

[0031] A, normal pressure, active high-purity magnesium oxide, magnesium chloride, polyolefin and silicon carbide are mixed and stirred at room temperature, and the stirring rate is 700r / min to obtain mixture A;

[0032] B. Mix and stir glass fiber and PVC, carry out polymerization reaction with ethanol as a catalyst under high temperature and high pressure, set...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention relates to a fireproof cable material and a preparation method thereof. The fireproof cable material is prepared from the following raw material ingredients in parts by weight: 10 to 15 parts of activated high-purity magnesium oxide, 5 to 8 parts of magnesium chloride, 14 to 17 parts of plant fiber, 6 to 10 parts of lithopone, 4 to 9 parts of glass fiber, 8 to 12 parts of 4,4'-bis(alpha,alpha-dimethylbenzyl)diphenylamine, 5 to 10 parts of ceramic fiber, 8 to 10 parts of polyolefin, 5 to 12 parts of synthetic resin, 6 to 10 parts of silicon carbide, 6 to 9 parts of synthetic mica, 15 to 20 parts of HY-109 rubber adhesive, 3 to 12 parts of PVC, 50 to 60 parts of ethyl alcohol and 30 to 40 parts of helium. The materials of the fireproof cable material disclosed by the invention are easy to obtain; the fireproof cable material has the advantages of simple preparation method, low cost, large tensile strength, good self-lubricating effect, good electric insulating performance, good high temperature resistance, strong stability, oxidization resistance, good anti-ageing effect, small dielectric index, superstrong fireproof performance, small density, excellent heat-resistant effect and no crack in high temperature, low temperature and high pressure; service life of the fireproof cable material is prolonged.

Description

technical field [0001] The invention relates to a fireproof cable material and a preparation method thereof. Background technique [0002] The continuous development and application of electric energy is a double-edged sword. The convenience brings irreplaceable advantages to people. The other convenience is that people must always be alert to the occurrence of house fires. Electricity has become a common topic of the times, and fireproof cables have emerged as the times require. Although the technology is increasing day by day, fireproof cables still have certain limitations in terms of time, temperature and effect. At the same time, there are also problems such as moisture absorption and poor flexibility of the fireproof layer. Not only It affects the safety of electricity use and increases the difficulty of installation. Contents of the invention [0003] The object of the present invention is to provide a fireproof cable material and a preparation method thereof in or...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/00C08L101/00C08L27/06C08L97/02C08K13/04C08K3/22C08K7/14C08K5/18C08K3/34H01B3/28
CPCC08K2003/222C08K2201/014C08L23/00C08L2201/02C08L2201/08C08L2203/202C08L2205/035C08L2205/16H01B3/28C08L101/00C08L27/06C08L97/02C08K13/04C08K3/22C08K7/14C08K5/18C08K3/34Y02P20/54
Inventor 方碧水
Owner 方碧水
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com