Preparation method for high-conductivity electromagnetic shielding rubber with electrochemical corrosion resistance

An electromagnetic shielding and high conductivity technology, which is applied in the field of conductive rubber, can solve the problems of reducing the shielding efficiency of conductive rubber, high price, and reduced electromagnetic shielding function, and achieves excellent conductivity and electrochemical corrosion resistance, simple operation process, and reduced production. cost effect

Inactive Publication Date: 2017-10-10
BEIJING UNIV OF CHEM TECH
View PDF6 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the silver-plated aluminum powder conductive rubber still has the following defects: it is expensive; it is easy to absorb moisture and expand in a humid environment, resulting in poor contact of the conductive powder, whic...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method for high-conductivity electromagnetic shielding rubber with electrochemical corrosion resistance
  • Preparation method for high-conductivity electromagnetic shielding rubber with electrochemical corrosion resistance
  • Preparation method for high-conductivity electromagnetic shielding rubber with electrochemical corrosion resistance

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] 100 parts of methyl silicone rubber;

[0024] Nickel-coated aluminum powder (particle size 10um, nickel content 10%) 100 parts;

[0025] White carbon black (particle diameter 5nm) 5 parts;

[0026] Dicumyl peroxide (DCP) 0.1 part;

[0027] 0.1 copy of TAIC;

[0028] The preparation method of conductive rubber of the present invention comprises the following steps:

[0029] 1) Evenly disperse the silane coupling agent A-137 in the ethanol solution according to 10% of the amount of conductive powder;

[0030] 2) Add nickel-coated aluminum powder into the coupling agent solution according to the parts by weight, and obtain a coupling agent-coated conductive powder after volatilization and drying;

[0031] 3) Add silicone rubber to the rubber mill or internal mixer, then add vulcanizing agent, white carbon black, conductive powder coated with coupling agent, and vulcanizing agent to make nickel-coated aluminum powder / silicone rubber compound , Nickel-clad aluminum po...

Embodiment 2

[0039] 100 parts of methyl vinyl silicone rubber;

[0040] Nickel-coated aluminum powder (particle size 50um, nickel content 40%) 300 parts;

[0041] White carbon black (particle diameter 30nm) 10 parts;

[0042] 3 parts of 2,5-dimethyl-2,5-bis(tert-butylperoxy)hexane (DBPMH);

[0043] 2 copies of TAIC;

[0044] The preparation method of conductive rubber of the present invention comprises the following steps:

[0045] 1) Evenly disperse the silane coupling agent A-151 in the ethanol solution according to 5% of the amount of conductive powder;

[0046] 2) Add nickel-coated aluminum powder into the coupling agent solution according to the parts by weight, and obtain a coupling agent-coated conductive powder after volatilization and drying;

[0047] 3) Add silicone rubber to the rubber mill or internal mixer, then add vulcanizing agent, white carbon black, conductive powder coated with coupling agent, and vulcanizing agent to make nickel-coated aluminum powder / silicone rub...

Embodiment 3

[0055] 100 parts of fluorosilicone rubber;

[0056] Nickel-coated aluminum powder (particle size 100um, nickel content 60%) 450 parts;

[0057] White carbon black (particle diameter 60nm) 15 parts;

[0058] 1.5 parts of 1,3-bis(tert-butylperoxyisopropyl)benzene (BIPB);

[0059] 2 copies of TATC;

[0060] The preparation method of conductive rubber of the present invention comprises the following steps:

[0061] 1) Evenly disperse the silane coupling agent A-174 in the ethanol solution according to 7% of the amount of conductive powder;

[0062] 2) Add nickel-coated aluminum powder into the coupling agent solution according to the parts by weight, and obtain a coupling agent-coated conductive powder after volatilization and drying;

[0063] 3) Add silicone rubber to the rubber mill or internal mixer, then add vulcanizing agent, white carbon black, conductive powder coated with coupling agent, and vulcanizing agent to make nickel-coated aluminum powder / silicone rubber compou...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to a preparation method for high-conductivity electromagnetic shielding rubber with electrochemical corrosion resistance and belongs to the technical field of a conductive composite. In a nickel-coated aluminum powder/silicon rubber composite prepared according to the invention, the nickel-coated aluminum powder has the advantages of high electrical conductivity, low cost and excellent oxidation resistance. The rubber composite prepared according to the method has high electrical conductivity and high conductivity stability and has higher electromagnetic shielding effect and better electrochemical corrosion resistance. The preparation method is simple and feasible, is low in cost, is easy for industrialization, is suitable for the electromagnetic shielding protection in damp corrosion environments, such as, ships and unmanned stations in jungles, and has better national defense and safety significance and economic benefits.

Description

technical field [0001] The invention relates to a conductive rubber used for sealing and electromagnetic shielding, in particular to a conductive rubber with electrochemical corrosion resistance and a preparation method of the conductive rubber. Background technique [0002] The rapid development of the electronics and communication industries brings rapid information exchange, but also produces hazards such as electromagnetic wave information leakage, electromagnetic wave interference, and electromagnetic environmental pollution. Highly conductive rubber composite materials can not only effectively realize electromagnetic sealing in a wide frequency range, but also have the advantages of good elasticity, low density, low cost and easy processing. In recent years, high-conductivity rubber composite materials have developed rapidly and are widely used in various electronic and electrical equipment in military, national defense, and aerospace to play the role of electromagneti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L83/04C08L83/07C08L83/08C08K13/06C08K9/06C08K9/02C08K3/08C08K3/36C08K5/14
CPCC08K3/08C08K3/36C08K5/14C08K9/02C08K9/06C08K13/06C08K2003/0812C08K2003/0862C08K2201/001C08K2201/003C08K2201/011C08L83/04C08L83/08
Inventor 邹华许亭廖坤张继阳李红霞田明冯予星张立群
Owner BEIJING UNIV OF CHEM TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap