Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

A kind of preparation method of molten steel cleaning agent

A purification agent and molten steel technology, applied in metal processing equipment, transportation and packaging, etc., can solve the problem of not promoting the growth, floating and removal of inclusions, and not reducing the melting point of fine inclusions in steel, which is unfavorable for steel products Quality and other issues, to achieve the effect of improving purification effect, promoting removal and improving quality

Active Publication Date: 2019-07-09
MAANSHAN HUASHENG METALLURGICAL SCI & TECH DEV
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This invention improves the fluidity of the slag, purifies the molten steel to a certain extent, and reduces the content of inclusions in the molten steel. It can promote the growth, floating and removal of inclusions very well, which is not conducive to further improving the quality of steel products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of molten steel cleaning agent
  • A kind of preparation method of molten steel cleaning agent
  • A kind of preparation method of molten steel cleaning agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] The cleaning agent of this embodiment is granular, and the cleaning agent is spherical granular, and the particle diameter is 5 ~ 10mm; ): 1, the preferred 8:1 of the present embodiment, the effective components include aluminum metal, lime powder, silicon carbide powder, titanium dioxide and biomass, the effective components are as follows in parts by mass: 50-70 parts of metal aluminum, 20-70 parts of lime powder 40 parts, 5-20 parts of titanium dioxide, 5-15 parts of silicon carbide powder, 2-4 parts of biomass, selected in this embodiment: 60 kg of aluminum metal, 30 kg of lime powder, 18 kg of titanium dioxide, 15 kg of silicon carbide powder, and 3 kg of biomass.

[0042]It is worth noting that each component in the effective components is in powder form, and the particle size is ≤0.1mm, that is, metal aluminum, lime powder, titanium dioxide, and silicon carbide powder are in powder form, and metal aluminum, lime powder, titanium dioxide, raw The particle size of ...

Embodiment 2

[0067] The basic content of this embodiment is the same as that of Example 1, except that the cleaning agent is in the form of granules, the cleaning agent is in the form of spherical particles, and the diameter of the particles is 5-10mm; the cleaning agent includes effective components and bonding components, and the effective components The mass ratio to the adhesive component is (5-10):1, preferably 5:1 in this embodiment.

[0068] The effective components in the purification agent of this embodiment also include graphite powder, red jade soil and magnesium-manganese alloy; the effective components are composed according to the following mass parts, 50-70 parts of metal aluminum, 20-40 parts of lime powder, and 0-30 parts of graphite powder part, 5-20 parts of titanium dioxide, 5-15 parts of silicon carbide powder, 2-4 parts of biomass, 0-1 part of red jade soil, 0-2 part of magnesium-manganese alloy; the present embodiment is 50 kg of metal aluminum, 20 kg of lime powder, ...

Embodiment 3

[0079] The basic content of this embodiment is the same as that of Example 1, except that the adhesive component of the purifying agent also includes starch and kaolin, and the adhesive component is composed of the following parts by mass: 60-80 parts of kaolin, 20-40 parts of sulfonated phenolic resin parts, starch 0-10 parts, oil sands 0-5 parts. This embodiment is composed according to the following mass: 80 kg of kaolin, 40 kg of sulfonated phenolic resin, 5 kg of starch, and 2 kg of oil sand. Detect the total oxygen content in molten steel after modification, and record as shown in Table 1, the data change is as follows figure 1 As shown, the mass ratio of the effective component to the binding component is 6:1, and the mixture is completed to obtain the cleaning agent mixture.

[0080] A kind of preparation method of molten steel cleaning agent of the present embodiment, concrete steps are as follows:

[0081] Step 1: Preparation of Adhesive Components

[0082] Weigh ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a molten steel purifying agent, belonging to the technical field of clean steel smelting. According to the present invention, the cleaning agent mixture is obtained by mixing the effective components and the binding components, wherein the mass ratio of the effective components and the binding components is (5-10): 1; the effective components include metal aluminum, lime powder , silicon carbide powder, titanium dioxide and biomass; the bonding components include kaolin and sulfonated phenolic resin; the cleaning agent mixture is bonded and granulated under the action of a briquetting machine or a pelletizing machine to obtain a granular cleaning agent , dried and cooled for later use. The purification agent prepared by the present invention reduces the oxygen content in molten steel, and the CO gas produced by the reaction promotes the floating and removal of inclusions, and promotes the removal of inclusions in steel. The particles are small in size and evenly distributed, and the purification effect of molten steel can be improved through the cooperation of effective components and bonding components.

Description

technical field [0001] The invention belongs to the technical field of clean steel smelting, and more specifically relates to a preparation method of a molten steel purifying agent. Background technique [0002] The performance of steel mainly depends on the chemical composition and structure of steel. The existence of inclusions in the steel destroys the continuity of the steel matrix and causes the inhomogeneity of the steel structure, which will affect the ductility, strength, toughness, fatigue performance, smoothness, corrosion resistance, welding performance and electromagnetic properties of the steel. big impact. The continuous casting process will also cause nozzle nodules, which have a great impact on the production of the continuous casting process and the quality of the slab. Therefore, iron and steel researchers from various countries have devoted a lot of energy to the research on the removal of inclusions in steel, and have also achieved great results in the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C21C7/04B22F1/00
CPCC21C7/0037C21C7/04B22F1/065B22F1/10
Inventor 王海军从俊强凌海涛杨建刘桂成
Owner MAANSHAN HUASHENG METALLURGICAL SCI & TECH DEV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com