Anti-radiation computer screen protective film and preparation method thereof

A computer screen and protective film technology, which is applied in the field of computer equipment, can solve the problems of accumulating electric charge, absorbing dust, and discharge of surrounding objects, etc., and achieves the effects of low cost, reduced damage, and good film forming effect

Inactive Publication Date: 2017-10-17
HEFEI DONGHENGRUI ELECTRONICS TECH CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The working principle of the computer will cause the accumulation of charge on the computer screen, causing adverse consequences such as dust absorption and discharge with surrounding objects.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A radiation-proof computer screen protective film, comprising the following raw materials in parts by weight: 10 parts of xanthan gum, 15 parts of carrageenan, 2 parts of nano-titanium dioxide, 3 parts of nano-zinc oxide, 2 parts of rose essential oil, 1.5 parts of yttrium nitrate, graphite 3 parts of vinyl dispersion liquid, 1 part of polyimide resin, 1 part of diamine monomer, 0.5 parts of plasticizer.

[0023] The particle size of the nano titanium dioxide is 100nm.

[0024] The preparation method of described graphene dispersion liquid is:

[0025] Add 90mL of concentrated sulfuric acid to the reaction bottle placed in an ice-water bath, add a solid mixture of 2g graphite powder and 4g sodium nitrate while stirring, then add 10g potassium permanganate in at least three times, control the reaction temperature at 10°C, and stir the reaction After 20 minutes, heat the water bath to 20°C, continue to stir for 3h, filter, and place the filter cake in a vacuum drying ove...

Embodiment 2

[0036] A radiation-proof computer screen protective film, comprising the following raw materials in parts by weight: 15 parts of xanthan gum, 25 parts of carrageenan, 3 parts of nano-titanium dioxide, 6 parts of nano-zinc oxide, 6 parts of rose essential oil, 2.5 parts of yttrium nitrate, graphite 7 parts of vinyl dispersion liquid, 3 parts of polyimide resin, 2 parts of diamine monomer, 2.5 parts of plasticizer.

[0037] The particle size of the nano titanium dioxide is 200nm.

[0038] The preparation method of described graphene dispersion liquid is:

[0039] Add 95mL of concentrated sulfuric acid to the reaction flask placed in an ice-water bath, add a solid mixture of 2g graphite powder and 4g sodium nitrate while stirring, then add 10g potassium permanganate in at least three times, control the reaction temperature at 15°C, and stir the reaction After 25 minutes, heat the water bath to 25°C, continue to stir for 4 hours, filter, and place the filter cake in a vacuum dryi...

Embodiment 3

[0050]A radiation-proof computer screen protective film, comprising the following raw materials in parts by weight: 25 parts of xanthan gum, 35 parts of carrageenan, 5 parts of nano-titanium dioxide, 9 parts of nano-zinc oxide, 10 parts of rose essential oil, 3.5 parts of yttrium nitrate, graphite 10 parts of vinyl dispersion liquid, 4 parts of polyimide resin, 3 parts of diamine monomer, 3.5 parts of plasticizer.

[0051] The particle size of the nano titanium dioxide is 300nm.

[0052] The preparation method of described graphene dispersion liquid is:

[0053] Add 100mL of concentrated sulfuric acid to the reaction bottle placed in an ice-water bath, add a solid mixture of 2g of graphite powder and 4g of sodium nitrate while stirring, and then add 10g of potassium permanganate in at least three times, and control the reaction temperature at 10~20°C. Stir the reaction for 30 minutes, heat the water bath to 35°C, continue to stir for 5 hours, filter, and place the filter cake...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses an anti-radiation computer screen protective film which comprises the following raw materials in parts by weight: 10-25 parts of xanthan gum, 15-35 parts of carrageenan, 2-5 parts of nano titanium dioxide, 3-9 parts of nano zinc oxide, 2-10 parts of rose essential oil, 1.5-3.5 parts of yttrium nitrate, 3-10 parts of a graphene dispersing liquid, 1-4 parts of polyimide resin, 1-3 parts of a diamine monomer and 0.5-3.5 parts of a plasticizer. The invention provides a preparation method of the anti-radiation computer screen protective film. The preparation method is simple and feasible and relatively low in cost. The film is made from natural raw materials, so that the film-forming effect is relatively good. By adding nano titanium dioxide and nano zinc oxide into the raw materials, blue light of the computer screen can be prevented from penetrating through, so that damage to people by radiation can be reduced to a certain extent.

Description

technical field [0001] The invention belongs to the field of computer equipment, and in particular relates to a radiation-proof computer screen protective film and a preparation method thereof. Background technique [0002] In today's society, people rely more and more on computers. Computers are closely related to people's study, life and work, and many people face computer screens most of the day. The working principle of the computer will cause the accumulation of charge on the computer screen, causing adverse consequences such as dust absorption and discharge with surrounding objects. At the same time, the electromagnetic radiation and reflected light generated by the computer, when facing the computer for a long time, the eyes are prone to fatigue, redness, vision loss, and even seriously affect the health of the body, such as dizziness, headache, inability to concentrate, etc. Therefore, developing a radiation-proof computer protective film with simple process, low c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L5/00C08L91/00C08L79/08C08K13/06C08K9/02C08K3/22C08K3/04C08K3/28C08K5/17C08J5/18
CPCC08L5/00C08J5/18C08J2305/00C08J2405/00C08K2003/2241C08K2003/2296C08K2201/003C08K2201/011C08L2203/16C08L2205/025C08L2205/035C08L91/00C08L79/08C08K13/06C08K9/02C08K3/22C08K3/04C08K3/28C08K5/17
Inventor 齐慧
Owner HEFEI DONGHENGRUI ELECTRONICS TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com