Preparation method and application of tetracycline-polluted water body restoring material

A technology of ethanol aqueous solution and nano-cerium dioxide, which is applied in nanotechnology for materials and surface science, water pollutants, water/sewage treatment, etc., can solve the problems of reducing the reduction and degradation efficiency of nano-zero-valent iron, and achieve easy Promote the use, reduce agglomeration, and improve the removal efficiency

Active Publication Date: 2017-11-07
广州润方环保科技股份有限公司
View PDF0 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For example, nano-zero-valent iron is easy to agglomerate, which will reduce the

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method and application of tetracycline-polluted water body restoring material
  • Preparation method and application of tetracycline-polluted water body restoring material
  • Preparation method and application of tetracycline-polluted water body restoring material

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0034] A method for preparing nano-cerium dioxide includes the following steps:

[0035] 1) Add cerium nitrate and surfactant to water, mix and stir to obtain mixed solution A;

[0036] 2) Add ammonium carbonate solution to mixed solution A and stir to obtain mixed solution B;

[0037] 3) The mixed solution B is filtered, and the resulting precipitate is washed and dried, then calcined and ground into powder to obtain nano ceria.

[0038] Further, step 3) of the preparation method of nano ceria is specifically: filtering the mixed solution B, obtaining the white colloid and washing it with ultrapure water and ethanol three times to obtain the white colloid A, and putting the resulting precipitate into It is calcined in a muffle furnace and ground into powder to obtain nano-cerium oxide.

[0039] Preferably, in step 1) of the preparation method of nano-cerium dioxide, the mass ratio of cerium nitrate, surfactant and water is (30-50):(3-5):1000.

[0040] Preferably, in step 2) of the prep...

Example Embodiment

[0054] Preparation example:

[0055] A preparation method of nano ceria particles:

[0056] (1) Add 0.1mol / L cerium nitrate hexahydrate and 4g / L PEG 4000 to 100ml ultrapure water, stir and mix;

[0057] (2) Add 150ml of 0.1mol / L (NH 4 ) 2 CO 3 The aqueous solution was added to the solution described in step (1), and stirred at 45°C for 15 minutes, filtered and washed several times to obtain white colloidal cerium carbonate;

[0058] (3) Put the white colloid in a drying oven and dry it at 80℃ for 8h;

[0059] (4) Put the dried white colloid into a muffle furnace, heat up to 500°C at 20°C / min, and roast for 4h. After the temperature of the muffle furnace drops to room temperature, take out the yellow solid and grind it into a powder to obtain nanometer two Ceria.

[0060] A kind of nano Fe 0 @CeO 2 The preparation method of particles, the steps are:

[0061] (1) Add 0.023mol / L of the above-prepared nano ceria, 0.05mol / L ferrous sulfate hexahydrate, 4g / LPVP into 100ml of 30%v / v ethanol aqu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method and application of a tetracycline-polluted water body restoring material. A preparation method of nanometer cerium dioxide comprises the following steps of (1) adding cerium nitrate and surfactant into water, mixing and stirring, so as to obtain a mixed solution A; (2) adding an ammonia carbonate solution into the mixed solution A, and stirring, so as to obtain a mixed solution B; (3) filtering the mixed solution B, washing and drying the obtained precipitate, calcining, and grinding into powder, so as to obtain the nanometer cerium dioxide. The invention also discloses a preparation method of the nanometer FeO@CeO2 (ferrous oxide@cerium dioxide) by using the nanometer cerium dioxide, and a restoration method of the tetracycline-polluted water body by using the nanometer FeO@CeO2. A heterogeneous Feton technique using the FeO@CeO2 as a catalyst is proposed to prepare the FeO@CeO2 to be applied into the restoring of the tetracycline pollution in the water body, so that the reaction activity is improved, the mineralizing degree of the tetracycline is improved, and the risk of secondary pollution is reduced.

Description

technical field [0001] The invention relates to a preparation method and application of a tetracycline polluted water restoration material. Background technique [0002] Pharmaceuticals and personal care products (PPCPs) now constitute a new class of world pollutants that have attracted great attention in recent years, including various types of antibiotics, synthetic musk, pain relievers, blood pressure drugs, contraceptives, hypnotics , diet pills, hairspray, hair dye and fungicide, etc. Tetracycline antibiotics are broad-spectrum antibiotics widely used throughout the world in human and veterinary health, in aquaculture, in feed as growth promoters and to inhibit fungal growth in fruit trees. [0003] Traditional tetracycline removal methods are mainly physical adsorption and photodegradation, but physical adsorption cannot completely degrade pollutants, and other methods need to be further selected to achieve complete mineralization, while photodegradation is limited by...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01J23/83C01F17/00C02F1/72C02F1/28C02F1/52B82Y30/00B82Y40/00C02F101/30
CPCB01J23/83B82Y30/00B82Y40/00C01P2004/03C01P2004/04C02F1/281C02F1/5236C02F1/722C02F1/725C02F2101/30C02F2305/026C01F17/206
Inventor 方战强陈俊毅
Owner 广州润方环保科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products