Anti-interference waterproof weather-proof data cable material and preparation method thereof

A cable and data technology, applied in the field of anti-interference, waterproof, weather-resistant data cable materials and their preparation, can solve the problems of failing to meet the increasingly demanding requirements of consumers, lack of dry hand feel, and high signal distortion. Good application prospect, smooth touch, high mechanical strength effect

Inactive Publication Date: 2017-11-07
HEFEI DONGHENGRUI ELECTRONICS TECH CO LTD
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In addition, the thermoplastic elastomers currently commonly used in the production of earphone cables and data cables generally contain mineral oils such as paraffin oil or naphthenic oil, which are likely to cause yellowing of the wire during product use, and the surface is sticky, dust-absorbed, precipitated, and not resistant to dirt , there is no dry feel, and it cannot meet the increasingly stringent requirements of consumers
For signal transmission cables with high signal transmission requirements, the anti-interference ability is poor during the transmission process, and the signal distortion is high, so it cannot meet people's needs.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] An anti-interference waterproof and weather-resistant data cable material in this embodiment includes the following raw materials in parts by weight:

[0035] 60 parts of low molecular weight polyvinylidene fluoride, 40 parts of PVB resin, 10 parts of polyethylene wax, 6 parts of polyvinyl alcohol, 4 parts of coupling agent, 7 parts of rare earth calcium zinc composite stabilizer, 8 parts of water resistance additive, 3 parts of lubricant parts, 10 parts of electromagnetic shielding additives, 12 parts of processing aids, and 7 parts of carbon black.

[0036] The average molecular weight of the low molecular weight polyvinylidene fluoride in this embodiment is 100,000-110,000, and the flow rate is 35-45 g / l0min.

[0037] In this embodiment, the coupling agent is a silane coupling agent.

[0038] The water-resistant additive in this embodiment is nano-barium sulfate; the lubricant is a mixture of zinc stearate, barium stearate, and silicone masterbatch in a weight ratio...

Embodiment 2

[0048] An anti-interference waterproof and weather-resistant data cable material in this embodiment includes the following raw materials in parts by weight:

[0049] 70 parts of low molecular weight polyvinylidene fluoride, 50 parts of PVB resin, 14 parts of polyethylene wax, 10 parts of polyvinyl alcohol, 8 parts of coupling agent, 9 parts of rare earth calcium zinc composite stabilizer, 10 parts of water resistance additive, 7 parts of lubricant parts, 20 parts of electromagnetic shielding additives, 16 parts of processing aids, and 9 parts of carbon black.

[0050] The average molecular weight of the low molecular weight polyvinylidene fluoride in this embodiment is 100,000-110,000, and the flow rate is 35-45 g / l0min.

[0051] In this embodiment, the coupling agent is a titanate coupling agent.

[0052] The water-resistant additive in this embodiment is nano-barium sulfate; the lubricant is a mixture of zinc stearate, barium stearate, and silicone masterbatch in a weight r...

Embodiment 3

[0062] An anti-interference waterproof and weather-resistant data cable material in this embodiment includes the following raw materials in parts by weight:

[0063] 65 parts of low molecular weight polyvinylidene fluoride, 45 parts of PVB resin, 12 parts of polyethylene wax, 8 parts of polyvinyl alcohol, 6 parts of coupling agent, 8 parts of rare earth calcium zinc composite stabilizer, 9 parts of water resistance additive, 5 parts of lubricant parts, electromagnetic shielding additives 15 parts, processing aids 14 parts, carbon black 8 parts.

[0064] The average molecular weight of the low molecular weight polyvinylidene fluoride in this embodiment is 100,000-110,000, and the flow rate is 35-45 g / l0min.

[0065] In this embodiment, the coupling agent is an aluminate coupling agent.

[0066] The water-resistant additive in this embodiment is nano-barium sulfate; the lubricant is a mixture of zinc stearate, barium stearate, and silicone masterbatch in a weight ratio of 2:2:1...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
thicknessaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses an anti-interference waterproof weather-proof data cable material which comprises the following raw materials in parts by weight: 60-70 parts of low molecular weight polyvinylidene fluoride, 40-50 parts of PVB resin, 10-14 parts of polyethylene wax, 6-10 parts of polyvinyl alcohol, 4-8 parts of coupling reagent, 7-9 parts of a rare earth zinc calcium compound stabilizer, 8-10 parts of a water-resisting additive, 3-7 parts of a lubricating agent, 10-20 parts of an electromagnetic shielding additive, 12-16 parts of a processing agent and 7-9 parts of carbon black. The cable material disclosed by the invention has better surface flexibility, smooth touch feel, acid-base resistance property, anti-aging property, excellent signal shielding effect, high temperature resistance and high mechanical strength; besides, the data cable material has a better waterproof property; and meanwhile, the material cost is low, the raw materials are easily available, the preparation method is simple and the data cable material has high practical value and excellent application prospect.

Description

technical field [0001] The invention relates to the technical field of electronic product accessories, in particular to an anti-interference waterproof and weather-resistant data cable material and a preparation method thereof. Background technique [0002] On the one hand, the low-smoke and halogen-free flame retardant systems of domestic cable sheaths are mainly concentrated in two directions: one is organic phosphorus and nitrogen; the other is inorganic hydrates. There are many kinds of organophosphorus nitrogen flame retardants, and the main flame retardant mechanism is to use the covering effect after carbonization. The disadvantage is that the molecular weight is small, and it is easy to drip after being charcoal. The flame retardant of inorganic hydrate mainly depends on the loss of water and heat absorption of inorganic hydrate at high temperature. The commonly used flame retardants are aluminum hydroxide, magnesium hydroxide, zinc borate, etc. The low-smoke and h...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/16C08L29/14C08L23/06C08L29/04C08L83/04C08K13/04C08K3/04C08K5/098C08K3/30C08K7/28C08K7/06C08K5/526H01B3/44
CPCC08L27/16C08K2003/3045C08K2201/011C08K2201/014C08L2201/08C08L2203/202C08L2205/035H01B3/443C08L29/14C08L23/06C08L29/04C08L83/04C08K13/04C08K3/04C08K5/098C08K3/30C08K7/28C08K7/06C08K5/526
Inventor 齐慧
Owner HEFEI DONGHENGRUI ELECTRONICS TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products