Radiation-proof anti-cracking heat-insulating concrete

A thermal insulation concrete and radiation protection technology, applied in the field of thermal insulation concrete, can solve problems such as cracking damage, volume deformation, etc., achieve the effects of improving strength, overcoming poor toughness, and remarkable early strength effect

Inactive Publication Date: 2017-11-17
BEIJING JUNXIU CONSULTATION CO LTD
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are still many defects in the current foamed concrete. For example, concrete is a brittle material. During use, it is subjected to various physical, chemical or mechanical effects from the environment, which will cause its volume to deform. When the deformation exceeds a certain limit, it will eventually lead to cracking. destroy

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Concrete components include 70 parts by weight of cement, 10 parts of zirconia, 4 parts of silicon micropowder, 5 parts of sodium silicate, 10 parts of sodium fluorosilicate, 10 parts of barite, 5 parts of carbon fiber, and hard boron calcium 4 parts of stone, 3 parts of polyurethane particles, 8 parts of cyanite honeycomb ceramic powder, 5 parts of polyethylene glycol monomethyl ether methacrylate, and 3 parts of calcium lignosulfonate.

[0016] The preparation method of the present embodiment comprises the following steps:

[0017] A. After mixing zirconia, silicon micropowder, sodium silicate, sodium fluorosilicate, barite, colemanite, polyurethane particles, and bluestone honeycomb ceramic powder, add them to the pulverizer and grind them at a speed of 1200 rpm. The crushing time was 20min to obtain mixture A;

[0018] B. Add carbon fiber, polyethylene glycol monomethyl ether methacrylate, and calcium lignosulfonate to mixture A, mix and add to a heating tank for h...

Embodiment 2

[0021] Concrete components include 100 parts by weight of cement, 20 parts of zirconia, 12 parts of silicon micropowder, 10 parts of sodium silicate, 20 parts of sodium fluorosilicate, 20 parts of barite, 12 parts of carbon fiber, and hard boron calcium 12 parts of stone, 9 parts of polyurethane particles, 18 parts of bluestone honeycomb ceramic powder, 12 parts of polyethylene glycol monomethyl ether methacrylate, and 9 parts of calcium lignosulfonate.

[0022] The preparation method of the present embodiment comprises the following steps:

[0023] A. After mixing zirconia, silicon micropowder, sodium silicate, sodium fluorosilicate, barite, colemanite, polyurethane particles, and bluestone honeycomb ceramic powder, add them to the pulverizer and grind them at a speed of 1200 rpm. The crushing time was 20min to obtain mixture A;

[0024] B. Add carbon fiber, polyethylene glycol monomethyl ether methacrylate, and calcium lignosulfonate to mixture A, mix and add to a heating t...

Embodiment 3

[0027] Concrete components include 75 parts by weight of cement, 12 parts of zirconia, 6 parts of silicon micropowder, 6 parts of sodium silicate, 12 parts of sodium fluorosilicate, 12 parts of barite, 6 parts of carbon fiber, and hard boron calcium 5 parts of stone, 4 parts of polyurethane particles, 9 parts of cyanite honeycomb ceramic powder, 7 parts of polyethylene glycol monomethyl ether methacrylate, and 4 parts of calcium lignosulfonate.

[0028] The preparation method of the present embodiment comprises the following steps:

[0029] A. After mixing zirconia, silicon micropowder, sodium silicate, sodium fluorosilicate, barite, colemanite, polyurethane particles, and bluestone honeycomb ceramic powder, add them to the pulverizer and grind them at a speed of 1200 rpm. The crushing time was 20min to obtain mixture A;

[0030] B. Add carbon fiber, polyethylene glycol monomethyl ether methacrylate, and calcium lignosulfonate to mixture A, mix and add to a heating tank for h...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses radiation-proof anti-cracking heat-insulating concrete. The concrete comprises the following components in parts by weight: 70-100 parts of cement, 10-20 parts of zirconia, 4-12 parts of silica powder, 5-10 parts of sodium silicate, 10-20 parts of sodium fluosilicate, 10-20 parts of barite, 5-12 parts of carbon fiber, 4-12 parts of colemanite, 3-9 parts of TPU, 8-18 parts of Cyanolite honeycomb powder, 5-12 parts of polyethylene methyl ether methacrylate, and 3-9 parts of calcium lignosulphonate. A preparation method is simple, the prepared concrete has excellent radiation-proof, anti-cracking and heat-insulating performances, and overcomes the defects that the concrete in the prior art is poor in toughness, low in strength and easy to crack.

Description

technical field [0001] The invention relates to the technical field of concrete preparation, in particular to a radiation-proof and crack-proof thermal insulation concrete. Background technique [0002] Foamed concrete is a kind of foaming agent that is fully foamed mechanically through the foaming system of the foaming machine, and the foam is evenly mixed with cement slurry, and then cast-in-place construction or mold molding is performed, and a large amount of concrete is formed through natural curing. A new type of lightweight thermal insulation material with closed pores; it has special properties such as thermal insulation, sound absorption and sound insulation, and lightweight porous, making it widely used not only in housing construction, but also in various industries such as roads, bridges, and tunnels. fields have been widely applied. However, there are still many defects in the current foamed concrete. For example, concrete is a brittle material. During use, it ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/26C04B14/06C04B14/38C04B14/36C04B24/18C04B24/32C04B111/34
CPCC04B28/26C04B14/062C04B14/36C04B14/386C04B24/18C04B24/32C04B2111/00025C04B2111/343C04B2201/50C04B7/00C04B14/306C04B22/126C04B14/368C04B24/282C04B18/027
Inventor 齐明
Owner BEIJING JUNXIU CONSULTATION CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka