Wear-resistant and low-cracking possibility football fabric and preparation method thereof

A football and fabric technology, applied in the field of football fabric and its preparation, can solve the problems of poor wear resistance, high price, easy cracking, etc., achieve good wear resistance and toughness, broad market prospects, and prolong the service life.

Inactive Publication Date: 2017-12-05
丁燕飞
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, football fabrics are generally made of genuine leather or artificial leather. The price of genuine leather fabrics is high and the performance is average, so the market share is low. The existing football fabrics made of artificial leather have the defects of poor wear resistance and easy cracking. , affecting the service life of football

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A wear-resistant and non-cracking football fabric, made of the following raw materials in parts by weight: 120 parts of thermoplastic polyurethane elastomer rubber, 30 parts of neoprene rubber, 18 parts of polyisoprene rubber, 3 parts of benzoyl peroxide 2 parts, 2 parts of dicumyl peroxide, 1 part of epoxy butyl octadecanoate, 2 parts of calcium lignosulfonate, 4 parts of sodium lauryl sulfate phenol, 20 parts of mica powder, 13 parts of modified basalt fiber , 7 parts of nano aluminum hydroxide, 0.5 parts of benzophenone, 2 parts of polyethersulfone, 3 parts of white carbon black, 1.5 parts of perchlorocyclopentane, 5 parts of melamine polyphosphate, 0.8 parts of antioxidant, 0.3 part of zinc borate, 1.0 part of antioxidant; wherein, the antioxidant is antioxidant 1010, and the antioxidant is antioxidant RD.

[0032] The preparation method of the modified basalt fiber is as follows:

[0033] a) Take basalt fiber, put it into 30% hydrochloric acid solution, ultrasonic...

Embodiment 2

[0046] A wear-resistant and non-cracking football fabric, made of the following raw materials in parts by weight: 123 parts of thermoplastic polyurethane elastomer rubber, 31 parts of neoprene rubber, 19 parts of polyisoprene rubber, 4.5 parts of benzoyl peroxide 2.8 parts of dicumyl peroxide, 1.7 parts of butyl epoxy octadecanoate, 2.3 parts of calcium lignosulfonate, 4.4 parts of sodium lauryl sulfate phenol, 21 parts of mica powder, 16 parts of modified basalt fiber , 9 parts of nano aluminum hydroxide, 0.9 parts of benzophenone, 2.2 parts of polyethersulfone, 3.3 parts of white carbon black, 1.6 parts of perchlorocyclopentane, 5.8 parts of melamine polyphosphate, 1.1 parts of antioxidant, 0.5 part of zinc borate, 1.1 part of antioxidant; wherein, the antioxidant is antioxidant 1010, and the antioxidant is antioxidant RD.

[0047] The preparation method of the modified basalt fiber is as follows:

[0048] a) Take basalt fiber, put it into 30% hydrochloric acid solution, ultr...

Embodiment 3

[0061] A wear-resistant and non-cracking football fabric, made of the following raw materials in parts by weight: 125 parts of thermoplastic polyurethane elastomer rubber, 33 parts of neoprene rubber, 20 parts of polyisoprene rubber, 4 parts of benzoyl peroxide 2.5 parts of dicumyl peroxide, 1.4 parts of butyl epoxy octadecanoate, 2.5 parts of calcium lignosulfonate, 4.5 parts of sodium lauryl sulfate phenol, 22 parts of mica powder, 15 parts of modified basalt fiber , 9 parts of nano aluminum hydroxide, 0.8 parts of benzophenone, 2.6 parts of polyethersulfone, 3.4 parts of white carbon black, 1.8 parts of perchlorocyclopentane, 5.5 parts of melamine polyphosphate, 1 part of antioxidant, 0.4 parts of zinc borate, 1.3 parts of antioxidant; wherein, the antioxidant is antioxidant 1010, and the antioxidant is antioxidant RD.

[0062] The preparation method of the modified basalt fiber is as follows:

[0063] a) Take basalt fiber, put it into 30% hydrochloric acid solution, ultra...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a wear-resistant and low-cracking possibility football fabric. The football fabric is prepared from thermoplastic urethane elastomer rubber, neoprene, polyisoprene rubber, benzoyl peroxide, dicumyl peroxide, butyl epoxyoctadecanoate, calcium lignosulfonate, sodium lauryl sulfate phenol, mica powder, modified basalt fibers, nanometer aluminum hydroxide, benzophenone, polyethersulfone, white carbon black, perchlorocyclopentane, melamine polyphosphate, an antioxidant, zinc borate and an antiager. The invention discloses a preparation method of the wear-resistant and low-cracking possibility football fabric. The wear-resistant and low-cracking possibility football fabric can satisfy football material requirements on weatherability, flame retardancy, thermal stability and corrosion resistance, has good abrasion resistance and toughness, is not easy to crack during use, prolongs a service life of a football and has a wide market prospect.

Description

technical field [0001] The invention relates to the technical field of artificial leather, in particular to a wear-resistant and hard-to-crack football fabric and a preparation method thereof. Background technique [0002] Football, known as "the world's number one sport", is the most influential individual sport in the global sports world. A standard football match consists of two teams consisting of 10 players and 1 goalkeeper, a total of 11 people, fighting and attacking on a rectangular grass field. The purpose of the game is to shoot the football into the opponent's goal as much as possible. Every time a ball is scored, one point can be scored. When the game is over, the team with the most points wins. If the score is the same within the specified time of the game, it depends on the rules of the game, and the competition can be divided in the form of drawing lots, rematch in overtime or penalty kicks (12 yards). [0003] Football is a prop needed for football. At pre...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L75/04C08L11/00C08L9/00C08L81/06C08K13/06C08K9/00C08K9/02C08K7/10C08K5/14C08K3/34C08K3/22C08K3/36C08K3/38
Inventor 丁燕飞
Owner 丁燕飞
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com