High-thermal-stability alkaline battery PA sealing ring and preparation method thereof

A high thermal stability, alkaline battery technology, applied in the direction of sealing materials, battery boxes/covers, battery pack components, etc., can solve the problems of poor low temperature resistance, large molding shrinkage, affecting applications, etc., to achieve good gas barrier properties, Good fatigue resistance and excellent electrical insulation effect

Inactive Publication Date: 2017-12-22
无锡九宇宝新能源科技有限公司
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Alkaline battery sealing rings in the prior art generally use polypropylene (PP) or nylon 66 (PA66), among which polypropylene has poor low temperature resistance, is flammable and has low mechanical strength, and its use rate is not as popular as that of nylon sealing rings.
Due to the presence of amide groups, nylon has good wear resistance, self-lubrication, oil resistance, mechanical properties, gas

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] Embodiment 1: a kind of alkaline battery PA sealing ring of high thermal stability, it is made up of the raw material of following parts by weight: nylon 66 100 parts, polytrimethylene terephthalate 12 parts, polypropylene 8 parts, compatibilizer 15 parts, SEBS thermoplastic elastomer 5 parts, flame retardant additive 4 parts, 1,1-ethylene diacetate 1 part.

[0014] Further, the compatibilizer is polypropylene grafted maleic anhydride and maleic anhydride grafted ethylene propylene diene rubber, the mass ratio of which is 2:1; the molecular weight of the SEBS thermoplastic elastomer is 290000 ~ 310000; The flame retardant additive mentioned is a fluorophosphazene compound, and its chemical formula is N 3 P 3 f 5 Oh 2 CH 3 .

[0015] A kind of preparation method of the alkaline battery PA sealing ring of described a kind of high thermal stability, comprises the following steps: raw material nylon 66, polytrimethylene terephthalate, polypropylene, compatibilizer, SEB...

Embodiment 2

[0016] Embodiment 2: a kind of alkaline battery PA sealing ring of high thermal stability, it is made up of the raw material of following parts by weight: nylon 66 100 parts, polytrimethylene terephthalate 8 parts, polypropylene 5 parts, compatibilizer 10 parts, 3 parts of SEBS thermoplastic elastomer, 2 parts of flame retardant additive, 0.5 part of 1,1-ethylene diacetate.

[0017] Further, the compatibilizer is polypropylene grafted maleic anhydride and maleic anhydride grafted ethylene propylene diene rubber, and its mass part ratio is 1:1; the molecular weight of the SEBS thermoplastic elastomer is 290000 ~ 310000; The flame retardant additive mentioned is a fluorophosphazene compound, and its chemical formula is N 3 P 3 f 5 Oh 2 CH 3 .

[0018] A kind of preparation method of the alkaline battery PA sealing ring of described a kind of high thermal stability, comprises the following steps: raw material nylon 66, polytrimethylene terephthalate, polypropylene, compatibi...

Embodiment 3

[0019] Embodiment 3: a kind of alkaline battery PA sealing ring of high thermal stability, it is made up of the raw material of following parts by weight: nylon 66 100 parts, polytrimethylene terephthalate 16 parts, polypropylene 10 parts, compatibilizer 20 parts, SEBS thermoplastic elastomer 8 parts, flame retardant additive 6 parts, 1,1-ethylene diacetate 2 parts.

[0020] Further, the compatibilizer is polypropylene grafted maleic anhydride and maleic anhydride grafted ethylene propylene diene rubber, the mass ratio of which is 3:1; the molecular weight of the SEBS thermoplastic elastomer is 290000 ~ 310000; The flame retardant additive mentioned is a fluorophosphazene compound, and its chemical formula is N 3 P 3 f 5 Oh 2 CH 3 .

[0021] A kind of preparation method of the alkaline battery PA sealing ring of described a kind of high thermal stability, comprises the following steps: raw material nylon 66, polytrimethylene terephthalate, polypropylene, compatibilizer, S...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high-thermal-stability alkaline battery PA sealing ring and a preparation method thereof. The high-thermal-stability alkaline battery PA sealing ring is prepared from the following raw materials in parts by weight: 100 parts of nylon 66, 8 to 16 parts of poly(trimethylene terephthalate), 5 to 10 parts of polypropylene, 10 to 20 parts of compatilizer, 3 to 8 parts of SEBS thermoplastic elastomer, 2 to 6 parts of flame retardant additive and 0.5 to 2 parts of 1,1-ethylidene diacetate. The alkaline battery sealing ring disclosed by the invention has the advantages of electrical insulating property, corrosion resistance, oil resistance, arc resistance, good mechanical property, good gas barrier property and good fatigue durability. By means of blending modification among raw materials, water absorption, thermal stability and processability of the nylon sealing ring are effectively improved; furthermore, the raw material combination has good fluidity in sealing ring forming processing, so that rejected products caused by the phenomena of insufficient injection, insufficient fill and the like in a sealing ring production process are prevented from being generated; the alkaline battery nylon sealing ring has excellent comprehensive performance.

Description

technical field [0001] The invention relates to the technical field of alkaline battery components, in particular to a highly thermally stable alkaline battery PA sealing ring and a preparation method thereof. Background technique [0002] Alkaline storage battery has been paid more and more attention by people because of its high capacity ratio and long life. The internal resistance of the battery is low and the current generated is large. Power tools and other fields have been widely used. The structure of alkaline battery is mainly composed of positive electrode, negative electrode, electrolyte, diaphragm and sealing ring. The battery sealing ring is one of the key parts of the battery. It not only plays the role of isolating the positive and negative electrodes of the battery, but also determines whether the battery is leaking or not. Liquid, so its structural design is becoming more and more complex, and the quality requirements are constantly improving. [0003] Alka...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L77/06C08L67/02C08L23/12C08L53/02C08L51/06C08L51/04C08K5/11C08K5/5399H01M2/08H01M50/186
CPCC08L77/06C08L2205/02C08L2205/035C08L2205/08C08L2201/08C08L2201/14C08K2201/008H01M50/183C08L67/02C08L23/12C08L53/025C08L51/06C08L51/04C08K5/11C08K5/5399Y02E60/10
Inventor 陈峰
Owner 无锡九宇宝新能源科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap