A kind of powder casting coating and its preparation and application method
A casting coating and powder technology, applied in casting molding equipment, coating, casting mold, etc., can solve the problems of short storage period, low bonding strength and high packaging requirements of finished coatings, achieve fast uniformity, and enhance contact opportunities. , easy to disperse effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0020] (1) Weigh 94 kg of 325 mesh zircon powder;
[0021] (2) Prepare 3.3 kg of 200-mesh sodium-based bentonite, 0.95 kg of 200-mesh calcium-based bentonite, 0.72 kg of 200-mesh rosin, 0.28 kg of 200-mesh phenolic resin, and 0.66 kg of 150-mesh low-viscosity polyvinyl butyral (viscosity of 5 seconds) kg, 0.09 kg of 200 mesh high viscosity polyvinyl butyral (viscosity of 200 seconds);
[0022] (3) Put the powdery material weighed in the first two steps into the mixer, start the machine and mix for 20 minutes to get the powdery coating, and pack it out to get the product.
[0023] When in use, take 100 kg of powdered paint and add it to the mixer (blade is rod-shaped), then take 10 kg of alcohol, 0.1 kg of penetrant fatty alcohol polyoxyethylene ether, first add the penetrant into the alcohol and stir well before use, start the mixer, While stirring, add alcohol mixed with penetrating agent until the addition is complete, continue stirring for 5 minutes to obtain a paste, then...
Embodiment 2
[0028] The first step, takes by weighing 93 kilograms of 400 mesh quartz powders;
[0029] The second step is to prepare 4 kg of 270-mesh sodium bentonite, 1.14 kg of 270-mesh calcium-based bentonite, 0.75 kg of 325-mesh rosin, 0.23 kg of 200-mesh phenolic resin, and 180-mesh low-viscosity polyvinyl butyral (viscosity of 8 seconds) 0.7 kg, 200 mesh high viscosity polyvinyl butyral (viscosity of 200 seconds) 0.18 kg;
[0030] Step 3: Add the powdery material weighed in the first two steps into the mixer, turn it on and mix it for 20 minutes to get the powdery coating, and pack it out to get the product;
[0031] When in use, take 100 kg of powdered paint and add it to the mixer (blade is rod-shaped), then take 12 kg of alcohol, and 0.12 kg of penetrant fatty alcohol polyoxyethylene ether, first add the penetrant into the alcohol and stir well before use, start the mixer, While stirring, add alcohol mixed with penetrating agent until the addition is complete, and continue stirr...
Embodiment 3
[0036] The first step, weigh 93 kilograms of 400 mesh white corundum powder;
[0037] The second step is to prepare 4.2 kg of 325-mesh sodium bentonite, 0.93 kg of 325-mesh calcium-based bentonite, 0.79 kg of 325-mesh rosin, 0.24 kg of 325-mesh phenolic resin, and 200-mesh low-viscosity polyvinyl butyral (viscosity of 5 seconds) 0.7 kg, 0.14 kg of 150 mesh high viscosity polyvinyl butyral (viscosity of 250 seconds);
[0038] Step 3: Add the powdery material weighed in the first two steps into the mixer, start the machine and mix for 20 minutes to get the powdery coating, and pack it out to get the product;
[0039] When using, take 100 kg of powdered paint and add it to the blender (the blade is rod-shaped), then take 15 kg of alcohol, and 0.15 kg of penetrant fatty alcohol polyoxyethylene ether, first add the penetrant into the alcohol and stir well before use, start the blender, and While stirring, add alcohol mixed with penetrating agent until the addition is complete, con...
PUM
Property | Measurement | Unit |
---|---|---|
particle size | aaaaa | aaaaa |
particle size | aaaaa | aaaaa |
particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap