High-temperature-resistant composite paper and preparation method thereof

A composite paper and high-temperature-resistant technology, which is applied in the field of paper product processing, can solve the problems of unable to meet production needs and low heat-resistant temperature, and achieve good promotion and application value, low quality loss rate, and reduce import dependence.

Active Publication Date: 2018-01-16
湖北夷盟包装材料有限公司
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the defect that the current domestic high-temperature-resistant paper has a low heat-resistant temperature and cannot meet the production ne

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-temperature-resistant composite paper and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A kind of high temperature resistant composite paper, which has 4 layers from bottom to top, the first layer is a parchment layer with a thickness of 0.3mm, the second layer is an alumina layer with a thickness of 0.1mm, and the third layer is a polycarbonate layer with a thickness of 0.2mm The ester layer and the fourth layer are fiber layers composed of polybenzimidazole fibers and polyarylethersulfone fibers with a thickness of 0.2 mm.

[0030] The preparation method of above-mentioned high temperature resistant composite paper comprises the following steps:

[0031] (1) Pretreatment of the parchment paper layer: spread the parchment paper on the thin steel plate;

[0032](2) Preparation of bauxite layer: drying, calcining, grinding, and crushing bauxite into 100 meshes to obtain bauxite powder, adding adhesive to the bauxite powder, the adhesive is acrylate adhesive, stirring and mixing at 400r / min for 10min , the mass ratio of adhesive to bauxite powder is 20:80, ...

Embodiment 2

[0036] A kind of high temperature resistant composite paper, with 4 layers from bottom to top, the first layer is a parchment layer with a thickness of 0.4mm, the second layer is an alumina layer with a thickness of 0.2mm, and the third layer is a polycarbonate layer with a thickness of 0.3mm The ester layer and the fourth layer are fiber layers composed of polybenzimidazole fibers and polyarylethersulfone fibers with a thickness of 0.3 mm.

[0037] The preparation method of above-mentioned high temperature resistant composite paper comprises the following steps:

[0038] (1) Pretreatment of the parchment paper layer: spread the parchment paper on the thin steel plate;

[0039] (2) Preparation of bauxite layer: drying bauxite, calcining, grinding, crushing bauxite into 120 meshes to obtain bauxite powder, adding adhesive to the bauxite powder, the adhesive is epoxy resin adhesive, stirring and mixing at 450r / min 15min, the mass ratio of the adhesive to the alumina powder is 2...

Embodiment 3

[0043] A kind of high temperature resistant composite paper, which has 4 layers from bottom to top, the first layer is a parchment paper layer with a thickness of 0.4mm, the second layer is an alumina layer with a thickness of 0.2mm, and the third layer is a polycarbonate layer with a thickness of 0.4mm The ester layer and the fourth layer are fiber layers composed of polybenzimidazole fibers and polyarylethersulfone fibers with a thickness of 0.4 mm.

[0044] The preparation method of above-mentioned high temperature resistant composite paper comprises the following steps:

[0045] (1) Pretreatment of the parchment paper layer: spread the parchment paper on the thin steel plate;

[0046] (2) Preparation of bauxite layer: Dry bauxite, calcinate, grind, and crush it into 140 meshes to obtain bauxite powder, add adhesive to the bauxite powder, the adhesive is epoxy resin adhesive and polyurethane adhesive, mixed at 500r / Stir and mix at min speed for 20min. The mass ratio of ad...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention provides high-temperature-resistant composite paper and a preparation method thereof and relates to the technical field of paper product processing. The composite paper comprises four layers from bottom to top, wherein the first layer is a parchment layer, the second layer is an alumina layer, the third layer is a polycarbonate layer, and the fourth layer is a fiber layer formed by mixing polybenzimidazole fiber with polyether sulphone fiber. The prepared high-temperature-resistant composite paper with the four-layer composite structure has good high temperature resistance and mechanical performance, is not prone to damage, has small mass loss rate (less than 1.17%) at the high temperature of 200 DEG C and can still keep higher tensile strength retention rate up to 70% afterworking at 100 DEG C for 6,500 h. The prepared composite paper has good promotion and application value, production of paper for non-traditional machining is further promoted, and import dependence isreduced.

Description

technical field [0001] The invention relates to the technical field of paper product processing, in particular to a high temperature resistant composite paper and a preparation method thereof. Background technique [0002] Paper is an important invention of the working people of the Han nationality in ancient times. The raw materials for papermaking are mainly plant fibers. In addition to the three main components of cellulose, hemicellulose and lignin, there are other components with less content, such as resin, ash, etc., in addition to sodium sulfate, etc. Auxiliary ingredients. Papermaking is one of the "Four Great Inventions" in ancient China. The invention of paper has greatly facilitated the storage and exchange of information, and has epoch-making significance for promoting the development of world civilization. Around the early Western Han Dynasty, people made paper out of hemp and ramie. This early paper was rough and not very suitable for writing. In the East...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D21H27/38B32B9/00B32B9/06B32B27/06B32B27/36B32B27/08B32B27/28
Inventor 陈庆司文彬
Owner 湖北夷盟包装材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap