Method for preparing anion template flocculant TPAS (Tissue Plasmogen Activator)
A flocculant and anion technology, which is applied in the field of preparation of anion template flocculant TPAS, can solve problems such as disordered arrangement, poor flocculation effect, and low proportion of anion monomers, and achieve concentrated distribution, better product properties and stable product properties. Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0022] Example 1:
[0023] The preparation method of the anionic template flocculant TPAS of this embodiment includes the following steps:
[0024] (1) Place acrylamide (309g) and sodium styrene sulfonate (206g) with a mass ratio of 1.5:1 in a reaction flask to prepare an aqueous solution with a mass fraction of 30%, and add anionic monomer to the aqueous solution. The templating agent polypropylene ammonium chloride (93.5g) with a mass ratio of sodium styrene sulfonate of 0.45:1, and the initiator VA044 (0.0515g) accounting for 0.01% of the mass of acrylamide and sodium styrene sulfonate;
[0025] (2) Adjust the pH of the above solution to 5 with hydrochloric acid, and then pour nitrogen into the reaction flask at 20°C for 15 minutes to remove the oxygen in the reaction flask, then seal the mouth of the flask and place it in an ultrasonic reactor at 30~ Ultrasonic reaction at 35°C for 20 minutes. After completion, place the reaction flask in a water bath at 50°C in a constant tempe...
Example Embodiment
[0028] Example 2:
[0029] A preparation method of anionic template flocculant TPAS includes the following steps:
[0030] (1) Place acrylamide (309g) and sodium styrene sulfonate (206g) with a mass ratio of 1.5:1 in a reaction flask to prepare an aqueous solution with a mass fraction of 40%, and add anionic monomer to the aqueous solution. The templating agent polypropylene ammonium chloride (74.8g) with a mass ratio of sodium styrene sulfonate of 0.36:1, and the initiator VA044 (0.103g) which accounts for 0.02% of the mass of acrylamide and sodium styrene sulfonate;
[0031] (2) Adjust the pH of the above solution to 5 with hydrochloric acid, and then pour nitrogen into the reaction flask at 20°C for 15 minutes to remove the oxygen in the reaction flask, then seal the mouth of the flask and place it in an ultrasonic reactor at 30~ Ultrasonic reaction at 35°C for 20 minutes. After completion, place the reaction flask in a water bath at 50°C in a constant temperature water bath for ...
Example Embodiment
[0033] Example 3:
[0034] A preparation method of anionic template flocculant TPAS includes the following steps:
[0035] (1) Place acrylamide (480.0g) and sodium styrene sulfonate (206g) with a mass ratio of 2.33:1 in a reaction flask to prepare an aqueous solution with a mass fraction of 40%. The templating agent polypropylene ammonium chloride (93.5g) with the mass ratio of bulk sodium styrene sulfonate of 0.45:1, and the initiator VA044 (0.206g) which accounts for 0.03% of the mass of acrylamide and sodium styrene sulfonate;
[0036] (2) Adjust the pH of the above solution to 8 with sodium hydroxide, and then pour nitrogen into the reaction flask at 20°C for 15 minutes to remove the oxygen in the reaction flask, then seal the mouth of the flask and place it in the ultrasonic reactor. Ultrasonic reaction at 35~40℃ for 20min. After completion, put the reaction flask in a constant temperature water bath at 55℃ for 10min for maturation. The ultrasonic power is 30W and the ultrasoni...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap