Antistatic PC/ABS (Polycarbonate/Acrylonitrile Butadiene Styrene) compound as well as preparation method and application thereof

An antistatic and compound technology, which is applied in the field of antistatic PC/ABS compound and its preparation, can solve the problems of failure to meet the requirements of the storage battery field, explosion and fire of chemical product warehouses, dust adsorption by materials, etc., and achieve good antistatic effect, Ease of processing and high stability

Inactive Publication Date: 2018-03-23
TIANJIN KINGFA NEW MATERIAL
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] PC/ABS alloy materials are used in the adhesive field, which requires extremely high bond strength and stability; such as PC/ABS alloy materials used in the field of lead-acid batteries, the initial bond strength is required to be ≧76.2Kgf/1.27cm 2 ; while the PC/ABS alloy materials currently on the market, the bond strength is mostly 50-70Kgf/1.27cm 2 ; Can not meet the requirements of the battery field
[0005]

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antistatic PC/ABS (Polycarbonate/Acrylonitrile Butadiene Styrene) compound as well as preparation method and application thereof
  • Antistatic PC/ABS (Polycarbonate/Acrylonitrile Butadiene Styrene) compound as well as preparation method and application thereof
  • Antistatic PC/ABS (Polycarbonate/Acrylonitrile Butadiene Styrene) compound as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0047] Example 1

[0048]Mix 45 parts of PC resin, 40.9 parts of ABS resin, 3 parts of compatibilizer, 1 part of adhesion modifier, 0.1 part of adhesion modification synergist, and 10 parts of antistatic agent in a high-speed mixer according to the ratio for 10 -60 minutes; the above-mentioned mixture is delivered to the twin-screw extruder through a precisely metered feeding device (wherein, the processing conditions for melt extrusion of the twin-screw extruder are as follows: the temperature in the first zone is 190°C, the temperature in the second zone is 210°C, and the temperature in the third zone is 210°C. The temperature of zone 230°C, the temperature of zone 4 is 240°C, the temperature of zone 5 is 240°C, the temperature of zone 6 is 240°C, the temperature of zone 7 is 240°C, the temperature of zone 8 is 240°C, the temperature of zone 9 is 240°C, the temperature of zone 10 is 250°C, the temperature of machine head 260℃; the screw speed is 200-800 rpm, and the aspect r...

Example Embodiment

[0049] Example 2

[0050] Mix 45 parts of PC resin, 36.8 parts of ABS resin, 3 parts of compatibilizer, 5 parts of adhesion modifier, 0.2 parts of adhesion modification synergist, and 10 parts of antistatic agent in a high-speed mixer according to the ratio for 10 -60 minutes; the above-mentioned mixture is delivered to the twin-screw extruder through a precisely metered feeding device (wherein, the processing conditions for melt extrusion of the twin-screw extruder are as follows: the temperature in the first zone is 190°C, the temperature in the second zone is 210°C, and the temperature in the third zone is 210°C. The temperature of zone 230°C, the temperature of zone 4 is 240°C, the temperature of zone 5 is 240°C, the temperature of zone 6 is 240°C, the temperature of zone 7 is 240°C, the temperature of zone 8 is 240°C, the temperature of zone 9 is 240°C, the temperature of zone 10 is 250°C, the temperature of machine head 260℃; the screw speed is 200-800 rpm, and the aspec...

Example Embodiment

[0051] Example 3

[0052] Mix 45 parts of PC resin, 26.5 parts of ABS resin, 3 parts of compatibilizer, 10 parts of adhesion modifier, 0.5 parts of adhesion modification synergist, and 10 parts of antistatic agent in a high-speed mixer according to the ratio for 10 -60 minutes; the above-mentioned mixture is delivered to the twin-screw extruder through a precisely metered feeding device (wherein, the processing conditions for melt extrusion of the twin-screw extruder are as follows: the temperature in the first zone is 190°C, the temperature in the second zone is 210°C, and the temperature in the third zone is 210°C. The temperature of zone 230°C, the temperature of zone 4 is 240°C, the temperature of zone 5 is 240°C, the temperature of zone 6 is 240°C, the temperature of zone 7 is 240°C, the temperature of zone 8 is 240°C, the temperature of zone 9 is 240°C, the temperature of zone 10 is 250°C, the temperature of machine head 260℃; the screw speed is 200-800 rpm, and the aspe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides an antistatic PC/ABS (Polycarbonate/Acrylonitrile Butadiene Styrene) compound as well as a preparation method and application thereof. The antistatic PC/ABS compound is preparedfrom the following components in parts by weight: 10 to 70 parts of PC resin, 20 to 80 parts of ABS resin, 2 to 10 parts of a compatilizer, 1 to 10 parts of a bonding modifier, 0.1 to 0.5 part of a bonding modification synergist, 10 to 15 parts of an antistatic agent and 0.1 to 3 parts of an auxiliary agent. The antistatic PC/ABS compound provided by the invention has excellent mechanical properties, excellent bonding strength and high stability.

Description

technical field [0001] The invention belongs to the field of polymer materials, and in particular relates to an antistatic PC / ABS compound, a preparation method and application thereof. Background technique [0002] PC / ABS alloy is an alloy material synthesized by PC (polycarbonate) and ABS (acrylonitrile-butadiene-styrene copolymer) in a certain proportion. Polycarbonate (PC) has the advantages of high impact strength, creep resistance, good dimensional stability, heat resistance, transparency, and excellent dielectric properties, but it also has poor processing fluidity, prone to stress cracking, sensitive to notches, and Disadvantages such as poor abrasiveness; acrylonitrile / butadiene / styrene copolymer (ABS) has good chemical resistance and molding processability, but its heat resistance and weather resistance are relatively poor. The PC / ABS alloy obtained by blending and modifying the two can complement each other in performance. Not only the heat resistance, impact str...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L69/00C08L55/02C08L71/02C08L51/00B29C47/92B29C45/78B29C45/77B29C48/92
CPCC08L69/00B29C45/77B29C45/78B29C48/92B29C2948/9258B29C2948/92704C08L2201/04C08L2205/035C08L55/02C08L71/02C08L51/00
Inventor 肖华明汪炉林宋晓辉陶四平宋晓东
Owner TIANJIN KINGFA NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap