Method for synthesizing grafted lysine viscose fibers

A viscose fiber and lysine technology, applied in plant fiber, fiber treatment, biochemical fiber treatment, etc., can solve the poor performance of acrylic fiber dyeing, washing, skin affinity, etc., cannot use physical and chemical properties, and cannot be reused and other issues, to achieve the effect of low production cost, huge social value and economic benefits, and easy operation

Inactive Publication Date: 2018-03-23
CHONGQING UNIV
View PDF6 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The deficiency of this method is: 1. the principle of this method is the reaction of cyano group and amino group, can only take place on the acrylic fiber, and can not be used on the fiber with better physical and chemical properties such as cotton fiber, viscose fiber
The dyeing, washi

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0023] Example 1

[0024] A method for synthesizing grafted lysine viscose fiber, the specific process steps are as follows:

[0025] (1) Preparation of purified viscose fiber

[0026] According to the volume ratio of the mass of commercially available viscose fiber to the sodium hydroxide solution with a concentration of 0.5% by mass, the volume ratio is 1:30 (kg / L), and the commercially available viscose fiber is dispersed at a concentration of 0.5% by mass. In the sodium hydroxide solution, the temperature was raised to 80°C, treated for 0.5h and placed in a three-foot centrifuge, centrifuged at a speed of 2000r / min for 10min, and the centrifugal fluid and the centrifuged viscose fiber were collected separately. The collected centrifugal viscose fibers were washed with purified water at a centrifugal speed of 2000 r / min until the pH of the washing centrifugal liquid was 7.0. Separately collect and wash centrifugal viscose fibers and washing centrifugal fluid. For the collected w...

Example Embodiment

[0035] Example 2

[0036] A method for synthesizing grafted lysine viscose fiber, the specific process steps are as follows:

[0037] (1) Preparation of purified viscose fiber

[0038] According to the ratio of 1:45 (kg / L) between the mass of commercially available viscose fiber and the sodium hydroxide solution with a concentration of 0.8% by mass, the commercially available viscose fiber was dispersed at a concentration of 0.8% by mass. In the sodium hydroxide solution, the temperature was raised to 85°C, treated for 1.0h, placed in a three-foot centrifuge, centrifuged at a speed of 3000r / min for 15min, and collected the centrifugal fluid and centrifuged viscose fibers. The collected centrifugal viscose fibers were washed with purified water at a centrifugal speed of 3000 r / min until the pH of the washing centrifugal liquid was 7.5. Separately collect and wash centrifugal viscose fibers and washing centrifugal fluid. For the collected washing centrifugal viscose fibers, purified ...

Example Embodiment

[0047] Example 3

[0048] A method for synthesizing grafted lysine viscose fiber, the specific process steps are as follows:

[0049] (1) Preparation of purified viscose fiber

[0050] According to the ratio of the mass of commercially available viscose fiber to the sodium hydroxide solution with a mass percentage of 1.0% by volume ratio of 1:60 (kg / L), the commercially available viscose fiber was dispersed at a mass percentage of 1.0%. In the sodium hydroxide solution, the temperature was raised to 90°C, treated for 1.5h, placed in a three-foot centrifuge, centrifuged at a speed of 4000r / min for 20min, and the centrifugal fluid and the centrifuged viscose fiber were collected separately. The collected centrifugal viscose fibers were washed with purified water at a centrifugal speed of 4000 r / min until the pH of the washing centrifugal liquid was 8.0. Separately collect and wash centrifugal viscose fibers and washing centrifugal fluid. For the collected washing centrifugal viscose ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a method for synthesizing grafted lysine viscose fibers and belongs to the technical field of modification of fiber materials. According to the method, commercially available viscose fibers and lysine are taken as raw materials, and the grafted lysine viscose fibers with good skin-friendly property, antibacterial property and dyeing property can be prepared stably through steps as follows: preparation of purified viscose fibers, preparation of carboxylated viscose fibers, preparation of ethylene glycol non-aqueous reaction media, preparation of the grafted lysine viscosefibers and preparation of purified ethylene glycol. The carboxylated viscose fibers and the grafted lysine viscose fibers are produced under catalysis of glucose oxidase and protease in sequence, thegrafted lysine viscose fibers are prepared in the ethylene glycol non-aqueous reaction media, reaction conditions are mild, reaction specificity and reaction efficiency are high, no by-products or three wastes are produced, and the method is a typical green production technology; the grafted lysine viscose fibers synthesized with the method are covered with amino acid, can be widely applied to the fields such as textiles, clothes, food and the like and have great social value and economic benefits.

Description

1. Technical field [0001] The invention belongs to the technical field of fiber material modification, and in particular relates to a method for synthesizing grafted lysine viscose fiber. 2. Background technology [0002] Rubber fiber, commonly known as rayon, has good water absorption, warmth, breathability, and soft touch, and is widely used in the textile industry. However, viscose fibers also have defects such as easy elongation, easy deformation, poor elasticity, high shrinkage rate, and low skin affinity. Therefore, improving the physical, chemical and clothing properties of the fiber has important scientific value, application prospects and market potential. [0003] The main component of human skin is collagen. Collagen is a kind of biological polymer substance, widely present in human skin and other organs, and has the functions of moisturizing skin, delaying aging, beautifying, and reducing wrinkles. The basic structural unit of collagen is 19 kinds of amino acid...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06M13/342D06M16/00D06M13/148D06M101/06
CPCD06M13/148D06M13/342D06M16/003D06M2101/06
Inventor 尹思力江文杨洋倪科张海龙朱云阳凌梦晨周小华
Owner CHONGQING UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap