Nickel chrome wire

A technology of nickel-chromium wire and passivation treatment, which is applied in the coating process of metal materials, etc., can solve the problems of unsatisfactory surface finish and achieve excellent anti-oxidation and good surface finish

Inactive Publication Date: 2018-03-27
CHANGSHU MEILI ALLOY MATERIAL CO LTD
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The oxidation resistance, abrasion resistance, corrosion resistance, heat resistance, cold resistance and

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0024] Example 1

[0025] The nickel-chromium wire has undergone passivation treatment, and the passivation treatment includes the following steps:

[0026] 1) Combine 1 to 2 parts by weight of alkylamine oxide polyoxyethylene ether, 0.7 parts by weight of disodium hydrogen phosphate, 3.2 parts by weight of tannic acid, 1.1 parts by weight of sodium persulfate, and 0.8 parts by weight of dodecyl trimethyl chloride Ammonium sulfide is sequentially poured into 25 parts by weight of deionized water and stirred evenly;

[0027] 2) Put in 1.3 parts by weight of benzotriazole, 4.2 parts by weight of polyacrylic acid, 1.3 parts by weight of isotridecyl alcohol polyoxyethylene ether phosphate, 0.3 parts by weight of zinc dihydrogen phosphate, and 0.7 parts by weight of dialkyl two Zinc thiophosphate, continue to stir until fully mixed and uniform, to obtain passivation treatment liquid;

[0028] 3) Put the nickel-chromium wire into the passivation treatment solution for passivation treatment...

Example Embodiment

[0029] Example 2

[0030] Nickel-chromium wire, which has been passivated, and the passivation includes the following steps:

[0031] 1) Combine 1 part by weight of alkylamine oxide polyoxyethylene ether, 0.7 part by weight of disodium hydrogen phosphate, 3.2 parts by weight of tannic acid, 1.1 parts by weight of sodium persulfate, and 0.8 parts by weight of dodecyltrimethylammonium chloride Put 25 parts by weight of deionized water in sequence and stir evenly;

[0032] 2) Put in 1.3 parts by weight of benzotriazole, 4.2 parts by weight of polyacrylic acid, 1.3 parts by weight of isotridecyl alcohol polyoxyethylene ether phosphate, 0.3 parts by weight of zinc dihydrogen phosphate, and 0.7 parts by weight of dialkyl Zinc thiophosphate, continue to stir until fully mixed and uniform, to obtain passivation treatment liquid;

[0033] 3) Put the nickel-chromium wire into the passivation treatment solution for passivation treatment, the treatment temperature is 50℃, and the treatment time ...

Example Embodiment

[0034] Example 3

[0035] The nickel-chromium wire has undergone passivation treatment, and the passivation treatment includes the following steps:

[0036] 1) Combine 2 parts by weight of alkylamine oxide polyoxyethylene ether, 0.7 parts by weight of disodium hydrogen phosphate, 3.2 parts by weight of tannic acid, 1.1 parts by weight of sodium persulfate, and 0.8 parts by weight of dodecyltrimethylammonium chloride Put 25 parts by weight of deionized water in sequence and stir evenly;

[0037] 2) Put in 1.3 parts by weight of benzotriazole, 4.2 parts by weight of polyacrylic acid, 1.3 parts by weight of isotridecyl alcohol polyoxyethylene ether phosphate, 0.3 parts by weight of zinc dihydrogen phosphate, and 0.7 parts by weight of dialkyl Zinc thiophosphate, continue to stir until fully mixed and uniform, to obtain passivation treatment liquid;

[0038] 3) Put the nickel-chromium wire into the passivation treatment solution for passivation treatment, the treatment temperature is 50℃...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a nickel chrome wire which is passivated. The passivating treatment comprises the following steps: (1) feeding 1 to 2 weight parts of alkyl polyoxyethylene oxide, 0.7 weight part of disodium hydrogen phosphate, 3.2 weight parts of tannic acid, 1.1 weight parts of sodium persulfate and 0.8 weight part of lauryl trimethyl ammonium chloride into 25 weight parts of deionized water in sequence for uniform stirring; (2) then feeding 1.3 weight parts of benzotriazole, 4.2 weight parts of polyacrylic acid, 1.3 weight parts of isomerous tridecanol polyoxyethylene ether phosphate, 0.3 weight part of zinc dihydrogen phosphate and 0.7 weight part of zinc dialkyl dithiophosphate in sequence, continuously stirring the components till the components are fully and uniformly mixed,thus preparing a passivating treatment solution; and (3) putting the nickel chrome wire into the passivating treatment solution for passivating treatment at treatment temperature of 50 DEG C for 30 s,taking out the nickel chrome wire, cleaning the nickel chrome wire with pure water, and drying the nickel chrome wire. The nickel chrome wire disclosed by the invention is high in performance after being subjected to the passivating treatment, and is high in surface smoothness.

Description

technical field [0001] The invention relates to a nickel-chromium wire. Background technique [0002] The oxidation resistance, abrasion resistance, corrosion resistance, heat resistance, cold resistance and weather resistance of the existing nickel-chromium wire need to be improved, and the surface finish is not ideal. Contents of the invention [0003] The object of the present invention is to provide a kind of nickel-chromium wire, which forms a uniform passivation protective film on the surface after passivation treatment, has excellent oxidation resistance, abrasion resistance, corrosion resistance, heat resistance, cold resistance, weather resistance, and the surface Good finish. [0004] In order to achieve the above object, the technical solution of the present invention is to design a kind of nickel-chromium wire, which is through passivation treatment, and said passivation treatment comprises the following steps: [0005] 1) Add 1 to 2 parts by weight of oxidiz...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23C22/54C23C22/06
CPCC23C22/06C23C22/54
Inventor 陈俊达
Owner CHANGSHU MEILI ALLOY MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products