Lignin raw lacquer compound coating

A composite coating and lignin technology, which is applied in the field of lignin raw lacquer composite coatings, can solve the problems of long drying time, high price, and inconvenient construction, and achieve the effects of low cost, improved adhesion, and improved hardness

Inactive Publication Date: 2018-04-24
ZHONGSHAN DEGAOXING INTPROP CENT LLP
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The object of the present invention is to provide a kind of lignin raw lacquer composite coating, to solve the problems of the existing raw lacquer composite coating proposed in the above-mentioned background technology that the price is expensive, the adhesion is poor, the drying time is long, the viscosity is large, and it is not convenient for construction.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] At a temperature of 32 degrees Celsius and a humidity of 85%, pour raw lacquer and drying vegetable oil into a mixing tank, stir and disperse for 2 hours at 110 rpm, and then pour in lignin, phenolic compounds, Chlorine salt, graphite powder, polyhydroxy acrylic resin and additives are poured in, and ultrasonic dispersion is used for 50 minutes under stirring.

[0017] In this example, lignin: 19 parts; phenolic compound: 9 parts, the phenolic compound is tannic acid; chlorine salt: 1 part, the chlorine salt is ferric chloride, antimony chloride and chlorinated One of aluminum; graphite powder: 3 parts; dry vegetable oil: 6 parts, the dry vegetable oil is raw tung oil; polyhydroxy acrylic resin: 6 parts, the hydroxyl value in the polyhydroxy acrylic resin is 70- 80㎎KOH / g; raw lacquer: 51 parts, the composition of the raw lacquer includes urushiol, water, nitride and gum, the content of urushiol is greater than 65%; auxiliary agent: 11 parts.

Embodiment 2

[0019] At a temperature of 28 degrees Celsius and a humidity of 75%, pour raw lacquer and drying vegetable oil into a mixing tank, stir and disperse for 1 hour at 90 rpm, and then pour in lignin, phenolic compounds, Chlorine salt, graphite powder, polyhydroxy acrylic resin and additives are poured in, and ultrasonic dispersion is used for 30 minutes under stirring.

[0020] In this example, lignin: 15 parts; phenolic compound: 12 parts, the phenolic compound is tannic acid; chloride salt: 0.8 part, the chloride salt is iron chloride, antimony chloride and chloride One of aluminum; graphite powder: 1 part; dry vegetable oil: 8 parts, the dry vegetable oil is raw tung oil; polyhydroxy acrylic resin: 4 parts, the hydroxyl value in the polyhydroxy acrylic resin is 70- 80㎎KOH / g; raw lacquer: 59 parts, the composition of the raw lacquer includes urushiol, water, nitride and gum, the content of urushiol is greater than 65%; auxiliary agent: 3 parts.

Embodiment 3

[0022] At a temperature of 30 degrees Celsius and a humidity of 80%, pour raw lacquer and drying vegetable oil into a mixing tank, stir and disperse at 100 rpm for 1.5 hours, and then pour in lignin, phenolic compounds, Chlorine salt, graphite powder, polyhydroxy acrylic resin and additives are poured in, and ultrasonic dispersion is used for 40 minutes under stirring.

[0023] In this example, lignin: 17.5 parts; phenolic compound: 10 parts, the phenolic compound is tannic acid; chloride salt: 0.9 part, the chloride salt is iron chloride, antimony chloride and chloride One of aluminum; graphite powder: 2 parts; dry vegetable oil: 7 parts, the dry vegetable oil is raw tung oil; polyhydroxy acrylic resin: 5 parts, the hydroxyl value in the polyhydroxy acrylic resin is 70- 80㎎KOH / g; raw lacquer: 55 parts, the composition of the raw lacquer includes urushiol, water, nitride and gum, the content of urushiol is greater than 65%; auxiliary agent: 9 parts.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hydroxyl valueaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of coatings, and particularly discloses a lignin raw lacquer compound coating. The lignin raw lacquer compound coating is prepared from 15-20 parts of lignin, 8-12 parts of phennolic compound, 0.8-1 part of chlorine salt, 1-3 parts of graphite powder, 6-8 parts of dried vegetable oil, 4-6 parts of polyhydroxy acrylic resin, 50-60 parts of raw lacquer and 3-15 parts of auxiliaries. The lignin raw lacquer compound coating can greatly improve the adhesive force of the raw lacquer, the raw lacquer can become an antistatic coating, the application rangeof the raw lacquer compound coating is expanded, and the mechanical performance of the raw lacquer compound coating like the rigidity, flexibility and the shock resistance is improved; meanwhile, thedrying time is shortened, the function of resisting ultraviolet light is improved, the cost is low, and manufacturing is facilitated.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a lignin raw lacquer composite coating. Background technique [0002] Raw lacquer, commonly known as "earth lacquer", also known as "national lacquer" or "big lacquer", is a milky white pure natural liquid paint harvested from lacquer trees. It gradually turns brown when exposed to air, and the surface dries and hardens in about 4 hours. to form a paint film. The economic value of raw lacquer is very high. It has the characteristics of corrosion resistance, wear resistance, acid resistance, solvent resistance, heat resistance, good water insulation and insulation, and luster. High quality coating for furniture etc. It is also one of the important materials traditionally exported by China, and it is famous in the world for its large quantity and good quality. In view of the defects of raw lacquer performance, it is necessary to modify it, but the existing raw lacquer composite...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D193/00C09D197/00C09D191/00C09D133/04C09D5/24
CPCC09D193/00C08L2201/04C08L2201/08C08L2205/035C09D5/24C08L97/005C08L91/00C08L33/04C08K3/04
Inventor 谢小坚梁荣强
Owner ZHONGSHAN DEGAOXING INTPROP CENT LLP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com