Hydrocolloid dressing with strong antibacterial capacity and preparation method of hydrocolloid dressing

A hydrocolloid and capable technology, applied in the field of medical supplies, can solve the problems of unsatisfactory effect, weak self-adhesion and elasticity, poor antibacterial performance, etc., to reduce the risk of biological safety, promote healing, and reduce the effect of adding concentration.

Inactive Publication Date: 2018-05-04
张立栋
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Due to the shortcomings of the existing hydrocolloid dressings such as poor antibacterial performance, self-adhesiveness, and weak elastic

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A hydrocolloid dressing with strong antibacterial ability, its components are calculated by weight: 35 parts of carboxymethyl cellulose sodium, 40 parts of carboxymethyl chitosan, 20 parts of polyurethane thermoplastic elastomer, 20 parts of sodium alginate, 5 parts of adhesive resin, 5 parts of plasticizer, 10 parts of gelatin, 3 parts of alkyl starch ester, 4 parts of polyisobutylene, 0.5 part of antioxidant, 2.5 parts of bacteriostatic agent, 0.5 part of synergistic bacteriostatic agent.

[0025] A kind of hydrocolloid dressing with strong antibacterial ability, its preparation method comprises the following steps:

[0026] a. The sodium carboxymethyl cellulose, sodium alginate powder and antibacterial agent are pulverized and fully mixed to obtain the mixed component A;

[0027] b. Add polyurethane thermoplastic elastomers, tackifying resins, plasticizers, gelatin, alkyl starch esters, polyisobutylene and antioxidants into the vacuum kneader in sequence, and mix for...

Embodiment 2

[0038] A hydrocolloid dressing with strong antibacterial ability, its components are calculated by weight: 40 parts of carboxymethyl cellulose sodium, 30 parts of carboxymethyl chitosan, 25 parts of polyurethane thermoplastic elastomer, 10 parts of sodium alginate, 10 parts of adhesive resin, 1 part of plasticizer, 12 parts of gelatin, 5 parts of alkyl starch ester, 1 part of polyisobutylene, 1.2 parts of antioxidant, 0.5 part of bacteriostatic agent, 1 part of synergistic bacteriostatic agent.

[0039] A kind of hydrocolloid dressing with strong antibacterial ability, its preparation method comprises the following steps:

[0040] a. The sodium carboxymethyl cellulose, sodium alginate powder and antibacterial agent are pulverized and fully mixed to obtain the mixed component A;

[0041] b. Add polyurethane thermoplastic elastomers, tackifying resins, plasticizers, gelatin, alkyl starch esters, polyisobutylene and antioxidants into the vacuum kneader in sequence, and mix for 50...

Embodiment 3

[0052]A hydrocolloid dressing with strong antibacterial ability, its components are calculated by weight: 50 parts of carboxymethyl cellulose sodium, 50 parts of carboxymethyl chitosan, 30 parts of polyurethane thermoplastic elastomer, 35 parts of sodium alginate, 15 parts of adhesive resin, 10 parts of plasticizer, 14 parts of gelatin, 6 parts of alkyl starch ester, 7 parts of polyisobutylene, 2.2 parts of antioxidant, 4.5 parts of bacteriostatic agent, 2 parts of synergistic bacteriostatic agent.

[0053] A kind of hydrocolloid dressing with strong antibacterial ability, its preparation method comprises the following steps:

[0054] a. The sodium carboxymethyl cellulose, sodium alginate powder and antibacterial agent are pulverized and fully mixed to obtain the mixed component A;

[0055] b. Add polyurethane thermoplastic elastomer, tackifying resin, plasticizer, gelatin, alkyl starch ester, polyisobutylene and antioxidant into the vacuum kneader in turn, and mix for 100min ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Stay stickyaaaaaaaaaa
Peel strengthaaaaaaaaaa
Stay stickyaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of medical supplies, and in particular relates to a hydrocolloid dressing with strong antibacterial capacity and a preparation method of the hydrocolloid dressing. The hydrocolloid dressing is prepared from the following raw materials in parts by weight: 35-55 parts of sodium carboxymethyl cellulose, 30-50 parts of carboxymethyl chitosan, 20-40 parts ofpolyurethane thermoplastic elastomers, 10-35 parts of sodium alginate, 5-20 parts of tackifying resin, 1-10 parts of a plasticizer, 10-15 parts of gelatin, 3-8 parts of alkyl starch ester, 1-7 partsof polyisobutene, 0.5-3.2 parts of an antioxidant, 0.5-4.5 parts of a fungicide, and 0.5-2.5 parts of a synergistic fungicide. For the prepared hydrocolloid dressing, the potential biosecurity risk ofthe product is reduced, the antibacterial rate of the product is improved, a moist heal environment is provided for the wound, meanwhile, the heal of the surface of the wound is also promoted, the hydrocolloid dressing provided by the invention has good autohension and elasticity, and can be softly applied to the surface of the skin, and a user feels comfortable.

Description

technical field [0001] The invention relates to the technical field of medical supplies, in particular to a hydrocolloid dressing with strong antibacterial ability and a preparation method thereof. Background technique [0002] Hydrocolloid dressing is a medical dressing made by blending water-absorbing polymer particles with hot-melt pressure-sensitive adhesive. This material combines the adhesive properties of rubber materials and the water-absorbing properties of water-absorbing polymer materials. Rubber The base material provides viscosity, which enables the dressing to stick to the wound surface, and the hydrocolloid particles dispersed in it swell after washing, providing a moist sealing environment for the wound and promoting wound healing. A moist environment plays an important role in wound healing The promotion effect brings great convenience to wound care. However, chronic wounds are skin tissue damages caused by external force factors such as surgery and heat. O...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): A61L15/46A61L15/40A61L15/26A61L15/28A61L15/42
CPCA61L15/46A61L15/26A61L15/28A61L15/40A61L15/42A61L2300/30A61L2300/404C08L75/04C08L5/08
Inventor 张立栋
Owner 张立栋
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap