A stainless steel wire, corrosion-resistant technology, applied in the field of metallurgy, can solve the problems of poor resistance to strong acid and strong alkali, poor corrosion resistance, low strength, etc., to increase corrosion resistance and corrosion resistance, high corrosion resistance, and prolong service life Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0018] The composition of stainless steel wire: contains 0.01-0.03% carbon, 18-20% chromium, 4-8% nickel, 0.1-0.12% copper, 0.4-0.5% phosphorus, and the rest is iron.
[0019] According to the above ratio, carry out raw material proportioning, mixing, primary refining and refining.
[0020] The refined stainless steel billet is rolled into a stainless steel wire rod with a diameter of 5.5 mm on a stainless steel high-speed wire rod rolling mill.
[0021] On the laying machine, the stainless steel wire rod is rolled into a steel coil with an inner diameter of 1000 mm.
[0022] The spun stainless steel wire coil is cooled to room temperature on the cooling roller table during transportation.
[0023] The stainless steel wire obtained above was put into a heat treatment furnace for heat treatment at a heat treatment temperature of 1100° C., kept for 1.5 hours, and then water-cooled after being taken out of the furnace.
[0024] Pickling the heat-treated stainless steel wire wit...
Embodiment 2
[0027] The composition of stainless steel wire: contains 0.01-0.03% carbon, 18-20% chromium, 4-8% nickel, 0.1-0.12% copper, 0.4-0.5% phosphorus, and the rest is iron.
[0028] According to the above ratio, carry out raw material proportioning, mixing, primary refining and refining.
[0029] The refined stainless steel billet is rolled into a stainless steel wire rod with a diameter of 6.0 mm on a stainless steel high-speed wire rod rolling mill.
[0030] On the laying machine, the stainless steel wire rod is rolled into a steel coil with an inner diameter of 1100mm.
[0031] The spun stainless steel wire coil is cooled to room temperature on the cooling roller table during transportation.
[0032] The stainless steel wire obtained above was put into a heat treatment furnace for heat treatment at a heat treatment temperature of 1100° C., kept for 1.5 hours, and then water-cooled after being taken out of the furnace.
[0033] Pickling the heat-treated stainless steel wire with...
Embodiment 3
[0036] The composition of stainless steel wire: contains carbon 0.01-0.03%, chromium 18-20%, nickel 4-8%, copper 0.1-0.12%, phosphorus 0.4-0.5%, niobium 0.3-0.8%, and the rest is iron.
[0037] According to the above ratio, carry out raw material proportioning, mixing, primary refining and refining.
[0038] The refined stainless steel billet is rolled into a stainless steel wire rod with a diameter of 5.4 mm on a stainless steel high-speed wire rod rolling mill.
[0039] On the laying machine, the stainless steel wire rod is rolled into a steel coil with an inner diameter of 1000 mm.
[0040] The spun stainless steel wire coil is cooled to room temperature on the cooling roller table during transportation.
[0041] The stainless steel wire obtained above was put into a heat treatment furnace for heat treatment at a heat treatment temperature of 1100° C., kept for 1.5 hours, and then water-cooled after being taken out of the furnace.
[0042] Pickling the heat-treated stainl...
PUM
| Property | Measurement | Unit |
|---|---|---|
| diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
Login to View More