Cable sleeve pipe

A technology of cable casing and chloroether resin, which is applied in the direction of plastic/resin/wax insulators, organic insulators, etc., can solve the problems of poor tensile and flexural strength, insufficient corrosion resistance, and flammability, and achieve good acid and alkali resistance Salt corrosion, low cost and long service life

Inactive Publication Date: 2018-06-12
苏永义
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to overcome the defects of insufficient corrosion resistance, poor tensile and bending strength, and flammability of the existing cable sleeves in the prior art, the present invention discloses a new type of cable sleeve, which has better performance , can be widely used in industrial production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A corrosion-resistant cable sleeve applied to the electric power industry, which includes the following raw materials in parts by weight:

[0028] Polyethylene resin 40 parts

[0029] Chlorine ether resin 30 parts

[0030] 5 parts phenolic resin

[0031] 3 parts chlorinated paraffin

[0032] 1 part borax

[0033] 1 part meerschaum

[0034] 0.6 parts of glass fiber

[0035] Magnesium hydroxide 0.5 parts

[0036] Palygorskite 0.5 parts

[0037] Zinc borate 0.3 parts

[0038] 0.2 parts of sodium dodecylsulfonate;

[0039] The preparation method of the above-mentioned cable casing comprises the following steps:

[0040] Step 1): Put the sepiolite and palygorskite into a pulverizer for crushing, then mix them with borax, and then put them into a ball mill for ball milling to a powder with a particle size of 100-200 mesh;

[0041] Step 2): Mix polypropylene resin and chloroether resin at 50°C for 5 minutes, then raise the temperature to 70°C, add chlorinated paraffi...

Embodiment 2

[0045] A corrosion-resistant cable sleeve applied to the electric power industry, which includes the following raw materials in parts by weight:

[0046] Polyethylene resin 70 parts

[0047] Chlorine ether resin 50 parts

[0048] 7 parts phenolic resin

[0049] Chlorinated paraffin 5 parts

[0050] Borax 2 parts

[0051] 2 parts meerschaum

[0052] 0.9 parts of glass fiber

[0053] Magnesium hydroxide 0.7 parts

[0054] Palygorskite 0.7 parts

[0055] Zinc borate 0.5 parts

[0056] 0.4 parts of sodium dodecylsulfonate;

[0057] The preparation method of the above-mentioned cable casing comprises the following steps:

[0058] Step 1): Put the sepiolite and palygorskite into a pulverizer for crushing, then mix them with borax, and then put them into a ball mill for ball milling to a powder with a particle size of 100-200 mesh;

[0059] Step 2): Mix polypropylene resin and chloroether resin at 50°C for 5 minutes, then raise the temperature to 70°C, add chlorinated paraf...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of an electric material and discloses a cable sleeve pipe. The cable sleeve pipe is prepared from the following raw materials: polyethylene resin, chloric ether resin, phenolic resin, chlorinated paraffin, borax, sepiolite, glass fiber, magnesium hydroxide, palygorskite, zinc borate and sodium dodecyl sulfate. The cable sleeve pipe provided by the invention has high acid, alkali and salt resistance and high high-temperature and cold resistance.

Description

technical field [0001] The invention belongs to the field of electric power materials, and specifically discloses a cable casing. Background technique [0002] Cable sleeve is a heat-shrinkable sleeve commonly used for insulation protection on cables. The main material of this type of product is PE. After two processes of irradiation cross-linking and heating expansion, it has the function of heat shrinkage, and the shrinkage ratio is about 3:1. , ranging from 50-350mm in diameter, can be used as heat-shrinkable inner sheath, outer sheath, and outer insulating and waterproof cable sleeve in cable accessories. The main purpose of the cable sleeve is to be used as a cable sheath to protect the cable from external damage and ensure the safety of electricity. The power cable sleeve is divided into buried type and ground type. In the last century, cable sleeves made of metal materials were generally used to protect cables; with the continuous development of the material field,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L27/06C08L61/06C08K13/04C08K3/34C08K3/38C08K7/14C08K3/22H01B3/44
CPCC08K2201/014C08L23/06C08L27/06C08L2201/08C08L2203/20C08L2205/035H01B3/441C08L61/06C08K13/04C08K3/346C08K2003/387C08K7/14C08K2003/2224
Inventor 苏玉祥陈华丰王东旭崔淑恒
Owner 苏永义
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com