A kind of healthy functional interior wall inorganic diatom mud coating and preparation method thereof

A diatom mud coating, functional technology, applied in the field of architectural interior wall coatings, can solve laborious and time-consuming problems, and achieve the effect of enhancing constructability, improving adhesion, and smooth coating surface

Active Publication Date: 2020-09-29
南京安德丽节能建材有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] It can be seen that those skilled in the art are limited to the research on multi-functional putty powder. After using the putty layer as a primer, they still need to go through three processes of latex paint and polishing, which are time-consuming and labor-intensive.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0051] The preparation method of silicon-containing binder comprises the following steps:

[0052] (1) Preparation of rosin resin: first, heat 40 parts of water to boiling state, put 40 parts of paraffin into it and stir to dissolve the paraffin; then add 60 parts of rosin resin, and carry out saponification reaction under stirring at 200r / min; Add 1 part of turpentine and 1 part of oxalic acid, and increase the speed to 400r / min to continue stirring to obtain a uniform mixture; finally, heat the mixture for 60 minutes to form pine wax resin;

[0053] (2) Emulsification: Stir 70 parts of acrylic emulsion, 8 parts of nano silicon dioxide, 5 parts of pine wax resin and 1 part of emulsifier.

[0054] The preparation method of alkali resistance agent comprises the following steps:

[0055] (1) Put 15 parts of polyborosiloxane in a crucible and heat it in a high temperature environment of 180°C until the polyborosiloxane is in a molten state;

[0056] (2) Add 50 parts of cement c...

Embodiment 1

[0068] A method for preparing a healthy functional interior wall inorganic diatom mud coating, comprising the steps of:

[0069] (1) Ingredients: Weigh 25 parts of plant rubber powder composition, 330 parts of Portland cement, 650 parts of quartz sand, 2 parts of iron oxide red, 10 parts of 3mm polypropylene short fiber, and 8 parts of alkali inhibitor;

[0070] (2) Add Portland cement, quartz sand, vegetable rubber powder composition and alkali inhibitor to the ball mill for full stirring, and adjust the speed to 300r / min;

[0071] (3) Increase the rotational speed to 450r / min, continue to add iron oxide red and polypropylene short fibers for full grinding.

Embodiment 2

[0073] A method for preparing a healthy functional interior wall inorganic diatom mud coating, comprising the steps of:

[0074] (1) Ingredients: Weigh 27 parts of plant rubber powder composition, 335 parts of Portland cement, 655 parts of quartz sand, 4 parts of iron oxide red, 15 parts of 3mm polypropylene short fiber, and 8 parts of alkali inhibitor;

[0075] (2) Add Portland cement, quartz sand, vegetable rubber powder composition and alkali inhibitor to the ball mill for full stirring, and adjust the speed to 300r / min;

[0076] (3) Increase the rotational speed to 450r / min, continue to add iron oxide red and polypropylene short fibers for full grinding.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
whitenessaaaaaaaaaa
viscosityaaaaaaaaaa
whitenessaaaaaaaaaa
Login to View More

Abstract

The invention discloses healthy and functional diatom ooze coating for an interior wall and a preparation method of the healthy and functional diatom ooze coating, applies to the field of interior wall decoration and aims at solving the problem that operation such as polishing is further needed after puttying because the interior wall coating is generally applied to a putty layer in the prior art.The interior wall coating has a function of integrating three procedures into one. The technical scheme of the coating is characterized in that the coating is prepared from components in parts by weight as follows: 25-35 parts of vegetable gum powder composition, 330-350 parts of Portland cement, 650-670 parts of quartz sand, 2-10 parts of iron oxide red, 10-30 parts of polypropylene staple fibers and 8-12 parts of an alkali resisting agent. The coating has the advantages of labor saving, time saving and money saving, more easiness is provided for decoration again, and scrape coating can be performed directly without bottom shoveling-off or coating brushing.

Description

technical field [0001] The invention relates to a building interior wall coating, in particular to a healthy functional interior wall inorganic diatom mud coating and a preparation method thereof. Background technique [0002] In order to meet the living needs and aesthetic requirements of people in modern society, more and more families choose to decorate the indoor environment, and creating an aesthetic, comfortable and convenient indoor environment has gradually become the choice of most families. [0003] When decorating the interior walls of the houses delivered by the rough, the wall surface needs to be repaired first to ensure that the base layer is flat and firm, without powdering, sanding, hollowing, falling off, etc.; after the wall surface is leveled, two coats of plastering are required In the second step, putty is usually applied to the wall, and the putty layer is leveled; finally, latex paint is applied to the wall to complete the wall decoration. [0004] At...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D1/00C09D1/08C09D7/65C09D7/61C09D7/63
CPCC09D1/00C09D1/08
Inventor 李晓利刘学影
Owner 南京安德丽节能建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com