Ceramic large board ground glaze and preparation method thereof

A bottom glaze and ceramic technology, applied in the field of ceramic tiles, can solve problems such as high production costs, reduced economic benefits, and low yield, and achieve good antifouling and chemical corrosion resistance, strong controllability of process parameters, and high production efficiency. high efficiency effect

Inactive Publication Date: 2018-07-13
广东金牌陶瓷有限公司
View PDF4 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, it is difficult for domestic ceramic slabs to overcome the technical difficulties of glazed surface. The glazed surface of the products after f...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ceramic large board ground glaze and preparation method thereof
  • Ceramic large board ground glaze and preparation method thereof
  • Ceramic large board ground glaze and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A ceramic slab base glaze, the high-temperature firing temperature of which is 1185-1215°C, comprising the following components in terms of raw material weight percentage:

[0027]

[0028] Wherein, the potassium feldspar is K 2 O content accounts for the feldspar raw material of 7%; The albite is Na 2 Feldspar raw material with O content of 13%; the mixed kaolin is a mixture of raw kaolin and calcined kaolin with a weight ratio of 1:3; Al in the nepheline is by mass percentage 2 o 3 Content is 20%, K 2 O content is 8%, Na 2 The O content is 5%; SiO is calculated by mass percentage in the medium temperature frit 2 The content is 60%, Al 2 o 3 The content is 10%; the base glaze includes the following main chemical components in terms of mass percentage: 22% Al 2 o 3 , 65% SiO 2 , 0.01% Fe 2 o 3 , 0.9% CaO, 0.1% MgO, 0.99% K 2 O, 1% Na 2 O, 0.6% TiO 2 , 5.4% ZrO 2 , 4% loss on ignition.

[0029] Preparation:

[0030] 1) Put each component into the glaz...

Embodiment 2

[0033] A ceramic slab base glaze, the high-temperature firing temperature of which is 1185-1215°C, comprising the following components in terms of raw material weight percentage:

[0034]

[0035] Wherein, the potassium feldspar is K 2 O content accounts for the feldspar raw material of 14%; The albite is Na 2 Feldspar raw material with O content of 7%; the mixed kaolin is a mixture of raw kaolin and calcined kaolin with a weight ratio of 1:3; Al in the nepheline is by mass percentage 2 o 3 Content is 30%, K 2 O content is 1%, Na 2 The O content is 10%; SiO is calculated by mass percentage in the medium temperature frit 2 The content is 75%, Al 2 o 3 The content is 2%; the base glaze includes the following main chemical components in terms of mass percentage: 29.25% Al 2 o 3 , 50% SiO 2 , 0.45% Fe 2 o 3 , 0.1% CaO, 0.1% MgO, 0.5% K 2 O, 1% Na 2 O, 0.6% TiO 2 , 10% ZrO 2 , 8% loss on ignition.

[0036] Preparation:

[0037]1) Put each component into the glaz...

Embodiment 3

[0040] A ceramic slab base glaze, the high-temperature firing temperature of which is 1185-1215°C, comprising the following components in terms of raw material weight percentage:

[0041]

[0042] Wherein, the potassium feldspar is K 2 O content accounts for the feldspar raw material of 10%; The albite is Na 2 Feldspar raw material with O content of 10%; the mixed kaolin is a mixture of raw kaolin and calcined kaolin with a weight ratio of 1:3; Al in the nepheline is by mass percentage 2 o 3 Content is 25%, K 2 O content is 4%, Na 2 The O content is 8%; SiO is calculated by mass percentage in the medium temperature frit 2 The content is 70%, Al 2 o 3 The content is 8%; the base glaze includes the following main chemical components in terms of mass percentage: 25% Al 2 o 3 , 55% SiO 2 , 0.2% Fe 2 o 3 , 0.7% CaO, 0.4% MgO, 1.5% K 2 O, 8% Na 2 O, 0.3% TiO 2 , 4% ZrO 2 , 4.9% loss on ignition.

[0043] Preparation:

[0044] 1) Put each component into the glaze ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses ceramic large board ground glaze. The ceramic large board ground glaze is prepared from the following raw materials in percentage by weight: 10 to 20 percent of potassium feldspar, 22 to 40 percent of sodium feldspar, 5 to 15 percent of nepheline, 20 to 30 percent of mixed kaolin, 5 to 15 percent of quartz powder, 10 to 20 percent of aluminum oxide, 5 to 10 percent of middle-temperature frit and 5 to 15 percent of zirconium silicate. According to the ceramic large board ground glaze disclosed by the invention, the ground glaze has excellent performance through adjustingraw material components and ratios thereof, and can be suitable for glaze spraying technological operation in a production process; meanwhile, after high-temperature firing is carried out, a glaze surface has no defects of needle holes, concave glaze, air bubbles and the like, so that the color, luster and lines have the advantage that a natural large rock plate is smooth and natural and the ground glaze also has a noble and elegant appearance of ceramic tiles; a ceramic large board has good pollution resistance and chemical corrosion resistance. The invention further discloses a preparationmethod of the ground glaze; the preparation method has the advantages of simple technology, strong controllable technological parameters and high production efficiency, and is suitable for large-scaleindustrial production.

Description

technical field [0001] The invention relates to the field of ceramic tiles, in particular to a ceramic tile bottom glaze. Background technique [0002] As a new type of ceramic product, ceramic slabs can carry richer texture elements than traditional ceramic tiles due to their super-large specifications. Combined with advanced technology, they can achieve excellent glaze quality. Ceramic large slabs have the advantages of simple and elegant decorative effects, less seams, avoiding dirt and dirt, and high construction and laying efficiency. Its market share in the high-end household products market will continue to increase. [0003] However, the size of ceramic large slabs exceeds the size of conventional ceramic tiles, which increases the difficulty of production. It is necessary to ensure the stability of the production process and improve the quality of the product. This requires that the glaze formula can be matched with the body and the kiln at the same time. Achieve s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C03C8/02
CPCC03C8/02
Inventor 谭旭日赖观忠毛星华
Owner 广东金牌陶瓷有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap