Heat insulation material for interior and exterior walls, and preparation method thereof

A technology for heat insulation materials and interior and exterior walls, applied in the direction of reflection/signal coatings, polyurea/polyurethane coatings, coatings, etc., can solve the problems of low cost and high cost, and achieve good film-forming properties, good pit pull strength, and convenience Effects of staining and decorating

Inactive Publication Date: 2018-08-03
江苏翔鹭节能科技有限公司
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The three kinds of heat insulation materials have their own advantages and disadvantages. Although the insulating conductive heat insulation coating has certain limitations in performance, it is relatively low in cost and widely used; while the reflective and radiation type heat insulation The thermal effect is good, but the cost is high; therefore, there is an urgent need for a thermal insulation coating with high cost performance and good thermal insulation effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] A heat insulation material that can be used for interior and exterior walls, and its raw material formula is as follows:

[0052] A. Elastic emulsion

[0053] B. Powder

[0054] C. Hollow microspheres

[0055] D. Nano slurry

[0056] E. Defoamer

[0057] F. Surfactant

[0058]The elastic emulsion is formed by mixing polyurethane-modified acrylate elastic emulsion and pure acrylate elastic emulsion in a ratio of 2-4:1.

[0059] A heat insulation material that can be used for interior and exterior walls, according to the ratio of parts by weight, its raw material formula is as follows:

[0060] A. Elastic emulsion: 175-210 parts

[0061] B. Powder: 21-60 parts

[0062] C. Hollow microspheres: 15-30 parts

[0063] D. Nano slurry: 30-50 parts

[0064] E. Defoamer: 2-7 parts

[0065] F, Surfactant 1-5 parts

[0066] The elastic emulsion is formed by mixing polyurethane-modified acrylate elastic emulsion and pure acrylate elastic emulsion in a ratio of 3:1.

[006...

Embodiment 2

[0075] A heat insulation material that can be used for interior and exterior walls, and its raw material formula is as follows:

[0076] A. Elastic emulsion

[0077] B. Powder

[0078] C. Hollow microspheres

[0079] D. Nano slurry

[0080] E. Defoamer

[0081] F. Surfactant

[0082] The elastic emulsion is formed by mixing polyurethane-modified acrylate elastic emulsion and pure acrylate elastic emulsion in a ratio of 2-4:1.

[0083] A heat insulation material that can be used for interior and exterior walls, according to the ratio of parts by weight, its raw material formula is as follows:

[0084] A. Elastic emulsion: 180-200 parts

[0085] B. Powder: 45-55 parts

[0086] C. Hollow microspheres: 21-25 parts

[0087] D. Nano slurry: 35-45 parts

[0088] E. Defoamer: 4-6 parts

[0089] F, 2-4 parts of surfactant

[0090] The elastic emulsion is formed by mixing polyurethane-modified acrylate elastic emulsion and pure acrylate elastic emulsion in a ratio of 3:1.

...

Embodiment 3

[0103] A heat insulation material that can be used for interior and exterior walls, according to the ratio of parts by weight, its raw material formula is as follows:

[0104] A. Elastic emulsion: 175-210 parts

[0105] B. Powder: 21-60 parts

[0106] C. Hollow microspheres: 15-30 parts

[0107] D. Nano slurry: 30-50 parts

[0108] E. Defoamer: 2-7 parts

[0109] F, Surfactant 1-5 parts

[0110] The elastic emulsion is formed by mixing polyurethane-modified acrylate elastic emulsion and pure acrylate elastic emulsion in a ratio of 3:1.

[0111] A method for preparing a thermal insulation material for interior and exterior walls, comprising the steps of:

[0112] (1) Take fine powder and elastic emulsion in stirring tank according to parts by weight, stir;

[0113] (2) taking hollow microspheres, nano slurry and surfactant according to the ratio of parts by weight, first adding hollow microspheres and nano slurry to the stirring tank, then adding surfactant while stirring...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of heat insulation coatings, and concretely relates to a heat insulation material for interior and exterior walls, and a preparation method thereof. A nano-slurry is innovatively added to a heat insulation coating based on the prior art, the nano-slurry adopts a silica nano-slurry, the silica has a good film-forming property and a low heat conductivity,and can assist heat conduction obstruction, and the nano-slurry has a good adhesion and a good viscosity, so the heat insulation material for interior and exterior walls has the advantages of easiness in dyeing and decorating and good heat insulation effect when applied indoors.

Description

technical field [0001] The invention belongs to the technical field of heat-insulating coatings, and in particular relates to a heat-insulating material that can be used for interior and exterior walls and a preparation method thereof. Background technique [0002] "Heat insulation coating": refers to a functional water-based coating developed in recent years that blocks, reflects, and radiates near-infrared heat from sunlight, which can insulate and cool roofs, save energy and reduce consumption. It has the characteristics of heat insulation, waterproof, anti-rust, anti-corrosion, short construction period, and quick results. It completely replaces the water spray system, thermal insulation cotton, foam sponge, interlayer iron sheet, etc. There are three main classifications of thermal insulation coatings in terms of characteristics and principles, insulating conductive thermal insulation coatings, reflective thermal insulation coatings and radiation thermal insulation coat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/14C09D133/04C09D7/61C09D5/33
Inventor 朱小明
Owner 江苏翔鹭节能科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap