Method for preparing high-toughness cyanate ester seamless tube

A cyanate ester and seamless pipe technology, applied in the field of pipeline design, can solve the problems of steel pipe fracture, damage, lack of protection, curling and deformation, etc., and achieve the effects of simple production technology, improved overall toughness and long service life

Inactive Publication Date: 2018-09-21
胡建芳
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Since the transportation of solid particles, ore, mud and other abrasive media in coal preparation, mining, metallurgy and other industries requires high wear resistance of pipelines, polyurethane materials are used as inner linings and steel pipes as outer protective layers to become the first choice for wear-resistant pipelines , but the polyurethane elastomer will curl up and deform under the action of strong persistent stress, hindering the transportation of solid particles, powder, slurry, liquid and other media, and even blockage and explosion will occur in harsh industrial and mining conditions. Under the impact of external force, it will be broken and damaged, and it will not be able to protect it. It will cause harm to the personal and property of industrial and mining enterprises, and the consequences will be serious.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0021] The present invention will be further described below.

[0022] A method for preparing a high-toughness cyanate ester seamless pipe, comprising the following steps:

[0023] Step 1), prepare the casting mixture raw materials by mass percentage, tetrahydrofuran propylene oxide copolyether 60%~80%, toluene diisocyanate 4%~20%, vulcanizing agent MOCA 5%~15%, polyester diol 5%~11 %, the rest is the crosslinking agent trihydric alcohol N3010;

[0024] Step 2) Equipped with steel pipes, after sandblasting the inner and outer surfaces of the steel pipes, uniformly open 5cm diameter holes in the pipe body of the steel pipes at a distance of 20cm, and air-dry them at room temperature;

[0025] Step 3), pour the tetrahydrofuran propylene oxide copolyether prepared in step 1) into the reaction kettle, start the agitator, turn on the heating power at the same time to start heating, and then put the prepared toluene diisocyanate, polyester diol, Slowly pour the joint agent trihydr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a method for preparing a high-toughness cyanate ester seamless tube. The method comprises the following steps: 1) casting mixture raw materials according to mass percentages;2) preparing a steel tube; 3) preparing a prepolymer; 4) preparing a cyanate ester prepolymer; 5) mounting the steel tube obtained in the step 2) on a centrifuge with a mold, maintaining casting holesin two ends in a horizontal direction, heating the steel tube, and keeping the temperature at 60-70 DEG C; 6) preparing a cast mixture; 7) carrying out casting molding; 8) vulcanizing the steel tube;9) carrying out inner / outer surface cleaning treatment on the vulcanized steel tube, so as to obtain the cyanate ester seamless tube, wherein the cyanate ester seamless tube is stored in warehouses after inspection qualification. By adopting the production process provided by the invention, the wearing resistance of the tube is improved, the toughness of the tube is improved, and tube layering can be effectively prevented.

Description

technical field [0001] The invention relates to a method for preparing a high-toughness cyanate ester seamless pipe, which belongs to the technical field of pipeline design. Background technique [0002] Since the transportation of solid particles, ore, mud and other abrasive media in coal preparation, mining, metallurgy and other industries requires high wear resistance of pipelines, polyurethane materials are used as inner linings and steel pipes as outer protective layers to become the first choice for wear-resistant pipelines , but the polyurethane elastomer will curl up and deform under the action of strong persistent stress, which will hinder the transportation of solid particles, powder, slurry, liquid and other media, and even blockage and explosion will occur in harsh industrial and mining conditions. It will be broken and damaged under the impact of external force, and it will not play a protective role, causing harm to the personal and property of industrial and m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08G18/76C08G18/66C08G18/48C08G18/42C08G18/32
CPCC08G18/3206C08G18/4018C08G18/42C08G18/4854C08G18/6611C08G18/7614
Inventor 乐少兵李林瑞
Owner 胡建芳
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products